Process for the continuous mass polymerization of polyblends having a bimodal rubber particle size
Assignee: Bayer Antwerpen NV
•
Filing: 1979-03-07
•
Granted: 1981-03-03
•
Expires: 1999-03-07
Abstract
Abstract The invention relates to a continuous mass polymerization process for polyblends having a dispersed rubber phase with a bimodal rubber particle size distribution, wherein, first and second monomer-rubber solutions are fed to a first back-mixed polymerization zone such that said first solution forms particles of about 0.5 to 1.5 microns and said second solution, having present a dissolved rubber and a dissolved polymer of said monomer, forms particles of about 2 to 5 microns during partial polymerization of 10 to 50% of said monomers. Said partially polymerized solutions are further polymerized in a second zone, with linear flow, to a conversion of 20 to 95%, forming said polyblend with a bimodal rubber particle size distribution having improved toughness and gloss.
Inventors
- 👤 Raymond D. Burk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 03:12
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
291 words
A method for continuously mass polymerizing polyblends having a dispersed diene rubber phase as rubber particles with a bimodal particle size distribution comprising: A. continuously and simultaneously charging, as separate feed streams, first and second monomer-rubber solutions to a first flow-through, back-mixed, reaction zone, said monomer being selected from the group consisting of alkenyl aromatic and alkenyl nitrile/alkenyl aromatic mixtures, said second monomer-rubber solution having present dissolved polymer of said monomer, B. continuously polymerizing said first and second solutions under steady state conditions, said monomer being polymerized to a conversion of about 15 to 50% forming a partially polymerized solution while, C. continuously dispersing in said partially polymerized solution, said first monomer-rubber solutions as first rubber-particles having an average particle size of about 0.5 to 1.5 microns and said second monomer-rubber solution as second rubber particles having a particle size of about 2 to 10 microns, said second monomer-rubber solution having present sufficient polymer of said monomer to size said second rubber particles to an average particle size of about 2 to 10 microns, D. continuously withdrawing said partially polymerized solution from said first reaction zone, E. continuously charging said partially polymerized solution to a second flow-through reaction zone and further polymerizing said partially polymerized solution to about 20 to 95% conversion of said monomers under substantially linear flow, F. continuously withdrawing an effluent from said second reaction zone and continuously separating said polyblend from said effluent, said polyblend having a matrix phase polymer of said monomer having dispersed therein said first and second rubber particles having a bimodal rubber particle size distribution, said first and second rubber particles having present occluded and grafted polymer of said monomer in an amount of about 1 to 5 parts per part of rubber.
Claim 2
Independent Claim
291 words
A method for continuously mass polymerizing polyblends having a dispersed diene rubber phase as rubber particles with a bimodal particle size distribution comprising: A. continuously and simultaneously charging, as separate feed streams, first and second monomer-rubber solutions to a first flow-through, back-mixed, reaction zone, said monomer being selected from the group consisting of alkenyl aromatic and alkenyl nitrile/alkenyl aromatic mixtures, said second monomer-rubber solution having present dissolved polymer of said monomer, B. continuously polymerizing said first and second solutions under steady state conditions, said monomer being polymerized to a conversion of about 15 to 50% forming a partially polymerized solution while, C. continuously dispersing in said partially polymerized solution, said first monomer-rubber solutions as first rubber-particles having an average particle size of about 0.5 to 1.5 microns and said second monomer-rubber solution as second rubber particles having a particle size of about 2 to 10 microns, said second monomer-rubber solution having present sufficient polymer of said monomer to size said second rubber particles to an average particle size of about 2 to 10 microns, D. continuously withdrawing said partially polymerized solution from said first reaction zone, E. continuously charging said partially polymerized solution to a second flow-through reaction zone and further polymerizing said partially polymerized solution to about 20 to 95% conversion of said monomers under substantially linear flow, F. continuously withdrawing an effluent from said second reaction zone and continuously separating said polyblend from said effluent, said polyblend having a matrix phase polymer of said monomer having dispersed therein said first and second rubber particles having a bimodal rubber particle size distribution, said first and second rubber particles having present occluded and grafted polymer of said monomer in an amount of about 1 to 5 parts per part of rubber.
Claim 3
Dependent Claim
28 words
A process of claim 1 wherein said alkenyl aromatic monomer is selected from the group consisting of styrene, a-methyl styrene, chlorostyrene, dichlorostyrene, bromostyrene or dibromostyrene and mixtures thereof.
Claim 4
Dependent Claim
33 words
A process of claim 1 wherein said diene rubber is selected from the group consisting of polybutadiene, polyisoprene, poly-2-chlorobutadiene, poly-1-chlorobutadiene, copolymers and block copolymers of butadiene-styrene, butadiene-chloroprene, chloroprene-styrene, chloroprene-isoprene, 2-chlorobutadiene-1-chlorobutadiene and mixtures thereof.
Claim 5
Dependent Claim
11 words
A process of claim 1 wherein said diene rubber is polybutadiene.
Claim 6
Dependent Claim
31 words
A process of claim 4 wherein said polybutadiene rubber has a cis isomer content of about 30 to 98% and a Tg range of from about -50° C. to -105 C.
Claim 7
Dependent Claim
12 words
A process of claim 1 wherein said alkenyl aromatic monomer is styrene.
Claim 8
Dependent Claim
48 words
A process of claim 1, said first reaction zone operating with essentially constant fillage of 10 to 90% of its volume with said solutions at a temperature of about 100° to 140° C. under a pressure of about 1 to 150 psig with isothermal and steady state polymerization.
Claim 9
Dependent Claim
72 words
A process of claim 1 wherein said second reaction zone is a staged, isobaric, stirred reaction zone, said partially polymerized solution being polymerized by progressive multistage substantially linear flow polymerization, all said stages operating with agitation and common evaporative vapor phase cooling under isobaric conditions, providing each said stage with steady state polymerization at a controlled temperature of about 130° to 180° C. and a pressure of about 7 to 28 psia.
Claim 10
Dependent Claim
36 words
A process of claim 1 wherein the continuous charging of said first and second solution in step (A) is at a rate about equal to the rate at which second effluent is withdrawn in step (F).
Claim 11
Dependent Claim
22 words
A process of claim 1 wherein said solutions have present about 0.01 to 3.0% by weight of a free radical generating catalyst.
Claim 12
Dependent Claim
38 words
A process of claim 10 wherein said free radical generating catalyst is selected from the group consisting of di-tert-butyl peroxide, tert-butyl peracetate, benzoyl peroxide, lauroyl peroxide, tert-butyl perbenzoate, dicumyl peroxide, tert-butyl peroxide and isopropyl carbonate or mixtures thereof.
Claim 13
Dependent Claim
59 words
A process of claim 1 wherein said dissolved polymer of said monomer is present in said second monomer-rubber solution in an amount of about 10 to 150% by weight based on said diene rubber and said first and second monomer solutions are fed in step (A) at a weight ratio of first to second of about 1:1 to 20:1.
Claim 14
Dependent Claim
29 words
A process of claim 1 wherein said diene rubber is present in each first and second solutions in an amount of about 2 to 15% based on said solution.
Claim 15
Dependent Claim
20 words
A process of claim 1 wherein said first and second solutions comprise a solution of a diene rubber in styrene.
Claim 16
Dependent Claim
23 words
A process of claim 1 wherein said first and second solutions comprise a solution of a diene rubber dissolved in styrene and acrylonitrile.
Claim 17
Dependent Claim
27 words
A process of claim 15 wherein said styrene and acrylonitrile are present in amounts having a weight ratio of styrene to acrylonitrile of about 90:10 to 50:50.
Claim 18
Dependent Claim
10 words
A process of claim 1 wherein said polymer is polystyrene.
Claim 19
Dependent Claim
19 words
A process of claim 17 wherein said polystyrene has a weight average molecular weight of about 100,000 to 300,000.
Claim 20
Dependent Claim
25 words
A process of claim 1 wherein said polymer is a styrene-acrylonitrile polymer having a weight ratio of styrene to acrylonitrile of about 90:10 to 50:50.
Claim 21
Dependent Claim
20 words
A process of claim 19 wherein said styrene-acrylonitrile polymer has a weight average molecular weight of about 100,000 to 300,000.
Claim 22
Dependent Claim
23 words
A process of claim 1 wherein said matrix phase comprises a matrix polymer selected from the group consisting of polystyrene and styrene-acrylonitrile polymer.
Claim 23
Dependent Claim
65 words
A process of claim 1 wherein said polyblend has a bimodal rubber particle size distribution wherein about 50 to 95% of said rubber particles have a weight average particle size diameter of about 0.5 to 1.5 microns as first rubber-particles and 5 to 50% of said rubber particles have a weight average particle size diameter of about 2 to 10 microns as second rubber particles.
Claim 24
Independent Claim
278 words
A method for continuously mass polymerizing polyblends having a dispersed polybutadiene rubber phase as rubber particles with a bimodal particle size distribution comprising: A. continuously and simultaneously charging, as separate feed streams, first and second monomer-rubber solutions to a first flow-through, back-mixed, reaction zone, said monomer being styrene, said second monomer-rubber solution having present a dissolved polymer of said monomer, B. continuously polymerizing said first and second solutions under steady state conditions, said monomer being polymerized to a conversion of about 15 to 50% forming a partially polymerized solution while, C. continuously dispersing in said partially polymerized solution, said first monomer-rubber solutions as first rubber-particles having an average particle size of about 0.5 to 1.5 microns and said second monomer-rubber solution as second rubber particles having a particle size of about 2 to 10 microns, said second monomer-rubber solution having present sufficient polymer of said monomer to size said second rubber particles to an average particle size of about 2 to 10 microns, D. continuously withdrawing said partially polymerized solution from said first reaction zone, E. continuously charging said partially polymerized solution to a second flow-through reaction zone and further polymerizing said partially polymerized solution to about 20 to 95% conversion of said monomers under substantially linear flow, F. continuously withdrawing an effluent from said second reaction zone and continuously separating said polyblend from said effluent, said polyblend having a matrix phase of polystyrene having dispersed therein said first and second rubber particles having a bimodal rubber particle size distribution, said first and second rubber particles having present occluded and grafted polymer of said monomer in an amount of about 1 to 5 parts per part of rubber.
Claim 25
Independent Claim
278 words
A method for continuously mass polymerizing polyblends having a dispersed polybutadiene rubber phase as rubber particles with a bimodal particle size distribution comprising: A. continuously and simultaneously charging, as separate feed streams, first and second monomer-rubber solutions to a first flow-through, back-mixed, reaction zone, said monomer being styrene, said second monomer-rubber solution having present a dissolved polymer of said monomer, B. continuously polymerizing said first and second solutions under steady state conditions, said monomer being polymerized to a conversion of about 15 to 50% forming a partially polymerized solution while, C. continuously dispersing in said partially polymerized solution, said first monomer-rubber solutions as first rubber-particles having an average particle size of about 0.5 to 1.5 microns and said second monomer-rubber solution as second rubber particles having a particle size of about 2 to 10 microns, said second monomer-rubber solution having present sufficient polymer of said monomer to size said second rubber particles to an average particle size of about 2 to 10 microns, D. continuously withdrawing said partially polymerized solution from said first reaction zone, E. continuously charging said partially polymerized solution to a second flow-through reaction zone and further polymerizing said partially polymerized solution to about 20 to 95% conversion of said monomers under substantially linear flow, F. continuously withdrawing an effluent from said second reaction zone and continuously separating said polyblend from said effluent, said polyblend having a matrix phase of polystyrene having dispersed therein said first and second rubber particles having a bimodal rubber particle size distribution, said first and second rubber particles having present occluded and grafted polymer of said monomer in an amount of about 1 to 5 parts per part of rubber.
Claim 26
Independent Claim
281 words
A method for continuously mass polymerizing polyblends having a dispersed polybutadiene rubber phase as rubber particles with a bimodal particle size distribution comprising: A. continuously and simultaneously charging, as separate feed streams, first and second monomer-rubber solutions to a first flow-through, back-mixed, reaction zone, said monomer being styrene and acrylonitrile, said second monomer-rubber solution having present a dissolved polymer of said monomer, B. continuously polymerizing said first and second solutions under steady state conditions, said monomer being polymerized to a conversion of about 15 to 50% forming a partially polymerized solution while, C. continuously dispersing in said partially polymerized solution, said first monomer-rubber solutions as first rubber-particles having an average particle size of about 0.5 to 1.5 microns and said second monomer-rubber solution as second rubber particles having a particle size of about 2 to 10 microns, said second monomer-rubber solution having present sufficient polymer of said monomer to size said second rubber particles to an average particle size of about 2 to 10 microns, D. continuously withdrawing said partially polymerized solution from said first reaction zone, E. continuously charging said partially polymerized solution to a second flow-through reaction zone and further polymerizing said partially polymerized solution to about 20 to 95% conversion of said monomers under substantially linear flow, F. continuously withdrawing an effluent from said second reaction zone and continuously separating said polyblend from said effluent, said polyblend having a matrix phase of styrene-acrylonitrile polymer having dispersed therein said first and second rubber particles having a bimodal rubber particle size distribution, said first and second rubber particles having present occluded and grafted polymer of said monomers in an amount of about 1 to 5 parts per part of rubber.
Claim 27
Independent Claim
281 words
A method for continuously mass polymerizing polyblends having a dispersed polybutadiene rubber phase as rubber particles with a bimodal particle size distribution comprising: A. continuously and simultaneously charging, as separate feed streams, first and second monomer-rubber solutions to a first flow-through, back-mixed, reaction zone, said monomer being styrene and acrylonitrile, said second monomer-rubber solution having present a dissolved polymer of said monomer, B. continuously polymerizing said first and second solutions under steady state conditions, said monomer being polymerized to a conversion of about 15 to 50% forming a partially polymerized solution while, C. continuously dispersing in said partially polymerized solution, said first monomer-rubber solutions as first rubber-particles having an average particle size of about 0.5 to 1.5 microns and said second monomer-rubber solution as second rubber particles having a particle size of about 2 to 10 microns, said second monomer-rubber solution having present sufficient polymer of said monomer to size said second rubber particles to an average particle size of about 2 to 10 microns, D. continuously withdrawing said partially polymerized solution from said first reaction zone, E. continuously charging said partially polymerized solution to a second flow-through reaction zone and further polymerizing said partially polymerized solution to about 20 to 95% conversion of said monomers under substantially linear flow, F. continuously withdrawing an effluent from said second reaction zone and continuously separating said polyblend from said effluent, said polyblend having a matrix phase of styrene-acrylonitrile polymer having dispersed therein said first and second rubber particles having a bimodal rubber particle size distribution, said first and second rubber particles having present occluded and grafted polymer of said monomers in an amount of about 1 to 5 parts per part of rubber.
References Cited (Backward Citations)
CA832523A
Cited
US3398214A
Cited
US3509238A
Cited
US3509237A
Cited
US3945976A
Cited
US3652721A
Cited
US3660535A
Cited
US3903202A
Cited
US4012462A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-02 | 1984-09-01 | 1985-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-02 | 1988-09-01 | 1989-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-02 | 1992-09-01 | 1993-03-03 | $7700.00 | Window Closed / Lapsed |