Process for preparing ABS polyblends
Assignee: Bayer Antwerpen NV
•
Filing: 1979-11-19
•
Granted: 1981-07-07
•
Expires: 1999-11-19
Abstract
Abstract The present invention relates to a process for preparing ABS polyblends having an alkenyl aromaticalkenyl nitrile monomer matrix polymeric phase reinforced with rubber particles grafted with said monomers and having a bimodal rubber particle size distribution, the process comprising: charging continuously a formulation of said monomers having a soluble diene dissolved therein and a first grafted diene rubber particle dispersed therein to a back-mixed reaction zone operating at 50-80% steady state, flow-through, conversion of said monomer formulation, continuously mass polymerizing said charged monomer formulation to 50-80% conversion, forming and dispersing said soluble rubber as second grafted diene particles having a particle size larger than said first grafted rubber particles, continuously withdrawing an effluent from said reaction zone and separating said ABS polyblend from said effluent.
Inventors
- 👤 Michael B. Jastrzebski
- 👤 Allen R. Padwa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:00
CPC Classifications
C; C08; C08F; C08F285/00
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
327 words
A continuous mass polymerization process for preparing an ABS polyblend having a bimodal rubber particle size distribution, the steps comprising: (A) continuously charging a monomer formulation of alkenyl aromatic and alkenyl nitrile monomers having a soluble diene rubber dissolved therein and first grafted diene rubber particles dispersed therein to a reaction zone, said grafted rubber having alkenyl aromatic and alkenyl nitrile grafts, said first grafted diene rubber particles having an average particle size of about 0.01 to 0.5 microns, (B) continuously mass polymerizing said charged monomer formulation in said reaction zone, to a conversion of about 30 to 80%, while forming and dispersing said soluble diene rubber as second grafted diene rubber particles having present occluded and grafted polymers of said monomers in amount of about 0.5 to 5.0 parts per part of rubber, said second grafted diene rubber particles having an average particle size of about 0.7 to 10.0 microns, said monomers forming a copolymer of said monomers as a matrix phase polymer having said first and second rubber particles dispersed therein, (C) continuously removing an effluent from said reaction zone at a rate essentially equal to that of said charged monomer formulation, and (D) separating said matrix polymer having said first and second grafted rubber particles dispersed therein from said effluent as said ABS polyblend having a bimodal rubber particle size distribution, wherein the weight ratio of alkenyl aromatic to alkenyl nitrile monomers in said monomer formulation is about 85:15 to 60:40; wherein said soluble rubber moiety and said first grafted rubber moiety are present in said monomer formulation in a total amount of about 2 to 40 percent by weight with said soluble rubber moiety being about 5 to 50 percent by weight of the total rubber moiety; wherein the polymerization of step (B) is conducted at temperatures of about 90° to 180° C. under a pressure of about 5 to 150 psia with shearing agitation; wherein said diene rubbers are polybutadiene based rubbers.
Claim 2
Dependent Claim
327 words
A continuous mass polymerization process for preparing an ABS polyblend having a bimodal rubber particle size distribution, the steps comprising: (A) continuously charging a monomer formulation of alkenyl aromatic and alkenyl nitrile monomers having a soluble diene rubber dissolved therein and first grafted diene rubber particles dispersed therein to a reaction zone, said grafted rubber having alkenyl aromatic and alkenyl nitrile grafts, said first grafted diene rubber particles having an average particle size of about 0.01 to 0.5 microns, (B) continuously mass polymerizing said charged monomer formulation in said reaction zone, to a conversion of about 30 to 80%, while forming and dispersing said soluble diene rubber as second grafted diene rubber particles having present occluded and grafted polymers of said monomers in amount of about 0.5 to 5.0 parts per part of rubber, said second grafted diene rubber particles having an average particle size of about 0.7 to 10.0 microns, said monomers forming a copolymer of said monomers as a matrix phase polymer having said first and second rubber particles dispersed therein, (C) continuously removing an effluent from said reaction zone at a rate essentially equal to that of said charged monomer formulation, and (D) separating said matrix polymer having said first and second grafted rubber particles dispersed therein from said effluent as said ABS polyblend having a bimodal rubber particle size distribution, wherein the weight ratio of alkenyl aromatic to alkenyl nitrile monomers in said monomer formulation is about 85:15 to 60:40; wherein said soluble rubber moiety and said first grafted rubber moiety are present in said monomer formulation in a total amount of about 2 to 40 percent by weight with said soluble rubber moiety being about 5 to 50 percent by weight of the total rubber moiety; wherein the polymerization of step (B) is conducted at temperatures of about 90° to 180° C. under a pressure of about 5 to 150 psia with shearing agitation; wherein said diene rubbers are polybutadiene based rubbers.
Claim 3
Dependent Claim
22 words
A process of claim 1 wherein said monoalkenylaromatic monomer is styrene, said ethylenically unsaturated monomer is acrylonitrile and said diene rubber polybutadiene.
Claim 4
Dependent Claim
11 words
A process of claim 1 wherein said monoalkenylaromatic monomer is styrene.
Claim 5
Dependent Claim
13 words
A process of claim 1 wherein said ethylenically unsaturated nitrile monomer is acrylonitrile.
Claim 6
Dependent Claim
26 words
A process of claim 1 wherein the said monoalkenylaromatic monomer and said ethylenically unsaturated nitrile monomer comprise at least 75% by weight of said monomer formulation.
Claim 7
Dependent Claim
39 words
A process of claim 1 wherein said soluble diene rubber of said second grafted rubber is polybutadiene having a cis isomer content of about 30 to 98% and a Tg range of from about -50° C. to -105° C.
Claim 8
Dependent Claim
27 words
A process of claim 1 wherein said first and second grafted rubbers have a swelling index of about 5 to 30 as contained in said ABS polyblend.
Claim 9
Dependent Claim
21 words
A process of claim 1 wherein the matrix copolymer formed has an average molecular weight of from about 20,000 to 1,000,000.
Claim 10
Dependent Claim
31 words
A process of claim 1 wherein the polymerization step (B) is carried out with said monomer formulation having present about 0.001 to 3.0% by weight of a free radical generating catalyst.
Claim 11
Dependent Claim
38 words
A process of claim 9 wherein said free radical generating catalyst is selected from the group consisting of di-tert-butyl peroxide, tert-butyl peracetate, benzoyl peroxide, lauroyl peroxide, tert-butyl perbenzoate, dicumyl peroxide, tert-butyl peroxide and isopropyl carbonate or mixtures thereof.
Claim 12
Dependent Claim
14 words
A process of claim 10 wherein said free radical generating catalyst is tert-butyl peracetate.
Claim 13
Dependent Claim
14 words
A process of claim 10 wherein said free radical generating catalyst is di-tert-butyl peroxide.
Claim 14
Dependent Claim
22 words
A process of claim 1 wherein the continuous mass polymerization of step (B) is conducted at temperatures of 90° to 180° C.
Claim 15
Dependent Claim
30 words
A process of claim 1 wherein the polymerization step (B) is controlled thermally by evaporating and removal of said monomers under isobaric conditions and shearing agitation from said reaction zone.
Claim 16
Dependent Claim
29 words
A process of claim 14 wherein the evaporated and removed monomers are liquified and returned to the reaction zone at a rate such that steady state polymerization is maintained.
Claim 17
Dependent Claim
30 words
A process of claim 1 wherein said separation of step (D) is carried out by devolatilization of said effluent at temperatures of about 150° to 250° C., under subatmospheric pressure.
Claim 18
Dependent Claim
52 words
A process of claim 1 wherein said first and second grafted diene rubber particles are present in said ABS polyblend in amount such that a total diene rubber moiety of about 2 to 40% by weight is present, said second grafted rubber being about 5 to 50% of said total rubber moiety.
Claim 19
Dependent Claim
29 words
A process of claim 1 wherein said reaction zone is a back-mixed, flow-through, reaction zone operating at a partial fillage of about 40 to 90% with monomer evaporational cooling.
Claim 20
Dependent Claim
307 words
A continuous mass polymerization process for preparing an ABS polyblend having a bimodal rubber particle size distribution, the steps comprising: (A) continuously charging a monomer formulation of styrene and acrylonitrile monomers having a soluble polybutadiene rubber dissolved therein and first grafted polybutadiene rubber particles dispersed therein to a reaction zone, said first grafted polybutadiene rubber particles having an average particle size of about 0.01 to 0.5 microns, (B) continuously mass polymerizing said charged monomer formulation in said reaction zone, to a conversion of about 30 to 80 percent, while forming and dispersing said soluble polybutadiene rubber as second grafted polybutadiene rubber particles having present occluded and grafted polymers of said monomers in amount of about 0.5 to 5.0 parts per part of rubber, said second grafted polybutadiene rubber particles having an average particle size of about 0.7 to 10.0 microns, said monomers forming a copolymer of said monomers as a matrix phase polymer having said first and second rubber particled dispersed therein, (C) continuously removing an effluent from said reaction zone at a rate essentially equal to that of said charged monomer formulation, and (D) separating said matrix polymer having said first and second grafted rubber particles dispersed therein from said effluent as said ABS polyblend having a bimodal rubber particle size distribution, wherein the polymerization of step (B) is conducted at temperatures of about 90° to 180° C. under pressure of about 5 to 150 psia with shearing agitation; wherein said soluble diene rubber moiety and said first grafted diene rubber moiety are present in said monomer formulation in a total amount of about 2 to 40 percent by weight with said soluble rubber moiety being about 5 to 50 percent by weight of the total rubber moiety; wherein the weight ratio of styrene to acrylonitrile monomers in said monomer formulation is about 85:15 to 60:40.
Claim 21
Dependent Claim
307 words
A continuous mass polymerization process for preparing an ABS polyblend having a bimodal rubber particle size distribution, the steps comprising: (A) continuously charging a monomer formulation of styrene and acrylonitrile monomers having a soluble polybutadiene rubber dissolved therein and first grafted polybutadiene rubber particles dispersed therein to a reaction zone, said first grafted polybutadiene rubber particles having an average particle size of about 0.01 to 0.5 microns, (B) continuously mass polymerizing said charged monomer formulation in said reaction zone, to a conversion of about 30 to 80 percent, while forming and dispersing said soluble polybutadiene rubber as second grafted polybutadiene rubber particles having present occluded and grafted polymers of said monomers in amount of about 0.5 to 5.0 parts per part of rubber, said second grafted polybutadiene rubber particles having an average particle size of about 0.7 to 10.0 microns, said monomers forming a copolymer of said monomers as a matrix phase polymer having said first and second rubber particled dispersed therein, (C) continuously removing an effluent from said reaction zone at a rate essentially equal to that of said charged monomer formulation, and (D) separating said matrix polymer having said first and second grafted rubber particles dispersed therein from said effluent as said ABS polyblend having a bimodal rubber particle size distribution, wherein the polymerization of step (B) is conducted at temperatures of about 90° to 180° C. under pressure of about 5 to 150 psia with shearing agitation; wherein said soluble diene rubber moiety and said first grafted diene rubber moiety are present in said monomer formulation in a total amount of about 2 to 40 percent by weight with said soluble rubber moiety being about 5 to 50 percent by weight of the total rubber moiety; wherein the weight ratio of styrene to acrylonitrile monomers in said monomer formulation is about 85:15 to 60:40.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-06 | 1985-01-05 | 1985-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-06 | 1989-01-05 | 1989-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-06 | 1993-01-05 | 1993-07-07 | $7700.00 | Window Closed / Lapsed |