Screen-printing composition and use thereof

Claim 2

A screen-printing curable composition consisting essentially of: (A) about 31 to about 55% by weight of a non-liquid epoxidized novola k represented by the formula: ##STR8## wherein n is at least about 0.2; E is hydrogen or an epoxyalkyl group, at least two E groups per polymer molecule being an epoxyalkyl group and wherein the epoxyalkyl group is represented by the formula: ##STR9## p is an integer from 1-8; R is hydrogen or alkyl or alkylene or aryl or aralkyl or alkaryl or cycloalkyl or furyl group; each R 1 individually is hydrogen or alkyl group of up to 7 carbon atoms; wherein the number of carbon atoms in any epoxy-alkyl group totals no more than 10 carbon atoms; each X and Y is individually hydrogen or chlorine or alkyl or hydroxyl; each R 2 individually is hydrogen or chlorine or a hydro-carbon group; (B) about 6 to about 12% by weight of a thermoplastic polyhydroxy ether reaction product of a polynuclear dihydric phenol and epichlorohydrin substantially free of 1,2-epoxy groups having the formula: --O--A--O--B].sub.m wherein A is the radical residuum of a polynuclear dihydric phenol, B is an hydroxyl-containing radical residuum of epichlorohydrin, and m is at least 30; (C) about 15 to about 21% of weight of a liquid anhydride of carboxylic acid; (D) about 4.5 to about 6% by weight of colloidal silica and wherein said colloidal silica has a surface area of about 50 to about 400 m 2 /gram and the particles have a diameter of about 5 to about 20 millimicrons; and (E) volatile diluent in an amount sufficient to provide a composition with a viscosity of about 14,000 to about 50,000 centipoises determined with a Haake Rotovisco with a shear rate of 249.6/sec. for 1.28 minutes at 25° C.; and wherein the ratio of (A):(B) is about 7:1 to aout 4:1, the above amounts being based upon the total of (A), (B), (C), (D), and (E) in said composition.

Claim 3

The composition of claim 1 wherein said epoxidized novolac is represented by the formula: ##STR10##

Claim 4

The composition of claim 1 wherein said epoxidized novolac is represented by the formula: ##STR11## wherein n is at least about 1.5.

Claim 5

The composition of claim 1 wherein said epoxidized novolac is represented by the formula: ##STR12## wherein n is from about 1.5 to about 2.

Claim 6

The composition of claim 1 wherein said thermoplastic polyhydroxy ether is the reaction product of bisphenol-A and epichlorohydrin and is represented by the formula: ##STR13##

Claim 7

The composition of claim 5 wherein the molecular weight of said thermoplastic polyhydroxy ether is from about 20,000 to about 50,000.

Claim 8

The composition of claim 5 wherein the molecular weight of said polyhydroxy ether is from about 25,000 to about 38,000.

Claim 9

The composition of claim 5 wherein the molecular weight of said polyhydroxy ether is about 29,500 to about 32,500.

Claim 10

The composition of claim 1 wherein said anhydride is nadic methyl anhydride.

Claim 11

The composition of claim 9 wherein said silica is fused silica gel.

Claim 12

The composition of claim 1 which further includes up to about 6% by weight of an accelerating agent for the cure of the epoxy.

Claim 13

The composition of claim 1 wherein the amount of said accelerating agent is about 2 to about 6% by weight.

Claim 14

The composition of claim 12 wherein said curing agent is 2-ethoxyhexanoic acid salt of 2,4,6-tris-N,N'-dimethylaminomethyl phenol.

Claim 15

The composition of claim 1 wherein said volatile diluent is a mono or dialkyl ether of ethyleneglycol or derivative thereof.

Claim 16

The composition of claim 1 wherein said volatile diluent is a mixture of cellosolve acetate and of diethyl carbitol wherein the composition contains about 15 to 21% by weight of said cellosolve acetate and about 0.1 to about 3% by weight of diethyl carbitol.

Claim 17

The composition of claim 1 which contains from about 45 to about 50% by weight of (A), about 7.5 to about 9.5% by weight of (B), about 16 to about 21% by weight of (C), about 4.5 to about 6% by weight of (D), about 15 to about 25% by weight of (E), and from about 2 to about 6% by weight of an accelerating agent (F) for cure of the epoxy wherein said amounts are based upon the total amount of (A), (B), (C), (D), (E), and (F) in said composition.

Claim 18

The composition of claim 16 which contains about 19 to about 21% by weight of (E), and from about 3 to about 4% by weight of (F), wherein said amounts are based upon the total amount of (A), (B), (C), (D), (E), and (F) in said composition.

Claim 19

The composition of claim 1 which further includes a leveling agent.

Claim 20

The composition of claim 18 wherein said leveling agent is present in an amount up to about 1% by weight.

Claim 21

The composition of claim 1 which has a viscosity of about 20,000 to about 50,000 centipoises.

Claim 22

The composition of claim 1 wherein the ratio of A:B is 4.5:1 to 7.1.

Claim 23

The composition of claim 1 wherein the ratio of A:B is 5:1 to 6:1.

Claim 24

The composition of claim 1 wherein the ratio of A:B is 5.5:1.

Claim 25

The composition of claim 1 wherein said composition further includes a UV brightener.

Claim 26

A surface coated with a cured composition from: (A) about 31 to about 55% by weight of a non-liquid epoxidized novolac represented by the formula: ##STR14## wherein n is at least about 0.2; E is hydrogen or an epoxyalkyl group, at least two E groups per polymer molecule being an epoxyalkyl group and wherein the epoxyalkyl group is represented by the formula: ##STR15## p is an integer from 1-8; R is hydrogen or alkyl or alkylene or aryl or aralkyl or alkaryl or cycloalkyl or furyl group; each R 1 individually is hydrogen or alkyl group of up to 7 carbon atoms; wherein the number of carbon atoms in any epoxyalkyl group totals no more than 10 carbon atoms, each X and Y is individually hydrogen or chlorine or alkyl or hydroxyl; each R 2 individually is hydrogen or chlorine or a hydrocarbon group; (B) about 6 to about 12% by weight of a thermoplastic polyhydroxy ether reaction product of a polynuclear dihydric phenol and epichlorohydrin substantially free of 1,2-epoxy groups having the formula: --O--A--O--B].sub.m ( 2) wherein A is the radical residuum of a polynuclear dihydric phenol, B is an hydroxyl-containing radical residuum of epichlorohydrin, and m is at least 30; (C) about 15 to about 21% by weight of a liquid anhydride of carboxylic acid; (D) about 4.5 to about 6% by weight of colloidal silica; and wherein said colloidal silica has a surface area of about 50 to about 400 m 2 /gram, and the particles have a diameter of about 5 to about 20 millimicrons; and (E) volatile diluent in an amount sufficient to provide a composition with a viscosity of about 14,000 to about 50,000 centipoises determined with a Haake Rotovisco with a shear rate of 249.6 lsec. for 1.28 minutes at 25° C; and wherein the ratio of (A):(B) is about 7:1 to about 4:1, the above amounts being based upon the total of (A), (B)l, (C), (D), and (E) in said composition.

Claim 27

A surface coated with a cured composition from: (A) about 31 to about 55% by weight of a non-liquid epoxidized novolac represented by the formula: ##STR14## wherein n is at least about 0.2; E is hydrogen or an epoxyalkyl group, at least two E groups per polymer molecule being an epoxyalkyl group and wherein the epoxyalkyl group is represented by the formula: ##STR15## p is an integer from 1-8; R is hydrogen or alkyl or alkylene or aryl or aralkyl or alkaryl or cycloalkyl or furyl group; each R 1 individually is hydrogen or alkyl group of up to 7 carbon atoms; wherein the number of carbon atoms in any epoxyalkyl group totals no more than 10 carbon atoms, each X and Y is individually hydrogen or chlorine or alkyl or hydroxyl; each R 2 individually is hydrogen or chlorine or a hydrocarbon group; (B) about 6 to about 12% by weight of a thermoplastic polyhydroxy ether reaction product of a polynuclear dihydric phenol and epichlorohydrin substantially free of 1,2-epoxy groups having the formula: --O--A--O--B].sub.m ( 2) wherein A is the radical residuum of a polynuclear dihydric phenol, B is an hydroxyl-containing radical residuum of epichlorohydrin, and m is at least 30; (C) about 15 to about 21% by weight of a liquid anhydride of carboxylic acid; (D) about 4.5 to about 6% by weight of colloidal silica; and wherein said colloidal silica has a surface area of about 50 to about 400 m 2 /gram, and the particles have a diameter of about 5 to about 20 millimicrons; and (E) volatile diluent in an amount sufficient to provide a composition with a viscosity of about 14,000 to about 50,000 centipoises determined with a Haake Rotovisco with a shear rate of 249.6 lsec. for 1.28 minutes at 25° C; and wherein the ratio of (A):(B) is about 7:1 to about 4:1, the above amounts being based upon the total of (A), (B)l, (C), (D), and (E) in said composition.

Claim 28

The composition of claim 1 wherein said epoxidized novolak is a non-liquid represented by the formula: ##STR16## wherein n is from about 1.5 to about 2; said thermoplastic polyhydroxy ether is the reaction product of bisphenol-A and epochlorohydrin and is represented by the formula: ##STR17## wherein the molecular weight of said polyhydroxy ether is from about 25,000 to about 38,000; said anhydride is nadic methyl anhydride; and said volatile diluent is a mono or dialkyl ether of ethyleneglycol or derivative thereof, and said composition has a viscosity of about 20,000 to about 50,000 centipoises.

Claim 29

The composition of claim 26 wherein said colloidal silica has a surface area of about 50 to about 400 m 2 /gram and the particles have a diameter of about 5 to about 20 millimicrons.

Claim 30

The composition of claim 26 wherein the amount of said accelerating agent is about 2 to about 6% by weight.

Claim 31

The composition of claim 28 wherein said curing agent is 2-ethoxyhexanoic acid salt of 2,4,6-tris-N,N'-dimethylaminomethyl phenol.

Claim 32

The composition of claim 26 wherein said volatile diluent is a mixture of cellosolve acetate and of diethyl carbitol wherein the composition contains about 15 to 21% by weight of said cellosolve acetate and about 0.1 to about 3% weight of diethyl carbitol.

Claim 33

The composition of claim 26 which contains from about 45 to about 50% by weight of (A), about 7.5 to about 9.5% by weight of (B), about 16 to about 21% by weight of (C), about 4.5 to about 6% by weight of (D), about 15 to about 25% by weight of (E), and from about 2 to about 6% by weight of an accelerating agent (F) for cure of the epoxy wherein said amounts are based upon the total amount of (A), (B), (C), (D), (E), and (F) in said composition.

Claim 34

The composition of claim 31 wherein the ratio of A:B is 5:1 to 6:1.