Method for adhesion of ceramics
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1980-04-25
•
Granted: 1981-10-06
•
Expires: 2000-04-25
Abstract
Abstract A method for providing strong adhesion of two ceramic articles to each other or one ceramic article to an article of metallic copper, which method comprises applying, in the former adhesion, a powder mixture of CuS-LaCrO 3 -SiO 2 -Cu to the opposed surfaces of the two ceramic articles or, in the latter adhesion, a powder mixture of CuS-LaCrO 3 -SiO 2 to the opposed surfaces of the ceramic article and the article of metallic copper and, thereafter, heating the pair of articles in the air at a temperature of from 1000° to 1200° C.
Inventors
- 👤 Yoshihiro Ebata
- 👤 Yasuo Toibana
- 👤 Tsuneo Uetsuki
- 👤 Saburo Kose
- 👤 Makoto Kinoshita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 09:58
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/003; C04B37/005; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B2235/00; C04B2235/02; C04B2235/50; C04B2235/54; C04B2235/5409; C04B2235/5418; C04B2235/5436; C04B2235/5445; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/08; C04B2237/09; C04B2237/12; C04B2237/124; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/36; C04B2237/368; C04B2237/50; C04B2237/60; C04B2237/72
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
127 words
A method for the adhesion of two ceramic articles, which comprises interposing between the opposed surfaces of the two ceramic articles a powder mixture of CuS-LaCrO 3 -SiO 2 -Cu wherein the proportion of CuS to LaCrO 3 -SiO 2 is in the range of from 80:20 to 90:20 by weight and the proportion of LaCrO 3 to SiO 2 is in the range of from 25:75 to 50:50 by weight, pressing the two ceramic articles into fast contact with each other across the interposed layer of powder mixture, and heating these two ceramic articles in the resultant state of fast contact in an oxidizing atmosphere at a temperature in the range of from 1000° to 1200° C. for a period of from 10 to 20 minutes.
Claim 2
Independent Claim
127 words
A method for the adhesion of two ceramic articles, which comprises interposing between the opposed surfaces of the two ceramic articles a powder mixture of CuS-LaCrO 3 -SiO 2 -Cu wherein the proportion of CuS to LaCrO 3 -SiO 2 is in the range of from 80:20 to 90:20 by weight and the proportion of LaCrO 3 to SiO 2 is in the range of from 25:75 to 50:50 by weight, pressing the two ceramic articles into fast contact with each other across the interposed layer of powder mixture, and heating these two ceramic articles in the resultant state of fast contact in an oxidizing atmosphere at a temperature in the range of from 1000° to 1200° C. for a period of from 10 to 20 minutes.
Claim 3
Independent Claim
121 words
A method for the adhesion of two ceramic articles, which comprises interposing between opposed surfaces of the two ceramic articles a paste consisting of a binder and a powder mixture of CuS-LaCrO 3 -SiO 2 -Cu, wherein the proportion of CuS to LaCrO 3 -SiO 2 is in the range of 80:20 to 90:10, by weight, and the proportion of LaCrO 3 to SiO 2 is in the range of 25:75 to 50:50, by weight, pressing the opposed surfaces against each other, with the paste interposed therebetween, and heating the articles in the resultant state of fast contact in an oxidizing atmosphere at a temperature in the range of 1000° to 1200° C. for a period of 10 to 20 minutes.
Claim 4
Independent Claim
121 words
A method for the adhesion of two ceramic articles, which comprises interposing between opposed surfaces of the two ceramic articles a paste consisting of a binder and a powder mixture of CuS-LaCrO 3 -SiO 2 -Cu, wherein the proportion of CuS to LaCrO 3 -SiO 2 is in the range of 80:20 to 90:10, by weight, and the proportion of LaCrO 3 to SiO 2 is in the range of 25:75 to 50:50, by weight, pressing the opposed surfaces against each other, with the paste interposed therebetween, and heating the articles in the resultant state of fast contact in an oxidizing atmosphere at a temperature in the range of 1000° to 1200° C. for a period of 10 to 20 minutes.
Claim 5
Independent Claim
137 words
A method for the adhesion of two ceramic articles, which comprises coating a surface of one of the articles with a paste consisting of a binder and a powder mixture of CuS-LaCrO 3 -SiO 2 , wherein the proportion of CuS to LaCrO 3 -SiO 2 is in the range of 80:20 to 90:10, by weight, and the proportion of LaCrO 3 to SiO 2 is in the range of 25:75 to 50:50, by weight, dusting the surface coated with the paste uniformly with powdered copper, placing a surface of the other article into contact with the coated surface of the one article, and heating the articles in the resultant state of fast contact in an oxidizing atmosphere at a temperature in the range of 1000° to 1200° C. for a period of 10 to 20 minutes.
Claim 6
Independent Claim
137 words
A method for the adhesion of two ceramic articles, which comprises coating a surface of one of the articles with a paste consisting of a binder and a powder mixture of CuS-LaCrO 3 -SiO 2 , wherein the proportion of CuS to LaCrO 3 -SiO 2 is in the range of 80:20 to 90:10, by weight, and the proportion of LaCrO 3 to SiO 2 is in the range of 25:75 to 50:50, by weight, dusting the surface coated with the paste uniformly with powdered copper, placing a surface of the other article into contact with the coated surface of the one article, and heating the articles in the resultant state of fast contact in an oxidizing atmosphere at a temperature in the range of 1000° to 1200° C. for a period of 10 to 20 minutes.
Claim 7
Dependent Claim
16 words
The method according to claim 1 or 2 or 3, wherein the oxidizing atmosphere is air.
Claim 8
Dependent Claim
14 words
The method according to claim 2 or 3, wherein the binder is printing ink.
Claim 9
Dependent Claim
35 words
The method according to claim 3, wherein the amount of powdered copper applied by dusting to the coated surface falls in the range of from 0.1 to 0.3 g per cm 2 of the surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-05 | 1985-04-06 | 1985-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-05 | 1989-04-06 | 1989-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-05 | 1993-04-06 | 1993-10-06 | $7700.00 | Window Closed / Lapsed |