Deoxidizer
Assignee: Tayca Corp
•
Filing: 1979-10-23
•
Granted: 1981-11-10
•
Expires: 1999-10-23
Abstract
Abstract A deoxidizer comprises ferrous carbonate having a specific surface area of at least 20 m2/g. The ferrous carbonate can be combined with a mixture of a reduced iron powder and a metal halide; or an alkli metal hydroxide and/or an alkline earth metal hydroxide or calcium oxide and/or ettringite. The deoxidizer is used for the deoxidation of a package so as to substitute oxygen by carbon dioxide.
Inventors
- 👤 Motohisa Aoki
- 👤 Isao Kawakami
- 👤 Masami Nishihara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:31
CPC Classifications
A; A23; A23B; A23B2/00; A23B2/70; A23B2/704; A23B2/708; A23B2/712; A23B2/717; C; C09; C09K; C09K15/00; C09K15/02
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
65 words
A deoxidizer packed in a gas permeable bag, which comprises: (a) a ferrous carbonate having a specific surface area of at least 20 m 2 /g as the main component, and (b) a component selected from the group consisting of (1) reduced iron powder and a metal halide, (2) an alkali metal hydroxide and/or an alkaline earth metal hydroxide and (3) calcium oxide and/or ettringite.
Claim 2
Dependent Claim
65 words
A deoxidizer packed in a gas permeable bag, which comprises: (a) a ferrous carbonate having a specific surface area of at least 20 m 2 /g as the main component, and (b) a component selected from the group consisting of (1) reduced iron powder and a metal halide, (2) an alkali metal hydroxide and/or an alkaline earth metal hydroxide and (3) calcium oxide and/or ettringite.
Claim 3
Dependent Claim
68 words
The deoxidizer of claim 1, wherein when said component (b) is component (1), said reduced iron powder is incorporated in said deoxidizer in an amount of 0.01 to 5 parts by weight per part by weight of said ferrous carbonate and the metal halide is incorporated in said deoxidizer in an amount of 0.0001 to 1 part by weight per part by weight of said reduced iron powder.
Claim 4
Dependent Claim
12 words
The deoxidizer of claim 1, wherein the metal halide is sodium chloride.
Claim 5
Dependent Claim
37 words
The deoxidizer of claim 1, wherein when said component (b) is said component (2), the amount of hydroxide incorporated in said deoxidizer ranges from 0.05 to 2 parts by weight per part by weight of ferrous carbonate.
Claim 6
Dependent Claim
11 words
The deoxidizer of claim 4, wherein the hydroxide is calcium hydroxide.
Claim 7
Dependent Claim
39 words
The deoxidizer of claim 1, wherein said component (b) is component (3), said calcium oxide is incorporated in said deoxidizer in an amount of 6 to 25 parts by weight per 100 parts by weight of said ferrous carbonate.
Claim 8
Dependent Claim
39 words
The deoxidizer of claim 1, wherein when said component (b) is component (3) said ettringite is incorporated in said deoxidizer in an amount of 12 to 50 parts by weight per 100 parts by weight of said ferrous carbonate.
Claim 9
Dependent Claim
42 words
The deoxidizer of claim 1, wherein when said component (b) is component (3), 4 to 20 parts by weight of calcium oxide and 10 to 40 parts by weight of ettringite are combined with 100 parts by weight of said ferrous carbonate.
Claim 10
Dependent Claim
53 words
The deoxidizer of claim 1, wherein when said component (b) is component (3), 3 to 18 parts by weight of calcium oxide, 8 to 35 parts by weight of ettringite and 4 to 16 parts by weight of an alkali metal hydroxide are combined with 100 parts by weight of said ferrous carbonate.
Claim 11
Dependent Claim
55 words
The deoxidizer according to claim 1, wherein when said component (b) is component (3), 3 to 18 parts by weight of calcium oxide, 8 to 35 parts by weight of ettringite and 4 to 16 parts by weight of an alkaline earth metal hydroxide are combined with 100 parts by weight of said ferrous carbonate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-09 | 1985-05-11 | 1985-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-09 | 1989-05-11 | 1989-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-09 | 1993-05-11 | 1993-11-10 | $7700.00 | Window Closed / Lapsed |