Method for manufacturing a thin and flexible ribbon of superconductor material
Assignee: Individual
•
Filing: 1980-07-21
•
Granted: 1982-07-13
•
Expires: 2000-07-21
Abstract
Abstract A method for manufacturing a thin and flexible ribbon of superconductor material such as V 3 Sn, V 3 Ge, V 3 Si, Nb 3 Sn, Nb 3 Ge, Nb 3 Si and La-Au having a fine and compact microscopic structure comprises heating raw superconductor material at a temperature within the range between its melting point and 300° C. above the melting point to form a melt having suitable wettability and viscosity; ejecting the melt through a nozzle under a pressure within the range from 0.01 to 1.5 atm. against a cooling surface of a moving substrate such as a rotating drum; and cooling instantaneously and very rapidly a jet flow of the melt on the cooling surface at a cooling rate of 1,000° C. to 1,000,000° C./sec. In order to manufacture the thin elongated ribbon of excellent configuration it is preferable to effect the cooling in a reduced atmosphere. The invention also provides the thin and flexible ribbon processed by the above mentioned process. When an intermetallic compound such as Nb-Si, Nb-Sn, Nb-Ge, V-Si, V-Sn and V-Ge is used as the raw superconductor material a thin and flexible ribbon of superconductor material having essentially a crystalline structure is formed. When La 1-x (Au y Cu 1-y ) x , wherein x>0.9, 0≦y≦1 is used as the raw superconductor material it is possible to obtain a thin and flexible ribbon of superconductor material having essentially a fine and compact crystalline structure mixed with amorphous of 10 to 90%.
Inventors
- 👤 Noboru Tsuya
- 👤 Kenichi Arai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:16
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/005; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0128; Y; Y10; Y10S; Y10S400/00; Y10S400/901; Y10S428/00; Y10S428/922; Y10S428/9265; Y10S428/93; Y10S505/00; Y10S505/80; Y10S505/801; Y10S505/805; Y10S505/806; Y10S505/812; Y10S505/813; Y10S505/815; Y10S505/822; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014; Y10T428/00; Y10T428/12; Y10T428/12431; Y10T428/12465; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/268
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
164 words
A thin and flexible ribbon of superconductor material having a fine and compact microscopic structure, processed by: (a) heating a material consisting essentially of a raw superconductor material selected from the group of intermetallic compounds consisting of Nb-Si, Nb-Sn, Nb-Ge, V-Si, V-Sn, V-Ge, La-Au, and La 1-x (Au y Cu 1-y )x, wherein x>0.9, 0≦y≦1 to form a uniform melt at a temperature within the range between the melting point of the raw material and 300° C. above the melting point; (b) adding a glass former selected from the group consisting of boron, bismuth, phosphorous, antimony, gallium, tin, in an amount not greater than 50 atomic percent of the raw superconductor material to the melt to produce a melt having suitable wettability and viscosity; (c) ejecting the melt through a nozzle under a pressure of 0.01-1.5 atm. against a cooling surface of a moving substrate; and (d) cooling a jet flow of the melt at a cooling rate of 1,000° C. to 1,000,000° C./sec.
Claim 2
Dependent Claim
164 words
A thin and flexible ribbon of superconductor material having a fine and compact microscopic structure, processed by: (a) heating a material consisting essentially of a raw superconductor material selected from the group of intermetallic compounds consisting of Nb-Si, Nb-Sn, Nb-Ge, V-Si, V-Sn, V-Ge, La-Au, and La 1-x (Au y Cu 1-y )x, wherein x>0.9, 0≦y≦1 to form a uniform melt at a temperature within the range between the melting point of the raw material and 300° C. above the melting point; (b) adding a glass former selected from the group consisting of boron, bismuth, phosphorous, antimony, gallium, tin, in an amount not greater than 50 atomic percent of the raw superconductor material to the melt to produce a melt having suitable wettability and viscosity; (c) ejecting the melt through a nozzle under a pressure of 0.01-1.5 atm. against a cooling surface of a moving substrate; and (d) cooling a jet flow of the melt at a cooling rate of 1,000° C. to 1,000,000° C./sec.
Claim 3
Dependent Claim
27 words
A thin and flexible ribbon of superconductor material as defined in claim 1, wherein the ribbon has a thickness within the range from 5 to 200 μm.
Claim 4
Dependent Claim
41 words
A thin and flexible ribbon of superconductor material as defined in claim 1, wherein the ribbon includes a fine crystalline grain structure, and wherein more than 50% of the grains have a diameter within the range from 1 to 100 μm.
Claim 5
Dependent Claim
44 words
A thin and flexible ribbon of superconductor material as defined in claim 1, wherein the raw superconductive material is an intermetallic compound selected from the group consisting of Nb-Si, Nb-Sn, Nb-Ge, V-Si, V-Sn and V-Ge, and wherein the ribbon is essentially of crystalline texture.
Claim 6
Dependent Claim
51 words
A thin and flexible ribbon of superconductor material as defined in claim 1, wherein the raw material is an intermetallic compound selected from the group consisting of La-Au and La 1-x (Au y Cu 1-y ) x , wherein x>0.9, 0≦y≦1 and wherein the ribbon is in essentially an amorphous state.
Claim 7
Independent Claim
204 words
A method of manufacturing a thin and flexible ribbon of superconductor material having a fine and compact microscopic structure comprising: (a) heating a material consisting essentially of a raw superconductor material selected from the group of intermetallic compounds consisting of Nb-Si, Nb-Sn, Nb-Ge, V-Si, V-Sn, V-Ge, La-Au, and La 1-x (Au y Cu 1-y )x, wherein x>0.9, 0≦y≦1 to form a uniform melt at a temperature of within the range between the melting point of raw material and 300° C. above said melting point to produce a melt having a suitable wettability and viscosity; (b) adding a glass former selected from the group consisting of boron, bismuth, phosphorous, antimony, gallium, and tin in an amount of not greater than 50 atomic percent of the raw superconductor to the melt; (c) ejecting the melt through a nozzle under a pressure of 0.01-1.5 atm. against an outer cooling surface of a moving substrate having good wettability for said melt; and (d) cooling a jet flow of the melt at a cooling rate of 1,000° C. to 1,000,000° C./sec, whereby a flexible ribbon of superconductor material having a microscopic crystalline structure mixed with an amorphous state in a ratio of from about 10 to 90% is produced.
Claim 8
Independent Claim
204 words
A method of manufacturing a thin and flexible ribbon of superconductor material having a fine and compact microscopic structure comprising: (a) heating a material consisting essentially of a raw superconductor material selected from the group of intermetallic compounds consisting of Nb-Si, Nb-Sn, Nb-Ge, V-Si, V-Sn, V-Ge, La-Au, and La 1-x (Au y Cu 1-y )x, wherein x>0.9, 0≦y≦1 to form a uniform melt at a temperature of within the range between the melting point of raw material and 300° C. above said melting point to produce a melt having a suitable wettability and viscosity; (b) adding a glass former selected from the group consisting of boron, bismuth, phosphorous, antimony, gallium, and tin in an amount of not greater than 50 atomic percent of the raw superconductor to the melt; (c) ejecting the melt through a nozzle under a pressure of 0.01-1.5 atm. against an outer cooling surface of a moving substrate having good wettability for said melt; and (d) cooling a jet flow of the melt at a cooling rate of 1,000° C. to 1,000,000° C./sec, whereby a flexible ribbon of superconductor material having a microscopic crystalline structure mixed with an amorphous state in a ratio of from about 10 to 90% is produced.
Claim 9
Dependent Claim
32 words
A method as defined in claim 6, wherein the raw material of superconductor is heated at a temperature within the range between the melting point and 100°-150° C. above the melting point.
Claim 10
Dependent Claim
36 words
A method as defined in claim 6, wherein the step of ejecting of the the melt against the cooling surface of the moving substrate is carried out in an inert gas atmosphere at a reduced pressure.
Claim 11
Dependent Claim
27 words
A method as defined in claim 6, wherein the step of ejecting the melt against the cooling surface of the moving substrate is conducted in a vacuum.
Claim 12
Dependent Claim
46 words
A method as defined in claim 6, wherein said nozzle for ejecting the melt comprises a heat resistant material selected from the group consisting of boron nitride, silicon nitride, silicon carbide, ceramics, fused silica, semi-fused alumina, magnesia, beryllium, platinum, platinum-rhodium, tungsten, molybdenum, tantalum, titanium and carbon.
Claim 13
Dependent Claim
27 words
A method as defined in claim 10, wherein the nozzle is lined with boron nitride in at least the edge and inner edge portion of the nozzle.
Claim 14
Dependent Claim
27 words
A method as defined in claim 6, wherein the pressure for ejecting the melt through the nozzle is selected from the range from 0.01 to 1.5 atm.
Claim 15
Dependent Claim
29 words
A method as defined in claim 6, wherein the cooling substrate is made of material selected from the group consisting of copper, copper-beryllium, brass, stainless steel and carbon steel.
Claim 16
Dependent Claim
34 words
A method as defined in claim 6, wherein the rotating cooling substrate is selected from a rotating drum and disc having at least one of a smooth inner surface and a smooth outer surface.
Claim 17
Dependent Claim
21 words
A method as defined in claim 6, wherein the cooling substrate is an endless belt conveyor having a smooth outer surface.
Claim 18
Dependent Claim
25 words
A method as defined in claim 6, wherein the nozzle comprises a single hole selected from the group consisting of circular, elliptical and rectangular configurations.
References Cited (Backward Citations)
US1756196A
Cited
US3427154A
Cited
US3381739A
Cited
US3595693A
Cited
US3576207A
Cited
US3596804A
Cited
US3645657A
Cited
US3748728A
Cited
US3838185A
Cited
US3845805A
Cited
US3896203A
Cited
DE2424840C3
Cited
US4000014A
Cited
GB1459716A
Cited
US4138445A
Cited
GB1525959A
Cited
GB1540771A
Cited
GB1549124A
Cited
US4221257A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-12 | 1986-01-11 | 1986-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-12 | 1990-01-11 | 1990-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-12 | 1994-01-11 | 1994-07-13 | $7700.00 | Window Closed / Lapsed |