Production of super-smooth articles
Assignee: United States Department of Energy
•
Filing: 1981-05-29
•
Granted: 1983-03-15
•
Expires: 2001-05-29
Abstract
Abstract Super-smooth rounded or formed articles made of thermoplastic materials including various poly(methyl methacrylate) or acrylonitrile-butadiene-styrene copolymers are produced by immersing the articles into a bath, the composition of which is slowly changed with time. The starting composition of the bath is made up of at least one solvent for the polymer and a diluent made up of at least one nonsolvent for the polymer and optional materials which are soluble in the bath. The resulting extremely smooth articles are useful as mandrels for laser fusion and should be useful for a wide variety of other purposes, for example lenses.
Inventors
- 👤 David V. Duchane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:22
CPC Classifications
A; A61; A61K; A61K9/00; A61K9/0012; A61K9/0019; A61K9/0024; B; B29; B29C; B29C71/00; B29C71/0009; G; G21; G21F; G21F1/00; G21F1/02; G21F1/10; B29K; B29K2033/00; B29K2033/04; B29K2033/12; B29K2055/00; B29K2055/02; Y; Y10; Y10T; Y10T428/00; Y10T428/31
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
174 words
A method of smoothing the surface of an article comprising a first material selected from the group consisting of poly(methyl methacrylate) and acrylonitrile-butadiene-styrene polymers, said method comprising: (a) immersing at least a portion of said article into a bath consisting essentially of (1) at least one solvent for said first material and (2) a diluent consisting essentially of at least one nonsolvent for said first material and optional accessory material which is soluble in said bath; and (b) slowly removing said solvent from said bath by diluting said bath with said diluent, wherein said nonsolvent is a mixture of water and a water-soluble polymer having a molecular weight within the range from about 2000 to about 20,000, wherein said at least one solvent is selected from the group consisting of ketones and esters which show some significant mutual solubility with water, and wherein the rate of dilution of said bath is such that it results in extraction of said solvent from said first material on a molecular scale, rather than on a massive scale.
Claim 2
Independent Claim
174 words
A method of smoothing the surface of an article comprising a first material selected from the group consisting of poly(methyl methacrylate) and acrylonitrile-butadiene-styrene polymers, said method comprising: (a) immersing at least a portion of said article into a bath consisting essentially of (1) at least one solvent for said first material and (2) a diluent consisting essentially of at least one nonsolvent for said first material and optional accessory material which is soluble in said bath; and (b) slowly removing said solvent from said bath by diluting said bath with said diluent, wherein said nonsolvent is a mixture of water and a water-soluble polymer having a molecular weight within the range from about 2000 to about 20,000, wherein said at least one solvent is selected from the group consisting of ketones and esters which show some significant mutual solubility with water, and wherein the rate of dilution of said bath is such that it results in extraction of said solvent from said first material on a molecular scale, rather than on a massive scale.
Claim 3
Dependent Claim
26 words
A method according to claim 1, wherein said first material is poly(methyl methacrylate), wherein said solvent is acetone, and wherein said water-soluble polymer is polyethylene glycol.
Claim 4
Dependent Claim
23 words
A method according to claim 1, wherein said polyethylene glycol has a molecular weight within the range from about 3000 to about 6000.
Claim 5
Dependent Claim
31 words
A method according to claim 3, wherein the starting composition of said bath is a volume ratio of said solvent:diluent which is within the range from about 40:60 to about 80:20.
Claim 6
Dependent Claim
26 words
A method according to claim 4, wherein the weight ratio of water:polyethylene glycol in said nonsolvent is within the range from about 75:25 to about 40:60.
Claim 7
Dependent Claim
50 words
A method according to claim 5, wherein said polyethylene glycol has a molecular weight of about 4000, wherein said weight ratio of water:polyethylene glycol in said nonsolvent is about 50:50, and wherein the starting composition of said bath is a volume ratio of said acetone:said diluent which is about 75:25.
Claim 8
Dependent Claim
31 words
A method according to claim 1 wherein said water-soluble polymer is polyvinylpyrrolidone (having a molecular weight of about 10,000) and wherein said nonsolvent includes also a small amount of isopropyl alcohol.
Claim 9
Dependent Claim
31 words
A method according to claim 7 wherein the starting composition of said bath has a volume ratio of solvent: diluent which is within the range from about 25:75 to about 65:35.
Claim 10
Dependent Claim
33 words
A method according to claim 8, wherein the weight ratio of polyvinylpyrrolidone:water is about 50:50 and wherein the starting composition of said bath is a volume ratio of solvent:diluent which is about 50:50.
Claim 11
Dependent Claim
27 words
A method according to claim 1 wherein said first material is an acrylonitrile-butadiene-styrene copolymer, wherein said solvent is acetone and wherein said water-soluble polymer is polyethylene glycol.
Claim 12
Dependent Claim
28 words
A method according to claim 10, wherein the starting composition of said bath has a volume ratio of solvent:diluent within the range from about 40:60 to about 80:20.
Claim 13
Dependent Claim
36 words
A method according to claim 11, wherein the starting composition of said bath has a volume ratio of acetone:diluent of 75:25 and wherein said diluent was 50 weight percent polyethylene glycol-4000 and 50 weight percent water.
References Cited (Backward Citations)
US2209940A
Cited
US2572719A
Cited
US3625755A
Cited
US3684553A
Cited
US4133912A
Cited
US4302418A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-14 | 1986-09-13 | 1987-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-14 | 1990-09-13 | 1991-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-14 | 1994-09-13 | 1995-03-15 | $7700.00 | Window Closed / Lapsed |