Zinc plating baths with condensating polymer brighteners

Claim 2

A zinc electroplating bath comprising a conductive aqueous solution containing zinc ions and a brightening amount of a water soluble brightening additive selected from the group consisting of a monomer of the following general formula and polymers thereof: ##STR9## wherein: n is from 1 to about 6; Y is --OX, --NX 2 , --SO 3 H, --SO 3 M, --COOH, --COOM, --SX, or --CN; X is H, or an alkanol, alkamine, sulfoalkyl, carboxyalkyl, hydroxyaryl, sulfoaryl, carboxyaryl, or aminoaryl having from 1 to about 10 carbon atoms; M is H, Li, Na, K, Be, Mg or Ca; Q is --OR 4 , --N(R 4 ) 2 , --OZ, --OM, or halogen; Z is an aryl group or a substituted aryl group having from about 6 to about 14 carbon atoms; R 1 is H or an alkyl group having from 1 to about 4 carbon atoms; R 2 is H or an alkyl, alkanol, or alkamine group having from 1 to about 4 carbon atoms, or ##STR10## R 3 is H or an alkyl group having from 1 to about 4 carbon atoms, phenyl, substituted-phenyl, or ##STR11## R 4 is H or an alkyl, alkenyl, alkynyl, alkanol, alkenol, alkynol, keto alkyl, keto alkynyl, keto alkenyl, alkamine, alkoxy, polyalkoxyl, sulfoalkyl, carboxyalkyl, mercapto alkyl, or nitriloalkyl group having from 1 to about 12 carbon atoms, phenyl or substituted phenyl or ##STR12## R 5 is H, --OH, or a hydroxyalkyl group having from 1 to about 4 carbon atoms; r is 1 to about 3; and mixtures thereof.

Claim 3

The bath of claim 1 wherein said brightening additive is selected from the group consisting of: Poly[N-(2-hydroxyethyl) nitrilo di-(ethylpropionate)]; Poly[N-(2-hydroxyethyl) nitrilo di-(N'-(2-hydroxyethyl) propionamide]; Poly[N-(2-hydroxyethyl)-N-(2-cyanoethyl)-β-amino propionic acid]; Tetra[N-methyl N-cyanomethyl β-amino propionate] pentaerythritol; Poly[N-(hydroxy tert-butyl)β-amino β-methylcarboxy methyl propionate]; Poly[N-(2-hydroxypropyl)β-amino-α-methyl aceto methyl propionate]; Poly[N-(2-hydroxyethyl)β-amino-β-phenyl methyl propionate]; Poly[β-tauryl ethyl propionate]; Poly[N,N-di(2-hydroxyethyl)nitrilo β-methyl propionamide]; Poly[N-(3-hydroxypropyl)β-aminopropionamide-(N'-isopropyl-sodium sulfonate]; Poly[N-(2-mercaptoethyl) nitrilo di(methyl propionate)]; Poly[N-(2-carboxyethyl)β-amine di(butyl propionate)]; Poly[N-(hydroxyethyl aminoethyl)β-amino(2-methoxyethyl) propionate]; Poly[N-(2-hydroxyethyl) nitrilo di-(2-ethyl hexyl propionate)]; N-(2-hydroxypropyl) nitrilo di-(polyethoxy propionate) where the molecular weight of the polyether group is 2000-4000; Tetra[N-(2-hydroxyethyl β-amino propionate] pentaerythritol; and mixtures thereof.

Claim 4

The bath of claim 1 or 2 wherein said brightening additive is present in an amount of from about 0.1 mg/l to about 10 g/l.

Claim 5

The bath of claim 1 or 2 wherein said brightening additive is present in an amount of from about 0.015 g/l to about 2 g/l.

Claim 6

The bath of claim 1 or 2 wherein said bath has a pH of from about 0 to about 6.

Claim 7

The bath of claim 1 or 2 wherein said bath has a pH of from about 9 to about 14.

Claim 8

The bath of claim 1 or 2 wherein said bath has a pH of from about 6 to about 9 and contains chelating agents to keep the zinc ions in solution.

Claim 9

A process for electroplating a zinc deposit onto a substrate comprising electrodepositing zinc from a conductive aqueous solution containing zinc ions and a brightening amount of a water soluble brightening additive selected from the group consisting of a monomer of the following general formula and polymers thereof: ##STR13## wherein: n is from 1 to about 6; Y is --OX, --NX 2 , --SO 3 H, --SO 3 M, --COOH, --COOM, --SX, or --CN; X is H, or an alkanol, alkamine, sulfoalkyl, carboxyalkyl, hydroxyaryl, sulfoaryl, carboxyaryl, or aminoaryl having from 1 to about 10 carbon atoms; M is H, Li, Na, K, Be, Mg or Ca; Q is --OR 4 , --N(R 4 ) 2 , --OZ, --OM, or halogen; Z is an aryl group or a substituted aryl group having from about 6 to about 14 carbon atoms; R 1 is H or an alkyl group having from 1 to about 4 carbon atoms; R 2 is H or an alkyl, alkanol, or alkamine group having from 1 to about 4 carbon atoms, or ##STR14## R 3 is H or an alkyl group having from 1 to about 4 carbon atoms, phenyl, substituted-phenyl, or ##STR15## R 4 is H or an alkyl, alkenyl, alkynyl, alkanol, alkenol, alkynol, keto alkyl, keto alkynyl, keto alkenyl, alkamine, alkoxy, polyalkoxyl, sulfoalkyl, carboxyalkyl, mercapto alkyl, or nitriloalkyl group having from 1 to about 12 carbon atoms, phenyl or substituted phenyl or ##STR16## R 5 is H, --OH, or a hydroxyalkyl group having from 1 to about 4 carbon atoms; r is 1 to about 3; and mixtures thereof.

Claim 10

A process for electroplating a zinc deposit onto a substrate comprising electrodepositing zinc from a conductive aqueous solution containing zinc ions and a brightening amount of a water soluble brightening additive selected from the group consisting of a monomer of the following general formula and polymers thereof: ##STR13## wherein: n is from 1 to about 6; Y is --OX, --NX 2 , --SO 3 H, --SO 3 M, --COOH, --COOM, --SX, or --CN; X is H, or an alkanol, alkamine, sulfoalkyl, carboxyalkyl, hydroxyaryl, sulfoaryl, carboxyaryl, or aminoaryl having from 1 to about 10 carbon atoms; M is H, Li, Na, K, Be, Mg or Ca; Q is --OR 4 , --N(R 4 ) 2 , --OZ, --OM, or halogen; Z is an aryl group or a substituted aryl group having from about 6 to about 14 carbon atoms; R 1 is H or an alkyl group having from 1 to about 4 carbon atoms; R 2 is H or an alkyl, alkanol, or alkamine group having from 1 to about 4 carbon atoms, or ##STR14## R 3 is H or an alkyl group having from 1 to about 4 carbon atoms, phenyl, substituted-phenyl, or ##STR15## R 4 is H or an alkyl, alkenyl, alkynyl, alkanol, alkenol, alkynol, keto alkyl, keto alkynyl, keto alkenyl, alkamine, alkoxy, polyalkoxyl, sulfoalkyl, carboxyalkyl, mercapto alkyl, or nitriloalkyl group having from 1 to about 12 carbon atoms, phenyl or substituted phenyl or ##STR16## R 5 is H, --OH, or a hydroxyalkyl group having from 1 to about 4 carbon atoms; r is 1 to about 3; and mixtures thereof.

Claim 11

The process of claim 8 wherein said brightening additive is selected from the group consisting of: Poly[N-(2-hydroxyethyl) nitrilo di-(ethylpropionate)]; Poly[N-(2-hydroxyethyl) nitrilo di-(N'-(2-hydroxyethyl) propionamide]; Poly[N-(2-hydroxyethyl)-N-(2-cyanoethyl)-β-amino propionic acid]; Tetra[N-methyl N-cyanomethyl β-amino propionate] pentaerythritol; Poly[N-(hydroxy tert-butyl)β-amino β-methylcarboxy methyl propionate]; Poly[N-(2-hydroxypropyl)β-amino-α-methyl aceto methyl propionate]; Poly[N-(2-hydroxyethyl)β-amino-α-phenyl methyl propionate]; Poly[β-tauryl ethyl propionate]; Poly[N,N-di(2-hydroxyethyl)nitrilo β-methyl propionamide]; Poly[N-(3-hydroxypropyl)β-aminopropionamide-(N'-isopropyl-sodium sulfonate]; Poly[N-(2-mercaptoethyl) nitrilo di(methyl propionate)]; Poly[N-(2-carboxyethyl)β-amine di(butyl propionate)]; Poly[N-(hydroxyethyl aminoethyl)β-amino(2-methoxyethyl) propionate]; Poly[N-(2-hydroxyethyl) nitrilo di-(2-ethyl hexyl propionate)]; N-(2-hydroxypropyl) nitrilo di-(polyethoxy propionate) where the molecular weight of the polyether group is 2000-4000; Tetra[N-2-hydroxyethyl)-β-amino propionate] pentaerythritol; and mixtures thereof.

Claim 12

The process of claim 8 or 9 wherein said brightening additive is present in an amount of from about 0.1 mg/l to about 10 g/l.

Claim 13

The process of claim 8 or 9 wherein said brightening additive is present in an amount of from about 0.015 g/l to about 2 g/l.

Claim 14

The process of claim 8 or 9 wherein said bath has a pH of from about 0 to about 6.

Claim 15

The process of claim 8 or 9 wherein said bath has a pH of from about 9 to about 14.

Claim 16

The process of claim 8 or 9 wherein said bath has a pH of from about 6 to about 9 and contains a chelating agent in an amount effective to keep zinc ions in solution.

Claim 17

The process of claim 8 or 9 wherein said electrodepositing is carried out at a high cathode current density of from about 100 to about 10,000 ASF.

Claim 18

The process of claim 8 or 9 wherein said bath has a pH of from about 0 to about 6 and said electrodepositing is carried out at a high cathode current density of from about 100 to about 10,000 ASF.