US4429003A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Protective coating for porous refractories
Assignee: Saint Gobain Abrasives Inc
•
Filing: 1981-10-05
•
Granted: 1984-01-31
•
Expires: 2001-10-05
Abstract
Abstract A porous refractory object, more particularly a porous silicon carbide igniter is shown, the interconnecting pores and passageways of its body being filled with sub-micron sized silicon carbide particles deposited therein from a slurry coated on the surface of the object, which particles are subsequently oxidized at least on the surface and within the passages or pores in the subjacent surface portion of the body, to provide a protective coating of silica within the pores and on the surfaces of the object to preclude oxidation of the internal phases of the body of the object in oxidizing atmospheres.
Inventors
- 👤 John I. Fredriksson
- 👤 John D. Morrow
- 👤 Giulio A. Rossi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 12:02
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B41/45; C04B41/50; C04B41/5025; C04B41/5035; C04B41/80; C04B41/81; C04B41/85; C04B41/87; F; F23; F23Q; F23Q7/00; F23Q7/22; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249986; Y10T428/249987; Y10T428/249988; Y10T428/24999; Y10T428/25; Y10T428/259; Y10T428/30
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
41 words
A porous refractory article including a coating of the silicon carbide particles having an average particle size of 2 micron or finer, and wherein said fine silicon carbide particles have penetrated into at least the surface pores of said refractory article.
Claim 2
Dependent Claim
41 words
A porous refractory article including a coating of the silicon carbide particles having an average particle size of 2 micron or finer, and wherein said fine silicon carbide particles have penetrated into at least the surface pores of said refractory article.
Claim 3
Dependent Claim
45 words
The porous refractory article of claim 1 wherein at least the fine silicon carbide in the surface pores of said refractory article have been oxidized to silicon dioxide thereby forming a barrier to the passage of oxidizing gases into the body of the refractory article.
Claim 4
Dependent Claim
17 words
A porous refractory body as in claim 2 wherein the body is a sintered silicon carbide element.
Claim 5
Dependent Claim
19 words
A porous refractory body as in claim 3 wherein the sintered silicon carbide element is an electrical resistance heater.
Claim 6
Dependent Claim
14 words
A porous refractory body as in claim 4 wherein the element is an igniter.
Claim 7
Dependent Claim
32 words
A porous refractory body as in claim 2 wherein the body is a sintered element and the silicon carbide has an average particle size with a maximum particle size of 2 microns.
Claim 8
Dependent Claim
36 words
The porous refractory article of claim 1 in which the coating contains an organic or inorganic deflocculating agent in the amount of 0.05 to 1% by weight of the weight of said fine silicon carbide powder.
Claim 9
Dependent Claim
48 words
A porous refractory body as in any one of claims 2, 3, 4, 5, 6, or 7, wherein 0.05 to 1% by weight of a silicate selected from the group consisting of lithium silicate, sodium silicate, potassium silicate, and ammonium silicate is present in said fine silicon carbide.
Claim 10
Dependent Claim
31 words
A porous refractory body as in any one of claims 2, 3, 4, 5, 6, or 7, wherein a small amount of sodium silicate is present in said fine silicon carbide.
Claim 11
Dependent Claim
136 words
A sintered silicon carbide resistance igniter, said igniter having a body with open and interconnected pores having entrances to said pores exposed on the surface thereof including a silicon oxide layer that covers the surface of the body and extends at least into the entrances to said pores which silicon oxide was produced in situ upon the selective oxidation of fine particles of silicon carbide positioned on the surface of the igniter and impregnated deeply into the pores in the igniter body, which silicon carbide particles having been deposited on the surface and within the pores while in a liquid suspension, and said silica layer blocking the pores within said body against oxidation of a portion of said sintered silicon carbide whereby to produce a self healing igniter should any of the surface coating be displaced.
Claim 12
Dependent Claim
136 words
A sintered silicon carbide resistance igniter, said igniter having a body with open and interconnected pores having entrances to said pores exposed on the surface thereof including a silicon oxide layer that covers the surface of the body and extends at least into the entrances to said pores which silicon oxide was produced in situ upon the selective oxidation of fine particles of silicon carbide positioned on the surface of the igniter and impregnated deeply into the pores in the igniter body, which silicon carbide particles having been deposited on the surface and within the pores while in a liquid suspension, and said silica layer blocking the pores within said body against oxidation of a portion of said sintered silicon carbide whereby to produce a self healing igniter should any of the surface coating be displaced.
References Cited (Backward Citations)
US3492153A
Cited
US3481780A
Cited
US3509072A
Cited
US4120829A
Cited
US3875476A
Cited
US3875477A
Cited
US4187344A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-30 | 1987-08-01 | 1988-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-30 | 1991-08-01 | 1992-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-30 | 1995-08-01 | 1996-01-31 | $7700.00 | Window Closed / Lapsed |