Patent US4434191A successfully refreshed from Google Patents.
US4434191A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Integral anti-reflective surfaces of silicate glasses
Assignee: Schott Glass Technologies Inc
•
Filing: 1981-10-06
•
Granted: 1984-02-28
•
Expires: 2001-10-06
Abstract
Abstract Glass surfaces are modified using controlled chemical corrosion to reduce reflection for a variety of existing optical and ophthalmic silicate glass compositions containing at least 5 weight % of alkali metal, using neutral or slightly alkaline aqueous solutions (pH: 7.0-8.5) at temperatures of 20 DEG -100 DEG C. The solutions contain an electrolyte having a dissociation constant greater than 10-6 and contain a polyvalent metal ion. Selection of the proper range of the ratio of glass surface area treated to treating solution volume is critical for achieving satisfactory results for optical applications as well as for making the process simple, repeatable, and inexpensive. Using this invention, antireflective surfaces may be produced on optical devices of complex configuration with high uniformity. Such surfaces provide substantially improved performance in high energy laser systems where exposure to laser light of extremely high intensity and short duration will destroy or degrade conventionally applied coatings.
Inventors
- 👤 Lee M. Cook
- 👤 Karl-Heinz Mader
- 👤 Roland Schnabel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:12
CPC Classifications
H; H01; H01S; H01S3/00; H01S3/0014; C; C03; C03C; C03C23/00; C03C23/008; G; G02; G02B; G02B1/00; G02B1/10; G02B1/12; H01S3/14; H01S3/16; H01S3/17; Y; Y10; Y10T; Y10T428/00; Y10T428/31; Y10T428/315
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
148 words
In a method of preparing an antireflective surface on a silicate glass surface of a particular silicate glass composition containing at least 5 weight % of alkali metal, comprising treating the silicate surface with an aqueous solution of pH 7.0-8.5 which contains an electrolyte with a dissociation constant at 20° C. greater than 10 -6 and which contains a polyvalent cation, the improvement comprising conducting the treatment step with a ratio of the area of said silicate glass surface to the volume of said aqueous treating solution such that the resultant antireflective surface is substantially uniform and has a predetermined wavelength range of minimum reflectance, and, in order to achieve said predetermined wavelength range, adjusting the duration of the treatment step in accordance with a premeasured dependence, for said particular silicate glass composition, of wavelength of minimum reflectance as a function of said ratio and duration of treatment.
Claim 2
Dependent Claim
148 words
In a method of preparing an antireflective surface on a silicate glass surface of a particular silicate glass composition containing at least 5 weight % of alkali metal, comprising treating the silicate surface with an aqueous solution of pH 7.0-8.5 which contains an electrolyte with a dissociation constant at 20° C. greater than 10 -6 and which contains a polyvalent cation, the improvement comprising conducting the treatment step with a ratio of the area of said silicate glass surface to the volume of said aqueous treating solution such that the resultant antireflective surface is substantially uniform and has a predetermined wavelength range of minimum reflectance, and, in order to achieve said predetermined wavelength range, adjusting the duration of the treatment step in accordance with a premeasured dependence, for said particular silicate glass composition, of wavelength of minimum reflectance as a function of said ratio and duration of treatment.
Claim 3
Dependent Claim
21 words
A method of claim 1, wherein said ratio is in the range of 1/1000 to 1/1 cm 2 /cm 3 .
Claim 4
Dependent Claim
21 words
A method of claim 2, wherein said ratio is in the range of 0.05 to 0.4 cm 2 /cm 3 .
Claim 5
Dependent Claim
44 words
A method of claim 1, which comprises preparing antireflective surfaces on multiple silicate surfaces of the same composition and adjusting the duration of treatment to reproducibly achieve essentially the same optical properties for each surface at a predetermined minimum wavelength range for each surface.
Claim 6
Dependent Claim
30 words
A method of claim 1, wherein the concentration of the polyvalent cation is in the range from the concentration of the electrolyte down to 1000 times lower than this concentration.
Claim 7
Dependent Claim
19 words
A method of claim 1, wherein the treatment temperature is 20°-100° C. and the treatment time is 90-12 hours.
Claim 8
Dependent Claim
36 words
A method of claim 1, wherein the electrolyte is 0.01-1 M Na 2 HAs 2 O 4 or Na 2 HPO 4 and the polyvalent cation is 3×10 -4 to 1×10 -3 M Al +3 .
Claim 9
Dependent Claim
16 words
A method of claim 1, wherein the silicate glass surface treated has a borosilicate glass composition.
Claim 10
Dependent Claim
21 words
A method of claim 1 or 8, wherein the silicate glass surface is a surface of a laser system optical element.
Claim 11
Dependent Claim
17 words
A method of claim 9, wherein the optical element is for use in a high energy laser.
Claim 12
Dependent Claim
39 words
A method of claim 1, further comprising, prior to said treatment step, pretreating the silicate glass surface with an aqueous solution as defined in claim 1 except containing essentially none of said polyvalent cation, whereby said surface is modified.
Claim 13
Dependent Claim
60 words
A method of claim 1 or 11 which is for preparing an antireflective surface on said silicate glass surface and then removing the same, further comprising, after said treatment step, post-treating the resultant antireflective silicate glass surface with an aqueous solution as defined in claim 1 except containing essentially none of said polyvalent cation, whereby the antireflective surface is removed.
Claim 14
Dependent Claim
34 words
A method of claim 12, wherein the aqueous solution used in the surface removal step is the same as that used in the treatment for applying the antireflective surface except for the polyvalent cation.
Claim 15
Dependent Claim
30 words
A method of claim 1, wherein the silicate glass surface is on a substrate which is not composed of silicate glass containing at least 5 wt % of alkali metal.
Claim 16
Dependent Claim
13 words
A method of claim 1, wherein said aqueous solution further comprises silicic acid.
Claim 17
Dependent Claim
18 words
A method of claim 1 which is conducted in a container which is inert to said aqueous solution.
Claim 18
Dependent Claim
18 words
A method of claim 2 which conducted in a container which is is inert to said aqueous solution.
Claim 19
Dependent Claim
18 words
A method of claim 3 which is conducted in a container which is inert to said aqueous solution.
Claim 20
Dependent Claim
18 words
A method of claim 7 which is conducted in a container which is inert to said aqueous solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-27 | 1987-08-29 | 1988-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-27 | 1991-08-29 | 1992-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-27 | 1995-08-29 | 1996-02-28 | $7700.00 | Window Closed / Lapsed |