Recoating of electrodes
Assignee: ELECTRODE Corp A CORP OF
•
Filing: 1982-03-08
•
Granted: 1984-05-01
•
Expires: 2002-03-08
Abstract
Abstract Used dimensionally stable electrodes having a valve-metal base and an originally conductive and electrocatalytic coating of e.g. ruthenium-titanium oxide are cleaned and activated by impregnation with a relatively dilute solution preferably containing only a decomposable platinum-group metal compound, followed by heating to enrich the old coating with platinum-group metal/oxide. A new outer electrocatalytic coating which is the same as or similar to the old coating is then applied on top.
Inventors
- 👤 Jean M. Hinden
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:21
CPC Classifications
C; C25; C25B; C25B11/00; C25B11/04; C25B11/051; C25B11/055; C25B11/057; C25B11/061; C25B11/063; C25B11/02; C25B11/073; C25B11/091; C25B11/093
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
222 words
A method of recoating previously-used dimensionally stable electrodes having a valve metal base and an originally conductive and electrocatalytic coating containing at least one oxide of a platinum-group metal and at least one oxide of a valve metal optionally with at least one other metal oxide, which comprises cleaning the electrode surface by removing loose material and foreign matter without removing adhering portions of the coating, and applying a new electrocatalytic coating similar in composition to the old coating over the old coating in a number of layers with drying and baking of each layer, characterized by activating the electrode surface after the cleaning and before application of the new electrocatalytic coating by applying to the cleaned electrode surface one or more coats of an essentially valve-metal free solution containing at least one decomposable compound of a platinum-group metal not present in said old or new coatings, allowing each coat of said solution to impregnate the old coating, drying and baking each applied coat to enrich the old coating with platinum group metal and/or oxide, said solution also containing an agent which attacks valve metal oxide in the old coating and converts it into ions of the valve metal which mix with compound(s) of platinum group metal and form compound(s) of valve metal and platinum-group metal and/or oxide during the baking step.
Claim 2
Independent Claim
222 words
A method of recoating previously-used dimensionally stable electrodes having a valve metal base and an originally conductive and electrocatalytic coating containing at least one oxide of a platinum-group metal and at least one oxide of a valve metal optionally with at least one other metal oxide, which comprises cleaning the electrode surface by removing loose material and foreign matter without removing adhering portions of the coating, and applying a new electrocatalytic coating similar in composition to the old coating over the old coating in a number of layers with drying and baking of each layer, characterized by activating the electrode surface after the cleaning and before application of the new electrocatalytic coating by applying to the cleaned electrode surface one or more coats of an essentially valve-metal free solution containing at least one decomposable compound of a platinum-group metal not present in said old or new coatings, allowing each coat of said solution to impregnate the old coating, drying and baking each applied coat to enrich the old coating with platinum group metal and/or oxide, said solution also containing an agent which attacks valve metal oxide in the old coating and converts it into ions of the valve metal which mix with compound(s) of platinum group metal and form compound(s) of valve metal and platinum-group metal and/or oxide during the baking step.
Claim 3
Dependent Claim
36 words
The method of claim 1, wherein the baking is carried out in an oxidizing atmosphere whereby the platinum-group metal from said solution forms a mixed platinum-group-valve metal oxide with valve metal ions from the old coating.
Claim 4
Dependent Claim
87 words
The method of claim 1 or 2, wherein after cleaning the electrode to be recoated has exposed areas of valve metal which are to be recoated with the new coating, said agent of the solution also attacking valve metal and converting valve metal from said exposed areas of the base into ions which are converted into a compound of the valve metal during the heating step to form in said exposed areas a barrier layer film of the valve metal compound incorporating the platinum-group metal and/or oxide.
Claim 5
Dependent Claim
36 words
The method of claim 1 wherein said solution also contains at least one decomposable compound of a non-valve metal, the amount of such non-valve metal compound(s) being less than the amount of platinum-group metal compound(s) therein.
Claim 6
Dependent Claim
25 words
The method of claim 4, wherein the activating solution contains at least one decomposition compound of cobalt, manganese, tin, bismuth, antimony, lead, iron or nickel.
Claim 7
Dependent Claim
24 words
The method of claim 1 or 4, wherein the activating solution contains 1-35 g/l, as metal, of the platinum-group metal and other metal compound(s).
Claim 8
Dependent Claim
19 words
The method of claim 6, wherein the activating solution contains 5-15 g/l, as metal, of the platinum-group metal compound(s).
Claim 9
Dependent Claim
38 words
The method of claim 6, wherein the new electrocatalytic coating is deposited from a solution which is more concentrated in metals than the activating solution and contains 35-150 g/l, as metal, of platinum-group metal and other metal compounds.
Claim 10
Dependent Claim
27 words
The method of claim 1, wherein the old coating is enriched with 0.1-1 g/m 2 , as metal, of platinum-group metal and/or oxide by the activating procedure.
Claim 11
Dependent Claim
33 words
The method of claim 1, wherein the activation includes the step of heating the electrode in a non-oxidizing atmosphere at a temperature of 350°-650° C. prior to or after applying the activating solution.
References Cited (Backward Citations)
US4318795A
Cited
US3773554A
Cited
US3684543A
Cited
SU522284A1
Cited
US4112140A
Cited
US4214971A
Cited
US4285798A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-01 | 1987-10-31 | 1988-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-01 | 1991-10-31 | 1992-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-01 | 1995-10-31 | 1996-05-01 | $7700.00 | Window Closed / Lapsed |