Reflector and method for manufacturing the same
Assignee: NHK Spring Co Ltd
•
Filing: 1981-12-22
•
Granted: 1984-07-03
•
Expires: 2001-12-22
Abstract
Abstract A reflector includes a base body made of a metallic material having substantially the same ionization potential as that of aluminum. A reflecting layer made of aluminum is formed over one surface of the base body by vacuum deposition. A light-transmitting water-insoluble inorganic oxide layer is formed on the aluminum reflecting layer. The light-transmitting inorganic oxide layer has its micropores sealed by H 2 O a carboxylate of an iron family element having a low valence.
Inventors
- 👤 Shitomi Katayama
- 👤 Hajime Shimabukuro
- 👤 Suguru Nomura
- 👤 Hiroyuki Kurita
- 👤 Akira Ohno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:36
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/06; B05D5/067; C; C23; C23C; C23C14/00; C23C14/06; C23C14/08; C23C14/58; G02B1/105; G; G02; G02B; G02B1/00; G02B1/10; G02B1/14; G02B5/00; G02B5/08; G02B5/0808; B05D2350/00; B05D2350/30; B05D2350/50; B05D2350/60; B05D2350/65; Y; Y10; Y10S; Y10S359/00; Y10S359/90; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12556; Y10T428/12569; Y10T428/12597; Y10T428/12604; Y10T428/12736; Y10T428/12993; Y10T428/31
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
87 words
A reflector comprising a base body made of a metallic material having substantially the same ionization potential as that of aluminum, an aluminum reflecting layer vacuum deposited on one surface of said base body directly or through a smoothing layer formed on the base body, a light-transmitting water-formed insoluble inorganic oxide layer directly vacuum deposited on said reflecting layer, and a sealing agent comprising H 2 O or a carboxylate of an iron family element having a low valence and sealing micropores of said inorganic oxide layer.
Claim 2
Dependent Claim
87 words
A reflector comprising a base body made of a metallic material having substantially the same ionization potential as that of aluminum, an aluminum reflecting layer vacuum deposited on one surface of said base body directly or through a smoothing layer formed on the base body, a light-transmitting water-formed insoluble inorganic oxide layer directly vacuum deposited on said reflecting layer, and a sealing agent comprising H 2 O or a carboxylate of an iron family element having a low valence and sealing micropores of said inorganic oxide layer.
Claim 3
Dependent Claim
20 words
A reflector according to claim 1, wherein said reflecting layer is formed on said base body through the smoothing layer.
Claim 4
Dependent Claim
20 words
A reflector according to claim 2, wherein said smoothing layer is formed of an inorganic compound or a resin paint.
Claim 5
Dependent Claim
28 words
A reflector according to any one of claims 1 to 3, comprising an insulating layer covering peripheral sides of at least said base body and said reflecting layer.
Claim 6
Dependent Claim
18 words
A reflector according to claim 4, wherein said insulating layer also covers peripheral side of said smoothing layer.
Claim 7
Dependent Claim
28 words
A reflector according to claim 5, wherein said insulating layer also covers a surface of said base body opposite to the surface covered by said aluminum reflecting layer.
Claim 8
Dependent Claim
19 words
A reflector according to claim 4, wherein said insulating layer also covers peripheral side of said inorganic oxide layer.
Claim 9
Dependent Claim
18 words
A reflector according to claim 1, wherein said reflecting layer has a thickness of 500 to 2,000 Å.
Claim 10
Dependent Claim
19 words
A reflector according to claim 1, wherein said inorganic oxide layer has a thickness of 0.5 to 5 μm.
Claim 11
Independent Claim
120 words
A method for manufacturing a reflector comprising the steps of: (a) forming a reflecting layer by vacuum depositing aluminum directly on one surface of a base body made of a metallic material having substantially the same ionization potential as that of aluminum, or by vacuum depositing aluminum on one surface of said base body through a smoothing layer by vacuum deposition; (b) forming a light-transmitting protective layer on said reflecting layer by directly depositing a water-insoluble inorganic oxide material thereon to provide an intermediate product; and (c) sealing micropores of said protective layer by treating with a sealing agent selected from the group consisting of H 2 O and a carboxylate of an iron family metal having a low valence.
Claim 12
Independent Claim
120 words
A method for manufacturing a reflector comprising the steps of: (a) forming a reflecting layer by vacuum depositing aluminum directly on one surface of a base body made of a metallic material having substantially the same ionization potential as that of aluminum, or by vacuum depositing aluminum on one surface of said base body through a smoothing layer by vacuum deposition; (b) forming a light-transmitting protective layer on said reflecting layer by directly depositing a water-insoluble inorganic oxide material thereon to provide an intermediate product; and (c) sealing micropores of said protective layer by treating with a sealing agent selected from the group consisting of H 2 O and a carboxylate of an iron family metal having a low valence.
Claim 13
Dependent Claim
19 words
A method according to claim 10, wherein said smoothing layer is formed on the surface of said base body.
Claim 14
Dependent Claim
39 words
A method according to claim 10 or 11, further including, between steps (a) and (b), the step of forming an insulating layer which covers pheripheral sides of at least said base body, said smoothing layer and said reflecting layer.
Claim 15
Dependent Claim
26 words
.A method according to claim 12, wherein said insulating layer covers a surface of said base body opposite to the surface covered by the reflecting layer.
Claim 16
Dependent Claim
41 words
A method according to claim 10 or 11, including the step, between steps (b) and (c), of forming an insulating layer which covers pheripheral sides of at least said base body, said smoothing layer, said reflecting layer and said protective layer.
Claim 17
Dependent Claim
27 words
A method according to claim 14, wherein said insulating layer also covers a surface of said base body opposite to the surface covered by the reflecting layer.
Claim 18
Dependent Claim
39 words
A method according to claim 10 or 11, including the step, after step (c), of forming an insulating layer which covers pheripheral sides of at least said base body, said smoothing layer, said reflecting layer and said protective layer.
Claim 19
Dependent Claim
27 words
A method according to claim 16, wherein said insulating layer also covers a surface of said base body opposite to the surface covered by the reflecting layer.
Claim 20
Dependent Claim
22 words
A method according to claim 10 or 11, wherein said reflecting layer is formed to a thickness of 500 to 2,000 Å.
Claim 21
Dependent Claim
22 words
A method according to claim 10 or 11, wherein said protective layer is formed to a thickness of 0.5 to 5 μm.
Claim 22
Dependent Claim
43 words
A method according to claim 10, wherein the step (c) comprises immersing said protective layer in an aqueous solution of the carboxylate under atmospheric pressure or under pressurized conditions at a temperature of 0 to 200° C. for 1 second to 1 hour.
Claim 23
Dependent Claim
30 words
A method according to claim 10, wherein the step (c) comprises spraying said protective layer with an aqueous solution of the carboxylate at a temperature of 0° to 200° C.
Claim 24
Dependent Claim
50 words
A method according to claim 10, wherein the step (c) comprises conducting electrolysis in an aqueous solution of the carboxylate, using the base body of the intermediate product as a cathode, and a metal piece as an anode which is the same kind as the metal of the carboxylate used.
Claim 25
Dependent Claim
35 words
A method according to claim 22, wherein the electrolysis is performed at a voltage of 10 V or less and a current density of 500 mA/cm 2 or less for 5 seconds to 1 hour.
Claim 26
Independent Claim
42 words
A method according to any one of claims 10, 20, 21, 22 or 23, wherein a carboxylic acid component of the carboxylate is selected from the group consisting of acetic acid, propionic acid, butyric acid, lactic acid, citric acid, and tartaric acid.
Claim 27
Dependent Claim
33 words
A method according to claim 10, wherein the step (c) comprises immersing the protective layer in boiling water at a pH of 5 to 9 for a period of time within 20 minutes.
Claim 28
Dependent Claim
47 words
A method according to claim 10, wherein the step (c) comprises allowing the protective layer to stand in a saturated water vapor at a temperature of up to 200° C. for a period of time such that the protective layer is not peeled from the reflecting layer.
Claim 29
Dependent Claim
20 words
A method according to claim 26, wherein the step (c) is conducted at 100° C. for 5 to 20 minutes.
Claim 30
Dependent Claim
20 words
A method according to claim 26, wherein the step (c) is conducted at 150° C. for 2 to 10 minutes.
Claim 31
Dependent Claim
20 words
A method according to claim 26, wherein the step (c) is conducted at 200° C. for 1 to 5 minutes.
References Cited (Backward Citations)
JPS5040348A
Cited
JPS5210741A
Cited
JPS5497155A
Cited
US4364634A
Cited
US4358507A
Cited
US4379196A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-03 | 1988-01-02 | 1988-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-03 | 1992-01-02 | 1992-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-03 | 1996-01-02 | 1996-07-03 | $7700.00 | Window Closed / Lapsed |