Wear-resistant and shock-resistant tools and method of manufacture thereof
Assignee: ACU-EDGE Inc A DE CORP
•
Filing: 1982-09-27
•
Granted: 1984-07-31
•
Expires: 2002-09-27
Abstract
Abstract Wear-resistant and shock-resistant tools are constructed by preforming carbide-containing working parts of high wear resistance and hardness and attaching them to a softer base metal of the tool by means of a highly shock-resistant steel-to-steel fusion weld. The working part is preformed by powdered metallurgy techniques utilizing steel powders having carbide-forming constituents therein which form carbides along the grain boundaries of the steel uniformly throughout the working part as a result of sintering of the compressed powders. Thereafter the fusion welding process renders the carbide structure of the working part nonuniform for optimum shock resistance, without reducing the effective wear resistance thereof, while also forming a highly shock-resistance joint between the working part and the base metal of the tool.
Inventors
- 👤 Fred G. Gunzner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 04:32
CPC Classifications
E; E21; E21B; E21B10/00; E21B10/46; E21B10/58; B; B22; B22F; B22F7/00; B22F7/06; B22F7/062; B23; B23D; B23D65/00; B23K; B23K31/00; B23K31/02; B23K31/025; C; C22; C22C; C22C33/00; C22C33/02; E02; E02F; E02F9/00; E02F9/28; E02F9/2808; E02F9/285; B22F5/00; B22F2005/001; B22F2998/00; Y; Y10; Y10T; Y10T407/00; Y10T407/26; Y10T83/00; Y10T83/929; Y10T83/9319; Y10T83/9367; Y10T83/9457; Y10T83/9464
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
119 words
A tool comprising: (a) a wear-resistant working part formed of steel powders, containing carbide-forming constituents, compressed into a preformed shape and bonded together by heating and containing carbide particles therein formed from said carbide-forming constituents of said steel powders; (b) a body of steel in abutment with said working part, said body of steel having a different composition of lesser hardness than said working part; and (c) a portion of said working part, constituting a minor fraction of said compressed and bonded steel powders, and an abutting portion of said body being fixedly fused with each other by melting and diffusion into each other of both of said portions while in abutment with each other, and subsequent cooling thereof.
Claim 2
Dependent Claim
119 words
A tool comprising: (a) a wear-resistant working part formed of steel powders, containing carbide-forming constituents, compressed into a preformed shape and bonded together by heating and containing carbide particles therein formed from said carbide-forming constituents of said steel powders; (b) a body of steel in abutment with said working part, said body of steel having a different composition of lesser hardness than said working part; and (c) a portion of said working part, constituting a minor fraction of said compressed and bonded steel powders, and an abutting portion of said body being fixedly fused with each other by melting and diffusion into each other of both of said portions while in abutment with each other, and subsequent cooling thereof.
Claim 3
Dependent Claim
29 words
The tool of claim 1 wherein said carbide particles are formed from said carbide-forming constituents along grain boundaries of said compressed and bonded steel powders of said working part.
Claim 4
Dependent Claim
46 words
The tool of claim 1 wherein said carbide particles are distributed nonuniformly through said working part, the concentration of said carbide particles adjacent the junction between said working part and said body of steel being less than the concentration of carbide particles remote from said junction.
Claim 5
Dependent Claim
22 words
The tool of claim 1, 2 or 3 wherein said carbide particles form less than 50% by weight of said working part.
Claim 6
Dependent Claim
22 words
The tool of claim 1, 2 or 3 wherein said carbide particles form less than 30% by weight of said working part.
Claim 7
Dependent Claim
137 words
A process for manufacturing a tool comprising: (a) preforming a wear-resistant working part by compressing steel powders having carbide-forming constituents therein into a preformed shape and bonding said powders together in said shape by heating thereof; (b) abutting a portion of said working part against a mating portion of a body of steel having a different composition of lesser hardness than said working part; (c) during said abutment, applying heat to the abutting portions of said working part and said body respectively sufficient to melt and diffuse into each other both of said respective abutting portions, but insufficient to melt a major fraction of said compressed and bonded steel powders in said working part; and (d) cooling the diffused portions of said working part and said body and thereby fixedly fusing said respective portions to each other.
Claim 8
Dependent Claim
137 words
A process for manufacturing a tool comprising: (a) preforming a wear-resistant working part by compressing steel powders having carbide-forming constituents therein into a preformed shape and bonding said powders together in said shape by heating thereof; (b) abutting a portion of said working part against a mating portion of a body of steel having a different composition of lesser hardness than said working part; (c) during said abutment, applying heat to the abutting portions of said working part and said body respectively sufficient to melt and diffuse into each other both of said respective abutting portions, but insufficient to melt a major fraction of said compressed and bonded steel powders in said working part; and (d) cooling the diffused portions of said working part and said body and thereby fixedly fusing said respective portions to each other.
Claim 9
Dependent Claim
28 words
The process of claim 6, further including forming carbide particles from said carbide-forming constituents along grain boundaries of said compressed and bonded steel powders of said working part.
Claim 10
Dependent Claim
51 words
The process of claim 6, further including forming carbide particles from said carbide-forming constituents nonuniformly through said working part such that the concentration of said carbide particles adjacent the junction between said working part and said body of steel is less than the concentration of carbide particles remote from said junction.
Claim 11
Dependent Claim
18 words
The process of claim 6 further including, prior to step (a), mixing carbide powders with said steel powders.
Claim 12
Dependent Claim
27 words
The process of claim 6, 7, 8 or 9 wherein said working part has carbide particles therein forming less than 50% by weight of said working part.
Claim 13
Dependent Claim
27 words
The process of claim 6, 7, 8 or 9 wherein said working part has carbide particles therein forming less than 30% by weight of said working part.
References Cited (Backward Citations)
US1733241A
Cited
US1901654A
Cited
US2683923A
Cited
US2880768A
Cited
US2833638A
Cited
US3063310A
Cited
US3034378A
Cited
US3104562A
Cited
US3241228A
Cited
US3295396A
Cited
US3718799A
Cited
US3800633A
Cited
US3882594A
Cited
US3766354A
Cited
US4306139A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-31 | 1988-01-30 | 1988-07-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-31 | 1992-01-30 | 1992-07-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-31 | 1996-01-30 | 1996-07-31 | $7700.00 | Window Closed / Lapsed |