Process for preparing adhesive-repellent coatings
Assignee: Wacker Chemie AG
•
Filing: 1984-02-09
•
Granted: 1984-09-25
•
Expires: 2004-02-09
Abstract
Abstract Coatings which have a predetermined degree of adhesive-repellency are prepared by applying to surfaces which are to be rendered adhesive-repellent an organopolysiloxane having Si-bonded hydrogen and an aliphatic multiple bond in the same molecule and a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond, and thereafter crosslinking the organopolysiloxane by the addition of Si-bonded hydrogen to an aliphatic multiple bond. The organopolysiloxane having both an aliphatic multiple bond and Si-bonded hydrogen in the same molecule, has a viscosity of at least 300 mPa.s at 25 DEG C. The adhesive-repellency of the coated substrate is at least partially dependent on the ratio of Si-bonded hydrogen to the aliphatic multiple bond, i.e., the higher the ratio of Si-bonded hydrogen to the aliphatic multiple bond, the lower the adhesive-repellency. Organic compounds containing at least one grouping of the formula <IMAGE> in an amount to retard or prevent the addition of Si-bonded hydrogen to an aliphatic multiple bond at room temperature, are to be excluded from the adhesive-repellent compositions of this invention.
Inventors
- 👤 Friedrich Hockemeyer
- 👤 Gerhard Preiner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:56
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/04; C08; C08L; C08L83/00; C08L83/04; D; D21; D21H; D21H19/00; D21H19/10; D21H19/14; D21H19/24; D21H19/32; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
142 words
An adhesive-repellent composition which may be applied to a substrate to form a coating thereon having a predetermined degree of adhesive-repellency which comprises a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond and an organopolysiloxane in which part of the organopolysiloxane consists of an organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C. and contains both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule, in which the ratio of Si-bonded hydrogen containing siloxane units to SiC-bonded aliphatic multiple bonded siloxane units is between 5:1 and 50:1, with the proviso that an organic compound having at least one group of the formula ##STR5## is not present in the composition in such an amount that it will retard or delay the addition of Si-bonded hydrogen to an aliphatic multiple bond at room temperature.
Claim 2
Dependent Claim
142 words
An adhesive-repellent composition which may be applied to a substrate to form a coating thereon having a predetermined degree of adhesive-repellency which comprises a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond and an organopolysiloxane in which part of the organopolysiloxane consists of an organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C. and contains both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule, in which the ratio of Si-bonded hydrogen containing siloxane units to SiC-bonded aliphatic multiple bonded siloxane units is between 5:1 and 50:1, with the proviso that an organic compound having at least one group of the formula ##STR5## is not present in the composition in such an amount that it will retard or delay the addition of Si-bonded hydrogen to an aliphatic multiple bond at room temperature.
Claim 3
Dependent Claim
150 words
The composition of claim 1, wherein the organopolysiloxane having both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule is represented by the formula R.sup.1 (CH.sub.3).sub.2 SiO(SiR.sub.2 O).sub.m (SiCH.sub.3 HO).sub.n (SiCH.sub.3 R.sup.1 O).sub.x Si(CH.sub.3).sub.2 R.sup.1, where R is selected from the group consisting of monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals which are free of aliphatic multiple bonds; R 1 is a hydrocarbon radical having an aliphatic multiple bond; m and n represent integers, x is 0 or an integer, and the sum of m+n+x is a value in which the average viscosity of the organopolysiloxane is at least 300 mPa.s at 25° C., with at least 3 Si-bonded hydrogen atoms being present per molecule and the ratio of m:n being between 1:1 and 99:1, and the ratio of the SiCH 3 HO units to the units having an R 1 group being between 5:1 and 50:1.
Claim 4
Dependent Claim
118 words
The composition of claim 1, wherein the organopolysiloxane having both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule is represented by the formula (CH.sub.3).sub.3 SiO(SiCH.sub.3 HO).sub.a (SiCH.sub.3 R.sup.1 O).sub.E (SiR.sub.2 O).sub.c Si(CH.sub.3).sub.3 wherein R is selected from the group consisting of monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals, which are free of aliphatic multiple bonds, R 1 is a hydrocarbon radical having an aliphatic multiple bond, a, b and c are each integers with the sum of a+b+c being at least 200, and at least 3 Si-bonded hydrogen atoms are present per molecule, with the ratio of SiCH 3 HO units to the units having an R 1 group being between 5:1 and 50:1.
Claim 5
Dependent Claim
119 words
The composition of claim 1, wherein the organopolysiloxane having both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule is represented by the formula H(CH.sub.3).sub.2 SiO(SiCH.sub.3 HO).sub.d (SiCH.sub.3 R.sup.1 O).sub.e (SiR.sub.2 O).sub.f Si(CH.sub.3).sub.2 H wherein R is selected from the group consisting of monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals, which are free of aliphatic multiple bonds, R 1 is a hydrocarbon radical having an aliphatic multiple bond, d, e and f are each integers with the sum of d+e+f being at least 200, and at least 3 Si-bonded hydrogen atoms are present per molecule, with the ratio of SiCH 3 HO units to the units having an R 1 group being between 5:1 and 50:1;
Claim 6
Dependent Claim
125 words
The composition of claim 1, wherein the organopolysiloxane having both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule is represented by the formula R.sup.1 (CH.sub.3).sub.2 SiO(SiCH.sub.3 HO).sub.g (SiR.sub.2 O).sub.h (SiCH.sub.3 R.sup.1 O).sub.i Si(CH.sub.3).sub.2 H wherein R is selected from the group consisting of monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals, which are free of aliphatic multiple bonds, R 1 is a hydrocarbon radical having an aliphatic multiple bond, g and h are each integers, i is 0 or an integer with the sum of g+h+i being at least 200, and at least 3 Si-bonded hydrogen atoms are present per molecule with the ratio of SiCH 3 HO units to the units having an R 1 group being between 5:1 and 50:1.
Claim 7
Dependent Claim
118 words
The composition of claim 1, wherein the organopolysiloxane having both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule is represented by the formula H(CH.sub.3).sub.2 SiO(SiCH.sub.3 HO).sub.1 (SiR.sub.2 O).sub.p (SiCH.sub.3 R.sup.1 O).sub.q Si(CH.sub.3).sub.3 wherein R is selected from the group consisting of monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals, which are free of aliphatic multiple bonds, R 1 is a hydrocarbon radical having an aliphatic multiple bond, l, p and q are each integers with the sum of l+p+q being at least 200 and at least 3 Si-bonded hydrogen atoms are present per molecule with the ratio of SiCH 3 HO units to the units having an R 1 group being between 5:1 and 50:1.
Claim 8
Dependent Claim
157 words
A process for preparing an adhesive-repellent coating which comprises applying to a substrate to be rendered adhesive-repellent a composition containing an organopolysiloxane and a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond in which part of the organopolysiloxane consists of an organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C., and contains both SiC-bonded groups having an aliphatic multiple bond and an Si-bonded hydrogen in the same molecule, in which the ratio of Si-bonded hydrogen containing siloxane units to SiC-bonded aliphatic multiple bonded siloxane units is between 5:1 and 50:1, with the proviso that an organic compound having at least one group of the formula ##STR6## is not present in the composition in such an amount that it will retard the addition of Si-bonded hydrogen to an aliphatic multiple bond at room temperature and thereafter crosslinking the organopolysiloxane by the addition of Si-bonded hydrogen to an aliphatic multiple bond.
Claim 9
Dependent Claim
157 words
A process for preparing an adhesive-repellent coating which comprises applying to a substrate to be rendered adhesive-repellent a composition containing an organopolysiloxane and a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond in which part of the organopolysiloxane consists of an organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C., and contains both SiC-bonded groups having an aliphatic multiple bond and an Si-bonded hydrogen in the same molecule, in which the ratio of Si-bonded hydrogen containing siloxane units to SiC-bonded aliphatic multiple bonded siloxane units is between 5:1 and 50:1, with the proviso that an organic compound having at least one group of the formula ##STR6## is not present in the composition in such an amount that it will retard the addition of Si-bonded hydrogen to an aliphatic multiple bond at room temperature and thereafter crosslinking the organopolysiloxane by the addition of Si-bonded hydrogen to an aliphatic multiple bond.
Claim 10
Dependent Claim
165 words
The process of claim 7, wherein the organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C. and containing SiC-bonded groups having an aliphatic multiple bond and an Si-bonded hydrogen in the same molecule is represented by the formula R.sup.1 (CH.sub.3).sub.2 SiO(SiR.sub.2 O).sub.m (SiCH.sub.3 HO).sub.n (SiCH.sub.3 R.sup.1 O).sub.x Si(CH.sub.3).sub.2 R.sup.1, where R is selected from the group consisting of monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals which are free of aliphatic multiple bonds; R 1 is a hydrocarbon radical having an aliphatic multiple bond; m and n represent integers, x is 0 or an integer, and the sum of m+n+x is a value in which the average viscosity of the organopolysiloxane is at least 300 mPa.s at 25° C., with at least 3 Si-bonded hydrogen atoms being present per molecule and the ratio of m:n being between 1:1 and 99:1, and the ratio of the SiCH 3 HO units to the units having an R 1 group being between 5:1 and 50:1.
Claim 11
Dependent Claim
133 words
An adhesive-repellent composition which may be applied to a substrate to form a coating thereon having a predetermined degree of adhesive-repellency consisting essentially of a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond and an organopolysiloxane in which part of the organopolysiloxane consists of an organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C. and contains both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule, in which the ratio of Si-bonded hydrogen containing siloxane units to SiC-bonded aliphatic multiple bonded siloxane units is between 5:1 and 50:1, and an inhibitor other than an organic compound having at least one group of the formula ##STR7## which will retard or delay the addition of Si-bonded hydrogen to an aliphatic multiple bond at room temperature.
Claim 12
Dependent Claim
133 words
An adhesive-repellent composition which may be applied to a substrate to form a coating thereon having a predetermined degree of adhesive-repellency consisting essentially of a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond and an organopolysiloxane in which part of the organopolysiloxane consists of an organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C. and contains both SiC-bonded aliphatic multiple bonds and Si-bonded hydrogen in the same molecule, in which the ratio of Si-bonded hydrogen containing siloxane units to SiC-bonded aliphatic multiple bonded siloxane units is between 5:1 and 50:1, and an inhibitor other than an organic compound having at least one group of the formula ##STR7## which will retard or delay the addition of Si-bonded hydrogen to an aliphatic multiple bond at room temperature.
Claim 13
Dependent Claim
147 words
An adhesive-repellent composition which may be applied to a substrate to form a coating thereon having a predetermined degree of adhesive repellency consisting essentially of a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond and an organopolysiloxane in which part of the organopolysiloxane consists of an organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C., and contains both SiC-bonded groups having an aliphatic multiple bond and an Si-bonded hydrogen in the same molecule, in which the ratio of Si-bonded hydrogen containing siloxane units to SiC-bonded aliphatic multiple bonded siloxane units is between 5:1 and 50:1, and an organic solvent, with the proviso that an organic compound having at least one group of the formula ##STR8## is not present in the composition in such an amount that it will retard the addition of Si-bonded hydrogen to an aliphatic multiple bond.
Claim 14
Dependent Claim
147 words
An adhesive-repellent composition which may be applied to a substrate to form a coating thereon having a predetermined degree of adhesive repellency consisting essentially of a catalyst which promotes the addition of Si-bonded hydrogen to an aliphatic multiple bond and an organopolysiloxane in which part of the organopolysiloxane consists of an organopolysiloxane having a viscosity of at least 300 mPa.s at 25° C., and contains both SiC-bonded groups having an aliphatic multiple bond and an Si-bonded hydrogen in the same molecule, in which the ratio of Si-bonded hydrogen containing siloxane units to SiC-bonded aliphatic multiple bonded siloxane units is between 5:1 and 50:1, and an organic solvent, with the proviso that an organic compound having at least one group of the formula ##STR8## is not present in the composition in such an amount that it will retard the addition of Si-bonded hydrogen to an aliphatic multiple bond.
Claim 15
Dependent Claim
12 words
The composition of claim 9, wherein the composition contains an organic solvent.
References Cited (Backward Citations)
US3220972A
Cited
US3445420A
Cited
US3882083A
Cited
US4260726A
Cited
US4421783A
Cited
US4347346A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-25 | 1988-03-26 | 1988-09-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-25 | 1992-03-26 | 1992-09-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-25 | 1996-03-26 | 1996-09-25 | $7700.00 | Window Closed / Lapsed |