Method of producing a semiconductor device
Assignee: Fujitsu Ltd
•
Filing: 1982-09-28
•
Granted: 1984-10-02
•
Expires: 2002-09-28
Abstract
Abstract In a process for producing a semiconductor device, having a thick silicon oxide layer, on an isolation region, an oxide layer is selectively formed on an area for providing the isolation region of the epitaxial layer. Then an anti-oxidation masking layer is selectively formed on the oxide layer. The semiconductor substrate is selectively oxidized using the anti-oxidation masking layer for forming the thick silicon oxide layer. The anti-oxidation masking layer on the silicon oxide layer, which corresponds to the area for providing the isolation region, is removed and impurities are introduced into the area for providing the isolation region. Then the semiconductor substrate is oxidized in an oxidizing atmosphere so that the impurities are activated to form an isolation region and an oxide layer on the isolation region, the oxide layer having an increased thickness. The thus-obtained thick silicon dioxide layer makes the parasitic capacitance between the conductive lines and the isolation region small.
Inventors
- 👤 Tadashi Kiriseko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:56
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/10; H10W10/01; H10W10/011; H10W10/012; H10W10/13; Y; Y10; Y10S; Y10S438/00; Y10S438/981
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
215 words
A method for producing a semiconductor device comprising an epitaxial layer of a first conductivity type formed on a semiconductor substrate of a second conductivity type opposite to the first conductivity type and an isolation region of the second conductivity type, the isolation region reaching to the semiconductor substrate from the surface of the epitaxial layer, said method comprising the steps of: (a) selectively forming a first oxide layer having a first thickness, on an area of the epitaxial layer to provide an isolation region in the epitaxial layer; (b) selectively forming a second oxide layer having a second thickness, on a predetermined region of the epitaxial layer, the first thickness being greater than the second thickness; (c) selectively forming an anti-oxidation masking layer on the second oxide layer; (d) selectively oxidizing the epitaxial layer by using the anti-oxidation masking layer as a mask; (e) selectively forming a photo-resist layer so as to expose the anti-oxidation masking layer formed on the first and second oxide layers through the photo-resist layer; (f) removing the exposed anti-oxidation masking layer by dry etching; (g) introducing second conductivity-type impurities into the area for providing the isolation region; (h) oxidizing the epitaxial layer in an oxidizing atmosphere by using the remaining portions of the anti-oxidation masking layer as a mask.
Claim 2
Independent Claim
215 words
A method for producing a semiconductor device comprising an epitaxial layer of a first conductivity type formed on a semiconductor substrate of a second conductivity type opposite to the first conductivity type and an isolation region of the second conductivity type, the isolation region reaching to the semiconductor substrate from the surface of the epitaxial layer, said method comprising the steps of: (a) selectively forming a first oxide layer having a first thickness, on an area of the epitaxial layer to provide an isolation region in the epitaxial layer; (b) selectively forming a second oxide layer having a second thickness, on a predetermined region of the epitaxial layer, the first thickness being greater than the second thickness; (c) selectively forming an anti-oxidation masking layer on the second oxide layer; (d) selectively oxidizing the epitaxial layer by using the anti-oxidation masking layer as a mask; (e) selectively forming a photo-resist layer so as to expose the anti-oxidation masking layer formed on the first and second oxide layers through the photo-resist layer; (f) removing the exposed anti-oxidation masking layer by dry etching; (g) introducing second conductivity-type impurities into the area for providing the isolation region; (h) oxidizing the epitaxial layer in an oxidizing atmosphere by using the remaining portions of the anti-oxidation masking layer as a mask.
Claim 3
Dependent Claim
17 words
A method as claimed in claim 1, wherein the anti-oxidation masking layer is a silicon nitride layer.
Claim 4
Dependent Claim
44 words
A method as claimed in claim 1, wherein said oxidizing step (d) is carried out at a temperature of approximately 1000° C. for fifty minutes and wherein said oxidizing step (f) is carried out at approximately 1000° C. for one hundred and forty-five minutes.
Claim 5
Dependent Claim
24 words
A method as claimed in claim 1, wherein said step (f) of removing the exposed anti-oxidation masking layer comprises a dry etching removal method.
Claim 6
Independent Claim
317 words
A method for producing a semiconductor device having a semiconductor substrate of a second conductivity type, having an epitaxial layer including first, second and third areas of a first conductivity type opposite that of the second conductivity type formed on the semiconductor substrate and having a buried layer of the first conductivity type formed in the semiconductor substrate, the method comprising the steps of: (a) forming a first oxide layer on the first area of the epitaxial layer; (b) forming a second oxide layer on the first oxide layer and on the second and third areas of the epitaxial layer; (c) selectively forming an anti-oxidation masking layer on the second oxide layer to obtain the first and second oxide layers and the anti-oxidation masking layer on the first area, and to obtain the second oxide layer and the anti-oxidation masking layer on the second area; (d) selectively oxidizing the semiconductor device to form a field insulating layer on the epitaxial layer, a portion of the field insulating layer comprising the first and second oxide layers; (e) selectively covering the field insulating layer with a photoresist layer to form an opening in which the anti-oxidation masking layer, formed over the first layer, is exposed; (f) removing the exposed anti-oxidation masking layer by dry etching so as to form an opening; (g) introducing impurities of the second conductivity type into the epitaxial layer through the opening; (h) oxidizing a portion of the field insulating layer to form a thick field insulating layer; (i) introducing impurities of the first conductivity type into the epitaxial layer under the second area; (j) annealing the semiconductor device so that the impurities of the second conductivity type diffuse into the epitaxial layer to form an isolation region under the first area and the impurities of the first conductivity type diffuse into the buried layer to form a collector contact region under the second area.
Claim 7
Independent Claim
317 words
A method for producing a semiconductor device having a semiconductor substrate of a second conductivity type, having an epitaxial layer including first, second and third areas of a first conductivity type opposite that of the second conductivity type formed on the semiconductor substrate and having a buried layer of the first conductivity type formed in the semiconductor substrate, the method comprising the steps of: (a) forming a first oxide layer on the first area of the epitaxial layer; (b) forming a second oxide layer on the first oxide layer and on the second and third areas of the epitaxial layer; (c) selectively forming an anti-oxidation masking layer on the second oxide layer to obtain the first and second oxide layers and the anti-oxidation masking layer on the first area, and to obtain the second oxide layer and the anti-oxidation masking layer on the second area; (d) selectively oxidizing the semiconductor device to form a field insulating layer on the epitaxial layer, a portion of the field insulating layer comprising the first and second oxide layers; (e) selectively covering the field insulating layer with a photoresist layer to form an opening in which the anti-oxidation masking layer, formed over the first layer, is exposed; (f) removing the exposed anti-oxidation masking layer by dry etching so as to form an opening; (g) introducing impurities of the second conductivity type into the epitaxial layer through the opening; (h) oxidizing a portion of the field insulating layer to form a thick field insulating layer; (i) introducing impurities of the first conductivity type into the epitaxial layer under the second area; (j) annealing the semiconductor device so that the impurities of the second conductivity type diffuse into the epitaxial layer to form an isolation region under the first area and the impurities of the first conductivity type diffuse into the buried layer to form a collector contact region under the second area.
Claim 8
Dependent Claim
42 words
A method as claimed in claim 5, wherein said step (a) comprises forming the first oxide layer having a thickness of approximately 50 nanometers, and wherein said step (b) comprises forming the second oxide layer having a thickness of approximately 30 nanometers.
Claim 9
Dependent Claim
22 words
A method as claimed in claim 6, wherein step (c) comprises forming the anti-oxidation mask having a thickness of approximately 70 nanometers.
Claim 10
Dependent Claim
45 words
A method as claimed in claim 5, wherein said step (d) comprises forming the field insulating layer having the portion comprising the first and second oxide layers having a thickness of approximately 80 nanometers and the remaining portions having a thickness of approximately 400 nanometers.
Claim 11
Dependent Claim
25 words
A method as claimed in claim 5, wherein said step (h) comprises forming the thick field insulating layer having a thickness of approximately 820 nanometers.
Claim 12
Dependent Claim
37 words
A method as claimed in claim 5, wherein said step (g) comprises introducing the impurities of the second conductivity type using an acceleration voltage of 35 kev and a dose rate of 5×10 15 cm -2 .
Claim 13
Dependent Claim
37 words
A method as claimed in claim 5, wherein said step (i) comprises introducing the impurities of the first conductivity type using an acceleration voltage of 120 kev and a dose rate of 2×10 15 cm -2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-02 | 1988-04-02 | 1988-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-02 | 1992-04-02 | 1992-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-02 | 1996-04-02 | 1996-10-02 | $7700.00 | Window Closed / Lapsed |