Doubly promoted platinum group metal catalysts for emission control
Assignee: WR Grace and Co Conn
•
Filing: 1983-01-26
•
Granted: 1984-10-09
•
Expires: 2003-01-26
Abstract
Abstract Catalysts are made from supports which are doubly promoted with ceria and an alkali metal oxide by adding these promoters and the catalytic noble metal components in a specified order. The ceria is first applied to the support. It can be applied in a salt form such as cerous nitrate. This impregnated support is then calcined to form a deposit of ceria. Next, solutions bearing the noble metals are applied to the ceria-promoted support and with these solutions the alkali metal component is applied. After subsequent elevated temperature activation, the alkali metal component is converted to an alkali metal oxide and the noble metals are converted into their metallic or oxide form. When lithium is chosen as the alkali metal promoter, it can alternatively be applied to the support along with the initial ceria promoter. After calcining the support to yield the ceria and lithia promoters, the noble metals can then be deposited and subsequently activated at an elevated temperature. Using this process it is possible to have the noble metals deposited on the support so that their penetration depth is less than 300 microns as measured by the SnCl2 solution staining method to provide an effective three-way catalyst suitable for use in auto emission control.
Inventors
- 👤 Gwan Kim
- 👤 Michael V. Ernest
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:47
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/38; B01J23/54; B01J23/56; B01J23/63; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J23/58; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
110 words
A method of making a catalyst suitable for use as a three-way catalyst for auto emission control comprising the steps of (a) impregnating a calcined or activated alumina support with a cerous salt solution; (b) air drying and air calcining the impregnated support to obtain a ceria impregnated support; (c) impregnating the ceria impregnated support with solutions bearing platinum group metals in the form of sulfito complex ions and at least one alkali metal at a temperature below about 250° C. to form a catalyst; (d) air drying the catalyst a temperature of about 100°-150° C; and (e) activating the catalyst with hydrogen at a temperature of about 250°-550° C.
Claim 2
Independent Claim
110 words
A method of making a catalyst suitable for use as a three-way catalyst for auto emission control comprising the steps of (a) impregnating a calcined or activated alumina support with a cerous salt solution; (b) air drying and air calcining the impregnated support to obtain a ceria impregnated support; (c) impregnating the ceria impregnated support with solutions bearing platinum group metals in the form of sulfito complex ions and at least one alkali metal at a temperature below about 250° C. to form a catalyst; (d) air drying the catalyst a temperature of about 100°-150° C; and (e) activating the catalyst with hydrogen at a temperature of about 250°-550° C.
Claim 3
Dependent Claim
47 words
The method according to claim 1, wherein the calcined alumina of step (a) has been calcined at a temperature of about 950°-1050° C. and wherein step (b) comprises drying at a temperature of about 100°-150° C. followed by air calcination at a temperature of about 500°-800° C.
Claim 4
Dependent Claim
47 words
The method according to claim 1, wherein the calcined alumina of step (a) has been activated at a temperature of about 300°-600° C. and wherein step (b) comprises drying at a temperature of about 100°-150° C. followed by air calcination at a temperature of about 950°-1050° C.
Claim 5
Dependent Claim
25 words
The method according to claim 1, wherein the activating in step (e) is done at a temperature of about 400° C. for about 1 hour.
Claim 6
Dependent Claim
20 words
The method according to claim 1, wherein the amount of ceria impregnated is about 1-10 weight percent CeO 2 .
Claim 7
Dependent Claim
20 words
The method according to claim 5, wherein the amount of ceria impregnated is about 2-6 weight percent CeO 2 .
Claim 8
Dependent Claim
30 words
The method according to claim 1, wherein the alkali metal expressed as the oxide M 2 O is present in an effective amount of up to about 5 weight percent.
Claim 9
Dependent Claim
19 words
The method according to claim 1, wherein the impregnation in step (c) is done in multiple steps of impregnation.
Claim 10
Dependent Claim
13 words
The method according to claim 1, wherein the support is an alumina pellet.
Claim 11
Dependent Claim
13 words
The method according to claim 1, wherein the support is an alumina powder.
Claim 12
Dependent Claim
12 words
The method according to claim 1, wherein the alkali metal is sodium.
Claim 13
Dependent Claim
17 words
The method according to claim 1, wherein the noble metal is platinum, palladium, rhodium or mixtures thereof.
Claim 14
Dependent Claim
13 words
The method according to claim 12, wherein both platinum and palladium are present.
Claim 15
Dependent Claim
9 words
A catalyst made by the method of claim 1.
Claim 16
Independent Claim
104 words
A method of making a catalyst which is suitable for use as a three-way catalyst for auto emission control comprising the steps of (a) impregnating an activated alumina support with a solution containing a cerous salt and a lithium salt; (b) air drying and air calcining the impregnated support to obtain a ceria-lithia impregnated support; (c) impregnating the ceria-lithia impregnated support with solutions bearing platinum group metals in the form of sulfito complex ions to form a catalyst; (d) air drying the catalyst at a temperature of about 100°-150° C.; and (e) activating the catalyst with hydrogen at a temperature of about 250°-550° C.
Claim 17
Independent Claim
104 words
A method of making a catalyst which is suitable for use as a three-way catalyst for auto emission control comprising the steps of (a) impregnating an activated alumina support with a solution containing a cerous salt and a lithium salt; (b) air drying and air calcining the impregnated support to obtain a ceria-lithia impregnated support; (c) impregnating the ceria-lithia impregnated support with solutions bearing platinum group metals in the form of sulfito complex ions to form a catalyst; (d) air drying the catalyst at a temperature of about 100°-150° C.; and (e) activating the catalyst with hydrogen at a temperature of about 250°-550° C.
Claim 18
Dependent Claim
25 words
The method according to claim 15, wherein the activating in step (e) is done at a temperature of about 400° C. for about 1 hour.
Claim 19
Dependent Claim
20 words
The method according to claim 15, wherein the amount of ceria impregnated is about 1-10 wt. % CeO 2 .
Claim 20
Dependent Claim
20 words
The method according to claim 17, wherein the amount of ceria impregnated is about 2-6 wt. % CeO 2 .
Claim 21
Dependent Claim
22 words
The method according to claim 15, wherein the amount of lithia impregnated is up to about 5 wt. % Li 2 O.
Claim 22
Dependent Claim
20 words
The method according to claim 19, wherein the amount of lithia impregnated is about 0.5-3 wt. % Li 2 O.
Claim 23
Dependent Claim
19 words
The method according to claim 15 wherein the impregnation in step (c) is done in multiple steps of impregnation.
Claim 24
Dependent Claim
13 words
The method according to claim 15, wherein the support is an alumina pellet.
Claim 25
Dependent Claim
13 words
The method according to claim 15, wherein the support is an alumina powder.
Claim 26
Dependent Claim
9 words
A catalyst made by the method of claim 15.
Claim 27
Dependent Claim
74 words
A catalyst suitable for use as a three-way catalyst for auto emission control comprising a pelleted alumina support having impregnated thereon about 2-6% by weight of ceria as a promoter, up to about 5% by weight of an alkali metal oxide as a promoter, and a catalytically effective amount of noble metals, said noble metals penetrating the alumina support to a distance less than 300 microns as measured, by the SnCl 2 solution staining
Claim 28
Dependent Claim
74 words
A catalyst suitable for use as a three-way catalyst for auto emission control comprising a pelleted alumina support having impregnated thereon about 2-6% by weight of ceria as a promoter, up to about 5% by weight of an alkali metal oxide as a promoter, and a catalytically effective amount of noble metals, said noble metals penetrating the alumina support to a distance less than 300 microns as measured, by the SnCl 2 solution staining
Claim 29
Dependent Claim
15 words
A catalyst according to claim 25, wherein the alkali metal oxide is Na 2 O.
Claim 30
Dependent Claim
15 words
A catalyst according to claim 25, wherein the alkali metal oxide is Li 2 O.
References Cited (Backward Citations)
US3755556A
Cited
US4054644A
Cited
US3903020A
Cited
US3993572A
Cited
US3932309A
Cited
US4051073A
Cited
US4140749A
Cited
US4179408A
Cited
JPS56102940A
Cited
US4369132A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |