Silicate binders and coatings
Assignee: Individual
•
Filing: 1983-05-04
•
Granted: 1984-10-30
•
Expires: 2003-05-04
Abstract
Abstract Inorganic binders for coatings such as paints are provided which are based on high single or mixed silicon dioxide to alkali metal oxide mol ratio inorganic alkali metal silicates. The binder composition comprises a mixed silicon dioxide silica gel sol having a silica to alkali metal oxide mol ratio of about 5.5-6.5:1. The binder composition is produced from a starter alkali metal silicate aqueous solution by mixing the solution with a silicone monomer and agitating until hydrolysis is essentially complete. A silica gel is then added as an aqueous slurry and blended until the silica gel is at least partially dissolved. Thereafter, the mixture is agitated to a smooth consistency and recovered as a binder composition. The inorganic binder is particularly suitable for providing coatings or paints having good brushability and which contain zinc dust or aluminum powder for application over ferrous substrates.
Inventors
- 👤 John B. Schutt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:20
CPC Classifications
C; C09; C09D; C09D1/00; C09D1/02; C09D1/04; C09D5/00; C09D5/08; C09D5/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
123 words
An inorganic alkali metal silicate binder composition, in the form of a mixed silicon dioxide silica gel sol, comprising an alkali metal silicate, a silicone, silica gel, and water, said composition having a silicon dioxide to alkali metal oxide mol ratio of about 5.5-6.5:1 , the composition being formed by adding the silicone to the alkali metal silicate contained in aqueous solution and then adding the silica gel with agitation, wherein the silica gel added becomes fully hydrated by the fluxing action during reaction and utilizes the silicone molecules to maintain the gel particles in suspension while freeing the alkali metals ions to promote hydration of additional gel particles; said composition having good brushability when applied as a binder for a paint composition.
Claim 2
Dependent Claim
123 words
An inorganic alkali metal silicate binder composition, in the form of a mixed silicon dioxide silica gel sol, comprising an alkali metal silicate, a silicone, silica gel, and water, said composition having a silicon dioxide to alkali metal oxide mol ratio of about 5.5-6.5:1 , the composition being formed by adding the silicone to the alkali metal silicate contained in aqueous solution and then adding the silica gel with agitation, wherein the silica gel added becomes fully hydrated by the fluxing action during reaction and utilizes the silicone molecules to maintain the gel particles in suspension while freeing the alkali metals ions to promote hydration of additional gel particles; said composition having good brushability when applied as a binder for a paint composition.
Claim 3
Dependent Claim
17 words
A composition according to claim 1 wherein the alkali metal silicate is sodium silicate or potassium silicate.
Claim 4
Dependent Claim
12 words
A composition according to claim 2 wherein the silicone is a methyltrimethyloxysilane.
Claim 5
Dependent Claim
17 words
A composition according to claim 1 to which additional colloidal silica or a silica sol are added.
Claim 6
Dependent Claim
21 words
A composition according to claim 4 wherein the additional colloidal silica has a particle size of between 0.1 and 10 microns.
Claim 7
Dependent Claim
18 words
A paint composition containing the inorganic binder of claim 1 and also contains zinc dust or aluminum powder.
Claim 8
Dependent Claim
17 words
A paint composition according to claim 4 wherein the composition also contains zinc dust or aluminum powder.
Claim 9
Independent Claim
78 words
A method for the production of an inorganic binder composition by a process which comprises: (a) providing a starter alkali metal silicate aqueous solution; (b) mixing the silicate solution with a silicone monomer and agitating until hydrolysis is essentially complete; (c) adding an aqueous slurry of a silica gel to the silicate solution and blending until the silica gel is at least partially dissolved; and (d) agitating the mixture to a smooth consistency and recovering the binder composition.
Claim 10
Independent Claim
78 words
A method for the production of an inorganic binder composition by a process which comprises: (a) providing a starter alkali metal silicate aqueous solution; (b) mixing the silicate solution with a silicone monomer and agitating until hydrolysis is essentially complete; (c) adding an aqueous slurry of a silica gel to the silicate solution and blending until the silica gel is at least partially dissolved; and (d) agitating the mixture to a smooth consistency and recovering the binder composition.
Claim 11
Dependent Claim
39 words
A method according to claim 8 wherein the alkali metal silicate is sodium silicate, potassium silicate, or a mixture thereof, and the solution has an SiO 2 to Na 2 O mol ratio in the range of about 2.0-4.0.
Claim 12
Dependent Claim
27 words
A method according to claim 9 wherein about 1-25 weight percent of silicone monomer is added to the solution, based on the weight of the silicate solution.
Claim 13
Dependent Claim
28 words
A method according to claim 10 wherein sufficient turbulence is maintained in the reaction to cause hydrolysis of the silicone monomer and essentially complete hydration of the silica.
Claim 14
Dependent Claim
12 words
A method according to claim 10 wherein the silicone monomer is methyltrimethyloxysilane.
Claim 15
Dependent Claim
23 words
A method according to claim 12 wherein temperatures are elevated to the range of about 50°-90° C. after addition of the silica gel.
Claim 16
Dependent Claim
30 words
A method according to claim 13 wherein additional water is added in aliquots to prevent gelation and to reduce the pH of the mixture after addition of the silica gel.
Claim 17
Dependent Claim
49 words
A method according to claim 14 wherein a sufficient amount of an additional silica selected from the group consisting of colloidal silica or micron-sized silica gel is added to the mixture to further increase the mol ratio of silica to alkali metal oxide after addition of the silica gel.
References Cited (Backward Citations)
US2786042A
Cited
US2891875A
Cited
US3009829A
Cited
US3522066A
Cited
US3493401A
Cited
US3620784A
Cited
US4162169A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |