Thermal barrier coating system
Assignee: United States, REPRESENTED BY SECRETARY OF NASA
•
Filing: 1983-08-16
•
Granted: 1984-11-27
•
Expires: 2003-08-16
Abstract
Abstract This invention relates to a high temperature oxidation resistant thermal barrier coating system for a nickel-, cobalt-, or iron-base alloy substrate. An inner metal bond coating contacts the substrate, and a thermal barrier coating covers the bond coating. NiCrAlR, FeCrAlR, and CoCrAlR alloys have been satisfactory as bond coating compositions where R=Y or Yb. These alloys contain, by weight, 24.9-36.7% chromium, 5.4-18.5% aluminum, and 0.05 to 1.55% yttrium or 0.05 to 0.53% ytterbium. The coatings containing ytterbium are preferred over those containing yttrium. An outer thermal barrier coating of partially stabilized zirconium oxide (zirconia) which is between 6% and 8%, by weight, of yttrium oxide (yttria) covers the bond coating. Partial stabilization provides a material with superior durability. Partially stabilized zirconia consists of mixtures of cubic, tetragonal, and monoclinic phases.
Inventors
- 👤 Stephan Stecura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 02:49
CPC Classifications
C; C23; C23C; C23C28/00; C23C4/00; C23C4/02; Y; Y02; Y02T; Y02T50/00; Y02T50/60; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12611; Y10T428/12618; Y10T428/12771; Y10T428/12778; Y10T428/12861; Y10T428/12931; Y10T428/12937; Y10T428/12944; Y10T428/12951; Y10T428/12958; Y10T428/12965; Y10T428/12972
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
99 words
A coated article of manufacture having a duplex thermal barrier coating system comprising a substrate of a material selected from the group consisting of nickel-base, cobalt-base, and iron-base alloys, a bond coating consisting essentially of an alloy of about 24.9 w/o to about 36.7 w/o chromium, about 5.5 w/o to about 18.5 w/o aluminum, and about 0.05 w/o to about 0.53 w/o ytterbium with a metal selected from the group consisting essentially of nickel, cobalt, and iron, and a thermal barrier coating consisting essentially of zirconia partially stabilized with about 6% by weight to about 8% by weight yttria.
Claim 2
Dependent Claim
99 words
A coated article of manufacture having a duplex thermal barrier coating system comprising a substrate of a material selected from the group consisting of nickel-base, cobalt-base, and iron-base alloys, a bond coating consisting essentially of an alloy of about 24.9 w/o to about 36.7 w/o chromium, about 5.5 w/o to about 18.5 w/o aluminum, and about 0.05 w/o to about 0.53 w/o ytterbium with a metal selected from the group consisting essentially of nickel, cobalt, and iron, and a thermal barrier coating consisting essentially of zirconia partially stabilized with about 6% by weight to about 8% by weight yttria.
Claim 3
Dependent Claim
24 words
A coated article of manufacture as claimed in claim 1 wherein the bond coating has a thickness between about 0.003 inch and 0.022 inch.
Claim 4
Dependent Claim
54 words
A coated article of manufacture as claimed in claim 2 wherein the substrate is a nickel base alloy, and the bond coating is an alloy comprising about 25.4 w/o to about 35.7 w/o chromium, about 5.6 w/o to about 6.4 w/o aluminum, about 0.34 w/o to about 0.53 w/o ytterbium, and the remainder nickel.
Claim 5
Dependent Claim
35 words
A coated article of manufacture as claimed in claim 2 wherein the substrate is an iron base, alloy and the bond coating contains about 0.09 w/o to about 0.14 w/o ytterbium, and the remainder iron.
Claim 6
Dependent Claim
98 words
A coated article of manufacture having a duplex thermal barrier coating system comprising a substrate of a material selected from the group consisting of nickel-base, cobalt-base, and iron-base alloys, a bond coating consisting essentially of an alloy of about 24.9 w/o to 36.7 w/o chromium, about 5.6 w/o to about 18.5 w/o aluminum, and about 0.05 w/o to about 0.53 w/o ytterbium with a metal selected from the group consisting essentially of nickel, cobalt, and iron, and a thermal barrier coating consisting essentially of zirconia partially stabilized with about 6% by weight to about 8% by weight yttria.
Claim 7
Dependent Claim
98 words
A coated article of manufacture having a duplex thermal barrier coating system comprising a substrate of a material selected from the group consisting of nickel-base, cobalt-base, and iron-base alloys, a bond coating consisting essentially of an alloy of about 24.9 w/o to 36.7 w/o chromium, about 5.6 w/o to about 18.5 w/o aluminum, and about 0.05 w/o to about 0.53 w/o ytterbium with a metal selected from the group consisting essentially of nickel, cobalt, and iron, and a thermal barrier coating consisting essentially of zirconia partially stabilized with about 6% by weight to about 8% by weight yttria.
Claim 8
Dependent Claim
54 words
A coated article of manufacture as claimed in claim 5 wherein the substrate is a nickel base alloy, and the bond coating is an alloy comprising about 25.4 w/o to about 35.6 w/o chromium, about 5.9 w/o to about 6.2 w/o aluminum, about 0.34 w/o to about 0.53 w/o ytterbium, and the remainder nickel.
Claim 9
Dependent Claim
31 words
A coated article of manufacture as claimed in claim 5 wherein the substrate is an iron base alloy, and the bond coating contains about 0.09 w/o to about 0.14 w/o ytterbium.
Claim 10
Dependent Claim
31 words
A coated article of manufacture as claimed in claim 5 wherein the substrate is a cobalt base alloy, and the bond coating contains about 0.05 w/o to about 0.15 w/o ytterbium.
References Cited (Backward Citations)
USRE24242E
Cited
US24242A
Cited
US3589894A
Cited
US3869779A
Cited
US4055705A
Cited
US4095003A
Cited
US4101713A
Cited
US4101715A
Cited
US4248940A
Cited
US4123594A
Cited
US4162918A
Cited
US4273824A
Cited
US4313760A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-27 | 1988-05-28 | 1988-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-27 | 1992-05-28 | 1992-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-27 | 1996-05-28 | 1996-11-27 | $7700.00 | Window Closed / Lapsed |