Porous irrigation pipe prepared from particulate elastomer and thermoplastic binder containing controlled moisture content
Assignee: Aquapore Moisture Systems Inc
•
Filing: 1984-01-24
•
Granted: 1985-05-14
•
Expires: 2004-01-24
Abstract
Abstract A mixture of crumb rubber, binder, such as polyethylene, and slip contact agent, such as talc, and lubricant, such as a metal stearate, is formed in a blender (10), is shaped into pellets (32) by extruding a strand of the mixture (26) into water (28) and breaking the strand into pellets. The pellets (32) are adjusted to a preselected water content in drier (46) before storage in closed bags (50), stored and reinforced in a container (54). The controlled water content pellets (32) are formed into porous pipe (88) by extrusion in pipe extruder (62) having the feeding, transition and metering zones separately heated to temperatures from 320° F. to 400° F. (T 1 , T 2 , T 3 ). The die has a separate jacket (90) receiving heat exchange fluid for heating the die (68) to a temperature from 290° F. to 380° F. to form a porous pipe (88) having more uniform porosity. Porosity is controlled by selecting water content of the pellets and controlling die temperature.
Inventors
- 👤 James W. Mason
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:55
CPC Classifications
B; B29; B29B; B29B17/00; B29B17/04; A; A01; A01G; A01G25/00; A01G25/06; B29B17/0026; B29B17/0042; B29B9/00; B29B9/02; B29B9/06; B29B9/065; B29B9/12; B29B9/16; B29D; B29D23/00; B29D23/001; B29C; B29C2793/00; B29C2793/009; B29C48/00; B29C48/001; B29C48/0012; B29C48/03; B29C48/09; B29C48/10; B29K; B29K2021/00; B29K2105/00; B29K2105/04; B29K2105/26; B29L; B29L2023/00; B29L2023/22; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62; Y10; Y10S; Y10S138/00; Y10S138/07
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
54 words
An extrudable composition having a controlled moisture content from 0.5 to 3 percent by weight and formed from a mixture consisting essentially of: 100 parts by weight of particulate elastomer; 10 to 60 phr of a thermoplastic binder; 1.0 t0 6.0 phr of a slip agent; and 0.1 to 1.0 phr of a lubricant.
Claim 2
Dependent Claim
54 words
An extrudable composition having a controlled moisture content from 0.5 to 3 percent by weight and formed from a mixture consisting essentially of: 100 parts by weight of particulate elastomer; 10 to 60 phr of a thermoplastic binder; 1.0 t0 6.0 phr of a slip agent; and 0.1 to 1.0 phr of a lubricant.
Claim 3
Dependent Claim
13 words
A composition according to claim 1 in which the elastomer is vulcanized rubber.
Claim 4
Dependent Claim
24 words
A composition according to claim 2 in which the elastomer is reclaimed rubber in crumb form having a size from 10 to 60 mesh.
Claim 5
Dependent Claim
17 words
A composition according to claim 3 in which the binder has a melting temperature below 300° F.
Claim 6
Dependent Claim
15 words
A composition according to claim 4 in which the binder resin is a linear polyethylene.
Claim 7
Dependent Claim
37 words
A composition according to claim 5 in which the resin is a mixture of 50 percent to 80 percent by weight of high density polyethylene and 20 percent to 50 percent by weight of low density polyethylene.
Claim 8
Dependent Claim
23 words
A composition according to claim 4 in which the slip agent is a finely divided mineral and the lubricant is a metal stearate.
Claim 9
Dependent Claim
26 words
A composition according to claim 7 in which the slip agent is a talc and the metal stearate is selected from calcium, magnesium or zinc stearates.
Claim 10
Dependent Claim
22 words
A composition according to claim 1 in which the moisture content of a batch does not vary by more than ±10 percent.
Claim 11
Dependent Claim
21 words
A composition according to claim 1 in the form of a pellet having a bulk density of at least 0.25 gm/cc.
Claim 12
Dependent Claim
19 words
A composition according to claim 10 in which the pellet has a diameter from about 3 to 20 mm.
Claim 13
Dependent Claim
10 words
A porous pipe extruded from the composition of claim 1.
Claim 14
Dependent Claim
15 words
A porous pipe according to claim 12 having a diameter from 2 to 10 inches.
Claim 15
Dependent Claim
20 words
A porous pipe according to claim 13 in which the pipe has a wall thickness from 0.1 to 2.0 inches.
Claim 16
Independent Claim
86 words
A method of forming lengths of porous pipe comprising the steps of: adjusting the moisture content to a value between 0.5 to 3.0 percent of a pelletized mixture comprising: 100 parts by weight of a particulate elastomer; 10 to 60 phr of a thermoplastic resin; 1.0 to 6.0 phr of a slip agent; and 0.1 to 1.0 phr of a lubricant; extruding the pellets in a pipe extruder at a temperature of from 320° F. to 400° F. to form a pipe; and cooling the pipe.
Claim 17
Independent Claim
86 words
A method of forming lengths of porous pipe comprising the steps of: adjusting the moisture content to a value between 0.5 to 3.0 percent of a pelletized mixture comprising: 100 parts by weight of a particulate elastomer; 10 to 60 phr of a thermoplastic resin; 1.0 to 6.0 phr of a slip agent; and 0.1 to 1.0 phr of a lubricant; extruding the pellets in a pipe extruder at a temperature of from 320° F. to 400° F. to form a pipe; and cooling the pipe.
Claim 18
Dependent Claim
23 words
A method according to claim 15 in which the die is separately heated to a predetermined temperature from 240° F. to 380° F.
Claim 19
Dependent Claim
16 words
A method according to claim 16 in which the barrel of the extruder is not vented.
Claim 20
Independent Claim
68 words
A method of forming an extrudable composition comprising the steps of: forming a mixture of: 100 parts by weight of particulate elastomer; 10 to 60 phr of a thermoplastic binder; 1.0 to 6.0 phr of a slip agent; and 0.1 to 1.0 phr of a lubricant; pelletizing the mixture; and adjusting the moisture content of the pellets to a value between 0.5 percent to 3.0 percent by weight.
Claim 21
Independent Claim
68 words
A method of forming an extrudable composition comprising the steps of: forming a mixture of: 100 parts by weight of particulate elastomer; 10 to 60 phr of a thermoplastic binder; 1.0 to 6.0 phr of a slip agent; and 0.1 to 1.0 phr of a lubricant; pelletizing the mixture; and adjusting the moisture content of the pellets to a value between 0.5 percent to 3.0 percent by weight.
Claim 22
Dependent Claim
28 words
A method according to claim 18 in which the pellets are formed by extruding the mixture as a strand into chilled water and breaking the strands into pellets.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-13 | 1988-11-12 | 1989-05-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-13 | 1992-11-12 | 1993-05-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-13 | 1996-11-12 | 1997-05-14 | $7700.00 | Window Closed / Lapsed |