Reaction injection molding method
Assignee: Ube Corp
•
Filing: 1983-09-16
•
Granted: 1985-06-18
•
Expires: 2003-09-16
Abstract
Abstract A molded article is formed by a reaction injection molding method wherein a starting material, e.g., an omega -lactam, is injected into a mold, the inner pressure of which is maintained at 0.5 to 20 kg/cm2xG with an inert gas; and the inner pressure of the mold is maintained at a level higher than the pressure increased by injection of the starting material until the polymerization molding of the starting material is completed.
Inventors
- 👤 Masao Nishiyama
- 👤 Keiichiro Katada
- 👤 Yoshiteru Akimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:00
CPC Classifications
B; B29; B29C; B29C45/00; B29C67/00; B29C67/24; B29C67/246; B29C37/00; B29C37/006; B29K; B29K2077/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
121 words
A process for forming a molded article by reaction injection molding, comprising the steps of: pressurizing a mold cavity by filling the cavity with an inert gas at a pressure in the range of 0.5 to 20 kg/cm 2 ·G; injecting into said pressurized cavity starting material capable of reacting to form a polymerized material, the injection of said starting material compressing said gas to increase the pressure within said cavity to a given value; and after injection of said starting material, raising the pressure of the gas within said cavity to an elevated value higher than said given value, and maintaining the pressure within said cavity at said elevated value until the polymerization molding of the starting material is completed.
Claim 2
Dependent Claim
121 words
A process for forming a molded article by reaction injection molding, comprising the steps of: pressurizing a mold cavity by filling the cavity with an inert gas at a pressure in the range of 0.5 to 20 kg/cm 2 ·G; injecting into said pressurized cavity starting material capable of reacting to form a polymerized material, the injection of said starting material compressing said gas to increase the pressure within said cavity to a given value; and after injection of said starting material, raising the pressure of the gas within said cavity to an elevated value higher than said given value, and maintaining the pressure within said cavity at said elevated value until the polymerization molding of the starting material is completed.
Claim 3
Dependent Claim
29 words
A method according to claim 1 wherein the inner pressure in the mold into which the starting material is injected is maintained at 1 to 10 kg/cm 2 ·G.
Claim 4
Dependent Claim
13 words
A metnod according to claim 1 wherein the starting material comprises an ω-lactam.
Claim 5
Dependent Claim
96 words
A method according to claim 1 wherein the starting material is a mixture of an ω-lactam, 0.05 to 10% by mole, based on the ω-lactam, of an alkali catalyst and 0.01 to 5% by mole, based on the ω-lactam, of a cocatalyst selected from the group consisting of N-acyl lactams, organic isocyanates, acid chloride, acid anhydrides, esters, urea derivatives, carbodiimides and ketenes, or 1 to 60% by weight, based on the ω-lactam, of a cocatalyst selected from the group consisting of reaction produts of the above-listed cocatalysts with a polyol, a polyamine or a polycarboxylic acid.
Claim 6
Dependent Claim
38 words
A method according to claim 3 therein the polymerization molding of the ω-lactam is carried out at a temperature not lower than the melting point of the ω-lactam but lower than the melting point of the formed polyamide.
Claim 7
Dependent Claim
29 words
A method according to claim 1 wherein the level of the inner pressure in the mold maintained during the polymerization molding is not higher than 50 kg/cm 2 ·G.
Claim 8
Dependent Claim
29 words
The process according to claim 1, wherein the pressure of the gas within said cavity is raised to said elevated value by introducing additional inert gas into said cavity.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-17 | 1988-12-17 | 1989-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-17 | 1992-12-17 | 1993-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-17 | 1996-12-17 | 1997-06-18 | $7700.00 | Window Closed / Lapsed |