Elastomer compositions containing humates
Assignee: Alfred D Lobo and Co LPA
•
Filing: 1984-10-18
•
Granted: 1985-07-30
•
Expires: 2004-10-18
Abstract
Abstract Elastomer compositions are provided which contain high molecular weight water-insoluble humic acid humates. The compositions show improved bloom resistance in both the uncured and the vulcanized or otherwise cured state. Methods to make sponge rubber are also disclosed in which the humic acid humate is the gas producing agent. A predominantly humic acid humate containing composition maintains a clean mold, and curing an uncured article coated with the humate at elevated temperature will clean metal molds which have dirty surfaces, particularly when green coated articles are vulcanized in contact with the mold's surfaces.
Inventors
- 👤 Harold R. MacKeighen
- 👤 Vincent T. Cortesi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 18:44
CPC Classifications
C; C08; C08L; C08L21/00; C08J; C08J9/00; C08J9/04; C08J9/06; C08L23/00; C08L23/02; C08L23/16; C08J2321/00; C08K; C08K5/00; C08K5/0008; C08K5/0025; C08K5/01; C08L2203/00; C08L2203/14; C08L97/00
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
69 words
A method for producing sponge rubber comprising mixing humic acid humate with a vulcanizable rubber to form an essentially homogeneous mixture, and vulcanizing said rubber mixture at a temperature sufficient to cause said rubber mixture to expand into a cellular mass, said humic acid humate having a molecular weight of from about 2,000 to about 1,300,000 and having carbon content of from about 20 percent to about 60 percent.
Claim 2
Independent Claim
69 words
A method for producing sponge rubber comprising mixing humic acid humate with a vulcanizable rubber to form an essentially homogeneous mixture, and vulcanizing said rubber mixture at a temperature sufficient to cause said rubber mixture to expand into a cellular mass, said humic acid humate having a molecular weight of from about 2,000 to about 1,300,000 and having carbon content of from about 20 percent to about 60 percent.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said temperature is in the range of from about 250° F. (121° C.) to about 450° F. (232° C.).
Claim 4
Dependent Claim
15 words
The method of claim 1 wherein said rubber mixture is vulcanized in an unconfined atmosphere.
Claim 5
Dependent Claim
41 words
The method of claim 3 wherein said rubber mixture is shaped into strips and said strips are vulcanized by passing through a bath, wherein said bath has a temperature of from about 300° F. (149° C.) to about 450° (232° C.).
Claim 6
Dependent Claim
14 words
The method of claim 4 wherein said rubber is an ethylene propylene diene rubber.
Claim 7
Independent Claim
57 words
A method of cleaning a metal mold comprising foaming and vulcanizing a rubber composition in contact with said mold surface wherein said composition comprises a humic acid humate said humic acid humate having a molecular weight of from about 2000 to about 1,300,00 and having a carbon content of from about 20 percent to about 60 percent.
Claim 8
Independent Claim
57 words
A method of cleaning a metal mold comprising foaming and vulcanizing a rubber composition in contact with said mold surface wherein said composition comprises a humic acid humate said humic acid humate having a molecular weight of from about 2000 to about 1,300,00 and having a carbon content of from about 20 percent to about 60 percent.
Claim 9
Dependent Claim
32 words
The method of claim 6 wherein said humic acid humate is present in an amount from about 1 to about 300 parts by weight per 100 parts by weight of vulcanized rubber.
Claim 10
Dependent Claim
32 words
The method of claim 7 wherein said humic acid humate is present in an amount from about 10 to about 100 parts by weight per 100 parts by weight of vulcanizable rubber.
Claim 11
Dependent Claim
34 words
The method of claim 7 wherein said humic acid humate has a molecular weight of from about 20,000 to about 50,000 and a carbon content of from about 30 percent to about 40 percent.
Claim 12
Independent Claim
60 words
The method for cleaning a metal mold comprising applying to the exterior surfaces of an unvulcanized rubber article a coating comprising humic acid humate, said humic acid humate having a molecular weight of from about 2000 to about 1,300,000 and having a carbon content of from aobut 20 percent to about 60 perent, and thereafter foaming and vulcanizing said composition.
Claim 13
Independent Claim
60 words
The method for cleaning a metal mold comprising applying to the exterior surfaces of an unvulcanized rubber article a coating comprising humic acid humate, said humic acid humate having a molecular weight of from about 2000 to about 1,300,000 and having a carbon content of from aobut 20 percent to about 60 perent, and thereafter foaming and vulcanizing said composition.
Claim 14
Dependent Claim
22 words
The method of claim 10 wherein said humic acid has a carbon content of from about 30 percent to about 40 percent.
Claim 15
Independent Claim
56 words
The method for improving the tack of an unvulcanized rubber composition comprising mixing humic acid humate, said humic acid humate having a molecular weight of from 2000 to about 1,300,000 and having a carbon content of from about 20 percent to about 60 percent, into said rubber composition and thereafter foaming and vulcanizing said rubber composition.
Claim 16
Independent Claim
56 words
The method for improving the tack of an unvulcanized rubber composition comprising mixing humic acid humate, said humic acid humate having a molecular weight of from 2000 to about 1,300,000 and having a carbon content of from about 20 percent to about 60 percent, into said rubber composition and thereafter foaming and vulcanizing said rubber composition.
Claim 17
Dependent Claim
32 words
The method of claim 12 wherein said humic acid humate is present at a level of from about 1 to about 300 parts by weight per 100 parts by weight of rubber.
Claim 18
Independent Claim
53 words
The method for reducing the bloom of a vulcanized rubber article comprising mixing humic acid humate, said humic acid humate having a molecular weight of from about 2,000 to about 1,300,000 and having a carbon content of from about 20 percent to about 60 percent, with rubber thereafter foaming and vulcanizing said mixture.
Claim 19
Independent Claim
53 words
The method for reducing the bloom of a vulcanized rubber article comprising mixing humic acid humate, said humic acid humate having a molecular weight of from about 2,000 to about 1,300,000 and having a carbon content of from about 20 percent to about 60 percent, with rubber thereafter foaming and vulcanizing said mixture.
Claim 20
Dependent Claim
32 words
The method of claim 14 wherein said humic acid humate is present at a level of from about 1 to about 300 parts by weight per 100 parts by weight of rubber.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-29 | 1989-01-28 | 1989-07-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-29 | 1993-01-28 | 1993-07-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-29 | 1997-01-28 | 1997-07-30 | $7700.00 | Window Closed / Lapsed |