Method of producing a biaxially oriented container of polyethylene terephthalate or similar material
Assignee: Rexam AB
•
Filing: 1983-04-29
•
Granted: 1985-09-10
•
Expires: 2003-04-29
Abstract
Abstract A method for producing a container from a tubular blank of polyethylene terephthalate or similar material, according to which a polyethylene terephthalate blank is stretched at least approximately 3-fold to produce a preform (20). In an axial section through the preform, the contour length substantially corresponds to the contour length in an axial section through the final container. The preform (20) is heated to a temperature above the glass transition temperature (TG) and is converted to the container (21) in a blow mold (12). In doing so, the contour length of the material is maintained through successive reduction of the axial length of the body (23) which the preform constitutes during the conversion to the container. In order to achieve this, the base portion of the blow mold (11) is moved towards the orifice (22) of the final container. The container acquires a neck portion (23) and a container body (26) which are axially oriented, in the case of polyethylene terephthalate to an extent corresponding to about a 3-fold monoaxial stretching, while the container body (26) is also transversely oriented, in the case of polyethylene terephthalate to an extent corresponding to about a 3-fold stretching as a maximum. The wall thickness of the container is inversely proportional to the radius of the container. The container is dimensionally very stable and has excellent strength characteristics.
Inventors
- 👤 Kjell M. Jakobsen
- 👤 Claes T. Nilsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:13
CPC Classifications
B; B29; B29C; B29C67/00; B29C67/0003; B29C31/00; B29C31/002; B29C49/00; B29C49/08; B29C49/10; B29C49/14; B29C49/42; B29C49/48; B29C49/54; B29C49/541; B29C55/00; B29C55/30; B29C59/00; B29C59/02; B29C59/04; B29C59/043; B29C67/0014; B65; B65D; B65D1/00; B65D1/02; B65D1/0207; B65D1/0223; B29C43/00; B29C43/32; B29C43/36; B29C43/361; B29C2043/3615; B29C2043/3618; B29C2043/3631; B29C2049/4879; B29C2049/4892; B29C2793/00; B29C2793/009; B29C2949/00; B29C2949/07; B29C2949/079; B29C2949/08; B29C2949/0861; B29C2949/0862; B29C2949/0863; B29C2949/0865; B29K; B29K2067/00; B29K2105/00; B29K2105/25; B29K2105/253; B29K2105/258; Y; Y10; Y10S; Y10S264/00; Y10S264/90; Y10S264/904; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1379
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
173 words
A method of forming a container from orientable thermoplastic material comprising: providing a hollow preform of thermoplastic material including a side wall and a closed end, the material of said side wall having axial orientation and being capable of circumferential expansion and circumferential orientation, positioning the preform in a mold having a movable mold part, expanding the preform in the mold to form the container, said preform, prior to its formation to the finished shape of said container, coming into contact with said movable mold part without any axial stretching of said side wall, and displacing the closed end portion of the preform by said movable mold part in correspondence with the expanding of the preform such that the material of the side wall is not stretched in a plane perpendicular to the direction of expanding and thereby the material does not undergo any axial strain due to elongation and said expanding produces circumferential stretching and circumferential orientation of the material in said side wall independent of and superimposed on said axial orientation.
Claim 2
Independent Claim
173 words
A method of forming a container from orientable thermoplastic material comprising: providing a hollow preform of thermoplastic material including a side wall and a closed end, the material of said side wall having axial orientation and being capable of circumferential expansion and circumferential orientation, positioning the preform in a mold having a movable mold part, expanding the preform in the mold to form the container, said preform, prior to its formation to the finished shape of said container, coming into contact with said movable mold part without any axial stretching of said side wall, and displacing the closed end portion of the preform by said movable mold part in correspondence with the expanding of the preform such that the material of the side wall is not stretched in a plane perpendicular to the direction of expanding and thereby the material does not undergo any axial strain due to elongation and said expanding produces circumferential stretching and circumferential orientation of the material in said side wall independent of and superimposed on said axial orientation.
Claim 3
Dependent Claim
25 words
A method as claimed in claim 1 wherein said preform is progressively expanded in correspondence with progressive displacement of the closed end of the preform.
Claim 4
Dependent Claim
28 words
A method as claimed in claim 1 comprising effecting said expanding with the temperature of the material in the vicinity of the glass transition temperature (T g ).
Claim 5
Dependent Claim
46 words
A method as claimed in claim 3 wherein the axial orientation of the material of the preform is effected by stretching the material in the axial direction at a temperature within or below the region of the glass transition temperature (T g ) of the material.
Claim 6
Dependent Claim
33 words
A method as claimed in claim 4 wherein said preform is tubular and is stretched in its axial direction to reduce its wall thickness while concurrently diminishing the outer circumference of the preform.
Claim 7
Dependent Claim
23 words
A method as claimed in claim 5 wherein the inner diameter of the preform is substantially maintained during the stretching of the blank.
Claim 8
Dependent Claim
51 words
A method as claimed in claim 4 wherein said preform is tubular and has inner and outer surfaces, said preform being stretched in its axial direction to reduce the wall thickness while substantially maintaining the diameter of one of said surfaces and changing the diameter of the other of said surfaces.
Claim 9
Dependent Claim
28 words
A method as claimed in claim 1 comprising heating said preform, prior to placement in the mold, to a temperature above the glass transition temperature (T g ).
Claim 10
Dependent Claim
18 words
A method as claimed in claim 1 wherein the preform is at a molding temperature prior to expanding.
Claim 11
Dependent Claim
33 words
A method as claimed in claim 1 wherein the side wall of the preform is out of contact with the mold when the closed end of the preform contacts said movable mold part.
Claim 12
Dependent Claim
23 words
A method as claimed in claim 1 wherein the preform comes into contact with said movable mold part before the preform is expanded.
Claim 13
Dependent Claim
16 words
A method as claimed in claim 11 wherein said expanding is effected by blowing under pressure.
Claim 14
Dependent Claim
36 words
A method as claimed in claim 1 wherein the circumferential stretching of the side wall causes reduction in the thickness thereof such that the resultant thickness of the side wall is inversely related to its diameter.
Claim 15
Dependent Claim
27 words
A method as claimed in claim 1 wherein said closed end of said preform is compressed against said movable mold part to undergo shaping and thickness change.
Claim 16
Dependent Claim
25 words
A method as claimed in claim 1 wherein said mold is heated and said container undergoes heat transfer with the mold and consequent heat setting.
Claim 17
Dependent Claim
57 words
A method as claimed in claim 1 wherein during the expanding of the preform to said container, said moveable mold part is moved in the axial direction of the preform, to assume an upper position corresponding to the final shape of the mold and thereby also to the final shape of the container produced in the mold.
Claim 18
Dependent Claim
42 words
A method as claimed in claim 16 wherein a central portion of the closed end of the preform is reduced in thickness by compressing the material in said central portion between the movable mold part and a mandrel located inside the preform.
Claim 19
Dependent Claim
85 words
A method as claimed in claim 17 wherein said preform is expanded to said container by applying pressure inside the preform to expand the same against the walls of the mold, said method further comprising supplying heat to the preform from said walls so that the material of the container, through heat transmission from the mold, acquires an additional crystallinity over and above that which results from the orientation of the material while additionally internal stresses of the material originating from the orientation are released.
Claim 20
Dependent Claim
34 words
A method as claimed in claim 1 wherein said thermoplastic material is polyethylene terephthalate, polyhexamethylene adipamide, polycaprolactam, polyhexamethylene sebacamide, polyethylene 2,6- and 1,5- naphthalate, polytetramethylene 1,2-dioxybenzoate or copolymers of ethylene terephthalate and ethylene isophthalate.
Claim 21
Dependent Claim
16 words
A method as claimed in claim 4 wherein the material has been stretched to undergo flow.
Claim 22
Dependent Claim
23 words
A method as claimed in claim 4 wherein said thermoplastic material is polyethylene terephthalate and said preform is stretched at least about 3-fold.
Claim 23
Dependent Claim
28 words
A method as claimed in claim 1 wherein said thermoplastic material is polyethylene terephthalate and said preform is produced by stretching a blank at a temperature below 105°.
Claim 24
Dependent Claim
21 words
A method as claimed in claim 22 wherein the temperature of the material at stretching is between 70° and 105° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |