Hollow proppants and a process for their manufacture
Assignee: Terra Tek Inc
•
Filing: 1983-06-30
•
Granted: 1985-10-15
•
Expires: 2003-06-30
Abstract
Abstract Hollow, fine-grained ceramic proppants are less expensive and improve fracture control when compared to conventional proppants (dense alumina, mullite, bauxite, zirconia, etc.). Hollow proppants of the present invention have been fabricated by spray drying, followed by sintering in order to obtain a dense case and a hollow core. These proppants generally have high sphericity and roundness (Krumbein sphericity and roundness greater than 0.8), have diameters on average between 2250 and 125 μm, depending on proppant size required, and have strength equal to or greater than that of sand. The hollow core, the size of which can be controlled, permits better fracture control in hydraulic fracturing treatments since the proppant can be transported in lower viscosity fluids. Hollow proppants produced at the same cost/weight as conventional proppants also provide for lower costs, since less weight is required to fill the same volume. The fine-grained (preferably less than 5 μm in diameter) ceramic case provides the strength necessary to withstand closure stresses and prevent crushing.
Inventors
- 👤 Arfon H. Jones
- 👤 Raymond A. Cutler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:07
CPC Classifications
E; E21; E21B; E21B43/00; E21B43/25; E21B43/26; E21B43/267; C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/16; C04B35/18; C04B35/185; C04B35/195; C04B35/48; C04B35/486; C04B35/622; C04B35/626; C04B35/62605; C04B35/62645; C04B35/62665; C04B38/00; C04B38/0022; C09; C09K; C09K8/00; C09K8/60; C09K8/80; C04B2235/00; C04B2235/02; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/70; C04B2235/94
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
82 words
A hollow ceramic proppant comprising, a polycrystalline ceramic sphere having a dense case with an average grain size of less than thirty (30) μm in diameter, a central void that is greater than five (5) and less than fifty (50) volume percent of the proppant, the proppant having a specific gravity lower than three point three (3.3) gm/cc and a crushing strength equal to or greater than that of Ottowa sand at closure stresses above 34.5 MPa, or five thousand (5,000) psi.
Claim 2
Dependent Claim
82 words
A hollow ceramic proppant comprising, a polycrystalline ceramic sphere having a dense case with an average grain size of less than thirty (30) μm in diameter, a central void that is greater than five (5) and less than fifty (50) volume percent of the proppant, the proppant having a specific gravity lower than three point three (3.3) gm/cc and a crushing strength equal to or greater than that of Ottowa sand at closure stresses above 34.5 MPa, or five thousand (5,000) psi.
Claim 3
Dependent Claim
22 words
A hollow ceramic proppant as recited in claim 1, wherein the proppant has a Krumbein sphericity and roundness of 0.8 and greater.
Claim 4
Dependent Claim
22 words
A hollow ceramic proppant as recited in claim 1, wherein the average grain size is less than five (5) μm in diameter.
Claim 5
Dependent Claim
27 words
A hollow ceramic proppant as recited in claim 1, wherein the inner void is greater than fifteen (15) volume percent and less than fifty (50) volume percent.
Claim 6
Dependent Claim
21 words
A hollow ceramic proppant as recited in claim 1, wherein the specific gravity is less than two point five (2.5) gm/cc.
Claim 7
Dependent Claim
14 words
A hollow ceramic proppant as recited in claim 1, wherein the ceramic is alumina.
Claim 8
Dependent Claim
14 words
A hollow ceramic proppant as recited in claim 1, wherein the ceramic is bauxite.
Claim 9
Dependent Claim
14 words
A hollow ceramic proppant as recited in claim 1, wherein the ceramic is mullite.
Claim 10
Dependent Claim
14 words
A hollow ceramic proppant as recited in claim 1, wherein the ceramic is cordierite.
Claim 11
Dependent Claim
14 words
A hollow ceramic proppant as recited in claim 1, wherein the ceramic is zirconia.
Claim 12
Dependent Claim
14 words
A hollow ceramic proppant as recited in claim 1, wherein the ceramic is porcelain.
Claim 13
Dependent Claim
150 words
A process for producing hollow ceramic proppants, including the steps of mixing a fine polycrystalline ceramic powder of particles of sizes less than twenty-five (25) μm in diameter with water and organic binders; injecting the mixture through a nozzle into a spray dryer, wherein, a temperature of between one hundred degress (100°) and four hundred degrees (400°) Centigrade (C) is maintained; passing the injected particles against a hot air flow; and sintering the particles at a sufficient temperature to produce proppant having a dense case with an average grain size of less than thirty (30) μm in diameter, a central void that is greater than five (5) volume percent of the proppant, the proppant having a specific gravity lower than three point three (3.3) gm/cc and a crushing strength equal to or greater than that of Ottowa sand at closure stresses of above 34.5 MPa, or five thousand (5,000) psi.
Claim 14
Dependent Claim
150 words
A process for producing hollow ceramic proppants, including the steps of mixing a fine polycrystalline ceramic powder of particles of sizes less than twenty-five (25) μm in diameter with water and organic binders; injecting the mixture through a nozzle into a spray dryer, wherein, a temperature of between one hundred degress (100°) and four hundred degrees (400°) Centigrade (C) is maintained; passing the injected particles against a hot air flow; and sintering the particles at a sufficient temperature to produce proppant having a dense case with an average grain size of less than thirty (30) μm in diameter, a central void that is greater than five (5) volume percent of the proppant, the proppant having a specific gravity lower than three point three (3.3) gm/cc and a crushing strength equal to or greater than that of Ottowa sand at closure stresses of above 34.5 MPa, or five thousand (5,000) psi.
Claim 15
Dependent Claim
25 words
A process for producing hollow ceramic proppants as recited in claim 12, wherein the fine ceramic powder grains are less than 5 m in diameter.
Claim 16
Dependent Claim
23 words
A process as recited in claim 12, further including adding a defoaming agent to the slurry prior to injecting it through a nozzle.
Claim 17
Dependent Claim
22 words
A hollow ceramic proppant as recited in claim 1, wherein the central void is spherical and concentric with the proppant outer surface.
Claim 18
Dependent Claim
14 words
A process as recited in claim 12, wherein the binder is a polyvinyl alcohol.
Claim 19
Dependent Claim
15 words
A process as recited in claim 14, wherein the defoaming agent is a polyethylene glycol.
References Cited (Backward Citations)
US3399727A
Cited
US3975194A
Cited
US4072193A
Cited
US4163637A
Cited
US4106574A
Cited
US4109717A
Cited
US4159296A
Cited
US4421562A
Cited
US4391646A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-14 | 1989-04-15 | 1989-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-14 | 1993-04-15 | 1993-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-14 | 1997-04-15 | 1997-10-15 | $7700.00 | Window Closed / Lapsed |