Friction element and method of manufacture thereof
Assignee: ZF International UK Ltd
•
Filing: 1984-02-17
•
Granted: 1986-03-18
•
Expires: 2004-02-17
Abstract
Abstract To produce a sintered metal type brake friction element which beds-in quickly and which has a "feel" similar to a resin-based element, powdered metallic friction material is subjected to a resistance sintering or furnace sintering operation, so as to produce a sintered substrate and an unsintered or partly sintered surface layer which has less wear resistance than the substrate but friction properties which are not substantially less than the substrate. The surface layer may be formed of the same or different material as the substrate layer depending upon the sintering technique chosen.
Inventors
- 👤 Melvyn Ward
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:49
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/02; B22F7/04; F; F16; F16D; F16D69/00; F16D69/02; F16D69/027; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12042; Y10T428/12063
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
119 words
A friction element comprising a sintered substrate formed of metallic friction material containing sintered metal particles and at least one friction modifier; and a surface layer having a thickness of up to about 2 mm on said sintered substrate and defining a friction surface of the friction element; said surface layer being formed of a metallic friction material containing at least one friction modifier and metal particles which are unsintered or sintered over substantially the whole of said friction surface to a lesser extent than said friction material of said sintered substrate so that said surface layer has less wear resistance than said sintered substrate and friction properties which are not substantially less than those of said sintered substrate.
Claim 2
Dependent Claim
119 words
A friction element comprising a sintered substrate formed of metallic friction material containing sintered metal particles and at least one friction modifier; and a surface layer having a thickness of up to about 2 mm on said sintered substrate and defining a friction surface of the friction element; said surface layer being formed of a metallic friction material containing at least one friction modifier and metal particles which are unsintered or sintered over substantially the whole of said friction surface to a lesser extent than said friction material of said sintered substrate so that said surface layer has less wear resistance than said sintered substrate and friction properties which are not substantially less than those of said sintered substrate.
Claim 3
Dependent Claim
30 words
A friction element as claimed in claim 1, wherein said surface layer is an unsintered or partly sintered portion of the same metallic friction material which forms said sintered substrate.
Claim 4
Dependent Claim
37 words
A friction element as claimed in claim 1, wherein said surface layer is formed of a different metallic friction material which is unsinterable or less easy to sinter than that of the substrate under the sintering conditions.
Claim 5
Dependent Claim
21 words
A friction element as claimed in claim 1, wherein the surface layer has a thickness of about 0.5 to 2 mm.
Claim 6
Independent Claim
217 words
A method of manufacturing a friction element comprising the steps of disposing in a resistance sintering die (1) at least one layer of powdered metallic friction material which (a) contains sinterable metallic particles and at least one friction modifier and (b) is destined to form a sintered friction material substrate of the friction element and (2) a surface layer of powdered metallic friction material which (a) contains metallic particles and at least one friction modifier and (b) is destined to form a friction material surface layer of the friction element; and subjecting said layers of powdered metallic friction material to a resistance sintering operation at a pressure and temperature such as to sinter said sinterable metallic particles of said at least one layer of powdered metallic friction material whereby said sintered substrate and said surface layer of the friction element having a thickness of up to 2 mm are produced, wherein said surface layer of powdered metallic friction material which is destined to form said surface layer of the friction element is formulated so as to be unsinterable or only partially sintered under said pressure and temperature whereby said surface layer of the friction element has less wear resistance than said sintered substrate and frictional properties which are not substantially less than those of said sintered substrate.
Claim 7
Independent Claim
217 words
A method of manufacturing a friction element comprising the steps of disposing in a resistance sintering die (1) at least one layer of powdered metallic friction material which (a) contains sinterable metallic particles and at least one friction modifier and (b) is destined to form a sintered friction material substrate of the friction element and (2) a surface layer of powdered metallic friction material which (a) contains metallic particles and at least one friction modifier and (b) is destined to form a friction material surface layer of the friction element; and subjecting said layers of powdered metallic friction material to a resistance sintering operation at a pressure and temperature such as to sinter said sinterable metallic particles of said at least one layer of powdered metallic friction material whereby said sintered substrate and said surface layer of the friction element having a thickness of up to 2 mm are produced, wherein said surface layer of powdered metallic friction material which is destined to form said surface layer of the friction element is formulated so as to be unsinterable or only partially sintered under said pressure and temperature whereby said surface layer of the friction element has less wear resistance than said sintered substrate and frictional properties which are not substantially less than those of said sintered substrate.
Claim 8
Dependent Claim
30 words
A method as claimed in claim 5, whrein the resistance sintering operation is effected using a metal electrode in direct contact with said surface layer of powdered metallic friction material.
Claim 9
Dependent Claim
40 words
A method as claimed in claim 6, wherein said metal electrode has a surface in contact with said surface layer of powdered metallic friction material, said surface of said metal electrical being defined completely by the metal of the electrode.
Claim 10
Dependent Claim
48 words
A method as claimed in claim 6, wherein said metal electrode has a surface in contact with the surface layer of powdered metallic friction material, said surface of said metal electrode being defined partly by an insert having a higher resistivity than the metal of said metal electrode.
Claim 11
Dependent Claim
56 words
A method as claimed in claim 5, wherein the sintering operation is effected using a sub electrode and a metal electrode, the sub electrode having a lower thermal conductivity than the metal electrode and being in contact with said surface layer of powdered friction material, and wherein the surface layer is different from the substrate material.
Claim 12
Independent Claim
184 words
A method of manufacturing a friction element comprising the steps of disposing in a resistance sintering die a layer of powdered metallic friction material which (a) contains sinterable metallic particles and at least one friction modifier and (b) is destined to form a sintered friction material substrate and a friction material surface layer of the friction element; and subjecting said layer of powdered friction material to a resistance sintering operation at a temperature and pressure such as to sinter a portion of said layer destined to form said substrate, wherein said resistance sintering operation is effected using a metal electrode in contact with a portion of said powdered metallic friction material destined to form said surface layer whereby a chill effect is produced so that a said portion of said powdered metallic friction material which is in contrast with said metal electrode remains unaltered or is only partially sintered so that said surface layer is produced which has a thickness of up to 2 mm, less wear resistance than said substrate and friction properties which are not substantially less than those of said substrate.
Claim 13
Independent Claim
184 words
A method of manufacturing a friction element comprising the steps of disposing in a resistance sintering die a layer of powdered metallic friction material which (a) contains sinterable metallic particles and at least one friction modifier and (b) is destined to form a sintered friction material substrate and a friction material surface layer of the friction element; and subjecting said layer of powdered friction material to a resistance sintering operation at a temperature and pressure such as to sinter a portion of said layer destined to form said substrate, wherein said resistance sintering operation is effected using a metal electrode in contact with a portion of said powdered metallic friction material destined to form said surface layer whereby a chill effect is produced so that a said portion of said powdered metallic friction material which is in contrast with said metal electrode remains unaltered or is only partially sintered so that said surface layer is produced which has a thickness of up to 2 mm, less wear resistance than said substrate and friction properties which are not substantially less than those of said substrate.
Claim 14
Independent Claim
147 words
A method of manufacturing a friction element comprising the steps of shaping a plurality of powdered metallic friction materials to produce a preform having a substrate portion and a surface portion which is (a) destined to form a surface layer portion of the friction element and (b) defined by one of said powdered metallic friction materials; and subjecting said preform to a furnace sintering operation so as to sinter the powdered metallic friction material which is destined to form said substrate; wherein said one of said powdered metallic friction materials which define said surface layer portion of the friction element is selected so that it remains unsintered or is only partially sintered during the furnace sintering step whereby said surface layer portion of the friction element has less wear resistance than said substrate and has friction properties which are not substantially less than those of said substrate.
Claim 15
Independent Claim
147 words
A method of manufacturing a friction element comprising the steps of shaping a plurality of powdered metallic friction materials to produce a preform having a substrate portion and a surface portion which is (a) destined to form a surface layer portion of the friction element and (b) defined by one of said powdered metallic friction materials; and subjecting said preform to a furnace sintering operation so as to sinter the powdered metallic friction material which is destined to form said substrate; wherein said one of said powdered metallic friction materials which define said surface layer portion of the friction element is selected so that it remains unsintered or is only partially sintered during the furnace sintering step whereby said surface layer portion of the friction element has less wear resistance than said substrate and has friction properties which are not substantially less than those of said substrate.
References Cited (Backward Citations)
GB584440A
Cited
GB807909A
Cited
GB830322A
Cited
GB944578A
Cited
GB990620A
Cited
GB1114698A
Cited
DE2054335A1
Cited
US3946192A
Cited
JPS55107702A
Cited
US4456578A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-17 | 1989-09-16 | 1990-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-17 | 1993-09-16 | 1994-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-17 | 1997-09-16 | 1998-03-18 | $7700.00 | Window Closed / Lapsed |