Glass bonding method
Assignee: Motorola Solutions Inc
•
Filing: 1985-01-29
•
Granted: 1986-06-03
•
Expires: 2005-01-29
Abstract
Abstract An improved semiconductor die bonding structure and method for electrical devices is described which utilizes a ductile foil between the semiconductor die and the base of the device package. The die is sealed to the foil with a die bonding material formed from a titania free base glass to which has been added 23.6 to 36.4 weight percent lead titanate powder to give a glass plus ceramic mixture consisting essentially of (by weight percent) 2.5-10.7% GeO2, 0-2.3% SiO2, 58.6-78.5% PbO, 0-5.3% PbF2, 7-13% B2O3, 2.5-6.9% Al2O3, 0-5.3% ZnO, 0.4-2.3% V2O5, 0-5.3% CdO, and 6.2-9.6% TiO2. The ductile foil is bonded to the ceramic package base directly without intermediate layers or alternatively by means of an improved foil bonding glass material consisting essentially of (by weight percent) 10-15% SiO2, 45-55% PbO, 8-12% ZnO, 2-5% Al2O3, and 25-30% B2O3.
Inventors
- 👤 Earl K. Davis
- 👤 James E. Drye
- 👤 David J. Reed
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:22
CPC Classifications
C; C03; C03C; C03C8/00; C03C8/24; C03C8/245; C04; C04B; C04B37/00; C04B37/02; C04B37/023; C04B37/025; H; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H10W70/692; H10W72/00; H10W72/30; H10W76/00; H10W76/60; C04B2237/00; C04B2237/02; C04B2237/10; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/40; C04B2237/402; C04B2237/50; C04B2237/70; C04B2237/708; C04B2237/84; C04B2237/86; H10W70/62; H10W70/65; H10W70/654; H10W70/655; H10W70/68; H10W70/682; H10W72/071; H10W72/073; H10W72/07331; H10W72/07337; H10W72/351; H10W72/353; H10W72/354; H10W72/381
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
189 words
A method for bonding a ductile foil having a predetermined foil melting temperature to a ceramic base comprising: providing a ceramic base of predetermined base coefficient of expansion and base melting temperature; locating said ductile foil above said ceramic base; placing a substantially alkali-free bonding glass between said foil and said ceramic base to form an assembly, said bonding glass having a predetermined glass softening temperature less than said foil and base melting temperatures and a predetermined glass coefficient of expansion, wherein said glass coefficient of expansion is smaller than said base coefficient of expansion; wherein said bonding glass comprises ingredients by weight percent in the range of SiO 2 (10-15%), PbO (45-55%), ZnO (8-12%), Al 2 O 3 (2-5%), and B 2 O 3 (25-30%); and applying heat and pressure to said assembly, said heat being sufficient to raise the temperature of said assembly so as to be in a range greater than said glass softening temperature, but less than said foil and base melting temperatures, and said pressure being sufficient to cause plastic flow of said glass to substantially eliminate voids between said base and said foil.
Claim 2
Independent Claim
189 words
A method for bonding a ductile foil having a predetermined foil melting temperature to a ceramic base comprising: providing a ceramic base of predetermined base coefficient of expansion and base melting temperature; locating said ductile foil above said ceramic base; placing a substantially alkali-free bonding glass between said foil and said ceramic base to form an assembly, said bonding glass having a predetermined glass softening temperature less than said foil and base melting temperatures and a predetermined glass coefficient of expansion, wherein said glass coefficient of expansion is smaller than said base coefficient of expansion; wherein said bonding glass comprises ingredients by weight percent in the range of SiO 2 (10-15%), PbO (45-55%), ZnO (8-12%), Al 2 O 3 (2-5%), and B 2 O 3 (25-30%); and applying heat and pressure to said assembly, said heat being sufficient to raise the temperature of said assembly so as to be in a range greater than said glass softening temperature, but less than said foil and base melting temperatures, and said pressure being sufficient to cause plastic flow of said glass to substantially eliminate voids between said base and said foil.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein said foil is substantially aluminum or ductile aluminum alloy.
Claim 4
Dependent Claim
30 words
The method of claim 1 wherein said bonding glass material consists by weight percent essentially of: ______________________________________
SiO.sub.2
12.2
PbO 48.0
ZnO 10.0
Al.sub.2 O.sub.3
3.5
B.sub.2 O.sub.3
26.3.
______________________________________
Claim 5
Dependent Claim
20 words
The method of claim 3 wherein said applying step comprises heating to a temperature of less than about 650° C.
Claim 6
Independent Claim
173 words
A method for attaching a semiconductor die to a ceramic base comprising: locating a ductile foil of a predetermined foil melting temperature and foil yield strength directly on a portion of said base, said foil yield strength being less than the yield strength of said die and base; bonding said foil directly to said base by heat and pressure; providing between said die and said foil a die bonding material comprising a glass-ceramic mixture and having predetermined softening temperature, coefficient of expansion, and yield strength, wherein said material has a softening temperature less than said foil melting temperature, and wherein said material has a yield strength greater than said foil yield strength; positioning said die and said base so that said material contacts said die and said foil; heating and pressing together said foil and said die at a temperature exceeding the softening temperature of said material and less than the melting temperature of said foil, so as to distribute substantially uniformly and without voids said material between said foil and said die.
Claim 7
Independent Claim
173 words
A method for attaching a semiconductor die to a ceramic base comprising: locating a ductile foil of a predetermined foil melting temperature and foil yield strength directly on a portion of said base, said foil yield strength being less than the yield strength of said die and base; bonding said foil directly to said base by heat and pressure; providing between said die and said foil a die bonding material comprising a glass-ceramic mixture and having predetermined softening temperature, coefficient of expansion, and yield strength, wherein said material has a softening temperature less than said foil melting temperature, and wherein said material has a yield strength greater than said foil yield strength; positioning said die and said base so that said material contacts said die and said foil; heating and pressing together said foil and said die at a temperature exceeding the softening temperature of said material and less than the melting temperature of said foil, so as to distribute substantially uniformly and without voids said material between said foil and said die.
Claim 8
Dependent Claim
30 words
The method of claim 5 wherein said bonding step comprises heating to a temperature less than said foil melting temperature and applying a pressure greater than said foil yield strength.
Claim 9
Dependent Claim
16 words
The method of claim 6 wherein said ductile foil comprises substantially aluminum or ductile aluminum alloy.
Claim 10
Dependent Claim
75 words
The method of claim 7 wherein said providing step comprises supplying a die bonding material made of a titania free base glass to which has been added 23.6 to 36.4 weight percent lead titanate powder to yield a mixture consisting essentially of ingredients by weight percent in the range of: ______________________________________
GeO.sub.2
2.5-10.7
SiO.sub.2
0-2.3
PbO 58.6-78.5
PbF.sub.2
0-5.3
B.sub.2 O.sub.3
7.0-13.0
Al.sub.2 O.sub.3
2.5-6.9
ZnO 0-5.3
V.sub.2 O.sub.5
0.4-2.3
CdO 0-5.3
TiO.sub.2
6.2-9.6.
______________________________________
Claim 11
Dependent Claim
24 words
The method of claim 8 wherein said supplying step comprises preparing a die bonding material having a thickness greater than 0.1 mil (2.5 μm).
Claim 12
Dependent Claim
25 words
The method of claim 9 wherein said supplying step further comprises preparing a die bonding material having a thickness greater than 0.5 mil (12.5 μm).
Claim 13
Dependent Claim
66 words
The method of claim 9 wherein said positioning, heating, and pressing together steps comprise pre-heating said base for a predetermined first time, pressing said die with said die bonding material against said foil for a predetermined second time, and scrubbing said die with respect to said base for a predetermined third time so as to spread said die bonding material between said die and said foil.
Claim 14
Independent Claim
250 words
A method for attaching a semiconductor die to a ceramic base comprising: locating a ductile foil of a predetermined foil melting temperature and foil yield strength on a portion of said base, said foil yield strength being less than the yield strength of said die and base; bonding said foil to said base by including a foil bonding glass between said foil and said base, heating to a temperature sufficient to permit said foil bonding glass to flow but less than said foil melting temperature and applying pressure sufficient to spread said foil bonding glass substantially uniformly between said foil and said base, and wherein said foil bonding glass comprises ingredients by weight percent in the range of SiO 2 (10-15%), PbO (45-55%), ZnO (8-12%), Al 2 O 3 (2-5%), and B 2 O 3 (25-30%); providing between said die and said foil a die bonding material comprising a glass-ceramic mixture and having predetermined softening temperature, coefficient of expansion, and yield strength, wherein said material has a softening temperature less than said foil melting temperature, and wherein said material has a yield strength greater than said foil yield strength; positioning said die and said base so that said material contacts said die and said foil; heating and pressing together said foil and said die at a temperature exceeding the softening temperature of said material and less than the melting temperature of said foil, so as to distribute substantially uniformly and without voids said material between said foil and said die.
Claim 15
Independent Claim
250 words
A method for attaching a semiconductor die to a ceramic base comprising: locating a ductile foil of a predetermined foil melting temperature and foil yield strength on a portion of said base, said foil yield strength being less than the yield strength of said die and base; bonding said foil to said base by including a foil bonding glass between said foil and said base, heating to a temperature sufficient to permit said foil bonding glass to flow but less than said foil melting temperature and applying pressure sufficient to spread said foil bonding glass substantially uniformly between said foil and said base, and wherein said foil bonding glass comprises ingredients by weight percent in the range of SiO 2 (10-15%), PbO (45-55%), ZnO (8-12%), Al 2 O 3 (2-5%), and B 2 O 3 (25-30%); providing between said die and said foil a die bonding material comprising a glass-ceramic mixture and having predetermined softening temperature, coefficient of expansion, and yield strength, wherein said material has a softening temperature less than said foil melting temperature, and wherein said material has a yield strength greater than said foil yield strength; positioning said die and said base so that said material contacts said die and said foil; heating and pressing together said foil and said die at a temperature exceeding the softening temperature of said material and less than the melting temperature of said foil, so as to distribute substantially uniformly and without voids said material between said foil and said die.
Claim 16
Independent Claim
276 words
A method for attaching a semiconductor die to a ceramic base comprising: locating a ductile foil comprising substantially aluminum or ductile aluminum alloy and having a predetermined foil melting temperature and foil yield strength, on a portion of said base, said foil yield strength being less than the yield strength of said die and base; bonding said foil to said base by heating to a temperature less than said foil melting temperature and applying a pressure greater than said foil yield strength; providing between said die and said foil a die bonding material comprising a glass-ceramic mixture and having predetermined softening temperature, coefficient of expansion, and yield strength, wherein said material has a softening temperature less than said foil melting temperature, and wherein said material has a yield strength greater than said foil yield strength; wherein said die bonding material is made of a titania free base glass to which has been added 23.6 to 36.4 weight percent lead titanate power to yield a mixture consisting essentially of ingredients by weight percent in the range of GeO 2 (2.5-10.7%), SiO 2 (0-2.3%), PbO (58.6-78.5%), PbF 2 (0-5.3%), B 2 O 3 (7.0-13.0%), Al 2 O 3 (2.5-6.9%), ZnO (0-5.3%), V 2 O 5 (0.4-2.3%), CdO (0-5.3%), TiO 2 (6.2-9.6%); positioning said die and said base so that said die bonding material contacts said die and said foil; heating and pressing together said foil and said die at a temperature exceeding the softening temperature of said die bonding material and less than the melting temperature of said foil, so as to distribute said die bonding material substantially uniformly and without voids between said foil and said die.
Claim 17
Independent Claim
276 words
A method for attaching a semiconductor die to a ceramic base comprising: locating a ductile foil comprising substantially aluminum or ductile aluminum alloy and having a predetermined foil melting temperature and foil yield strength, on a portion of said base, said foil yield strength being less than the yield strength of said die and base; bonding said foil to said base by heating to a temperature less than said foil melting temperature and applying a pressure greater than said foil yield strength; providing between said die and said foil a die bonding material comprising a glass-ceramic mixture and having predetermined softening temperature, coefficient of expansion, and yield strength, wherein said material has a softening temperature less than said foil melting temperature, and wherein said material has a yield strength greater than said foil yield strength; wherein said die bonding material is made of a titania free base glass to which has been added 23.6 to 36.4 weight percent lead titanate power to yield a mixture consisting essentially of ingredients by weight percent in the range of GeO 2 (2.5-10.7%), SiO 2 (0-2.3%), PbO (58.6-78.5%), PbF 2 (0-5.3%), B 2 O 3 (7.0-13.0%), Al 2 O 3 (2.5-6.9%), ZnO (0-5.3%), V 2 O 5 (0.4-2.3%), CdO (0-5.3%), TiO 2 (6.2-9.6%); positioning said die and said base so that said die bonding material contacts said die and said foil; heating and pressing together said foil and said die at a temperature exceeding the softening temperature of said die bonding material and less than the melting temperature of said foil, so as to distribute said die bonding material substantially uniformly and without voids between said foil and said die.
Claim 18
Dependent Claim
24 words
The method of claim 13 wherein said supplying step comprises preparing a die bonding material having a thickness greater than 0.1 mil. (2.5 microns).
Claim 19
Dependent Claim
25 words
The method of claim 14 wherein said supplying step further comprises preparing a die bonding material having a thickness greater than 0.5 mil (12.5 microns).
Claim 20
Dependent Claim
66 words
The method of claim 14 wherein said positioning, heating, and pressing together steps comprise pre-heating said base for a predetermined first time, pressing said die and said die bonding material against said foil for a predetermined second time, and scrubbing said die with respect to said base for a predetermined third time so as to spread said die bonding material between said die and said foil.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-02 | 1989-12-02 | 1990-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-02 | 1993-12-02 | 1994-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-02 | 1997-12-02 | 1998-06-03 | $7700.00 | Window Closed / Lapsed |