Antistatic thermoplastic composition comprising a graft polymer, halogenated thermoplastic polymer and conductive carbon black
Assignee: UNIROYAL TECHNOLOGY Corp A CORP OF DELAWARE
•
Filing: 1984-06-08
•
Granted: 1986-06-03
•
Expires: 2004-06-08
Abstract
Abstract An antistatic thermoplastic composition comprising a blend of a thermoplastic graft polymer; a thermoplastic halogenated polymer; and an amount of conductive carbon black effective to cause the composition to have a surface resistivity of 102-1012 ohm/square, wherein the ratio of (a)/(b) is from 9:1-1:9, by weight and the weight percentage of (c) is from 2-10%.
Inventors
- 👤 Solomon Bekele
- 👤 Victor W. Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:54
CPC Classifications
C; C08; C08L; C08L27/00; C08L27/02; C08L27/04; C08L27/06; C08K; C08K3/00; C08K3/02; C08K3/04; C08L51/00; C08L51/04; C08L51/06; C08L2205/00; C08L2205/02; C08L23/00; C08L23/26; C08L23/28; C08L23/286; C08L55/00; C08L55/02
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
61 words
An antistatic thermoplastic composition comprising a blend of (a) a thermoplastic graft polymer; (b) a thermoplastic halogenated polymer; and (c) an amount of conductive carbon black effective to cause the composition to have a surface resistivity of 10 2 -10 12 ohm/square, wherein the ratio of (a)/(b) is from 9:1-1:9, by weight and the weight percentage of (c) is from 2-10%.
Claim 2
Dependent Claim
61 words
An antistatic thermoplastic composition comprising a blend of (a) a thermoplastic graft polymer; (b) a thermoplastic halogenated polymer; and (c) an amount of conductive carbon black effective to cause the composition to have a surface resistivity of 10 2 -10 12 ohm/square, wherein the ratio of (a)/(b) is from 9:1-1:9, by weight and the weight percentage of (c) is from 2-10%.
Claim 3
Dependent Claim
22 words
The composition of claim 1 wherein said graft polymer (a) is based on a diene rubber spine or an ethylene-propylene-nonconjugated diene spine.
Claim 4
Dependent Claim
16 words
The composition of claim 1 wherein said halogenated polymer (b) is a thermoplastic containing chlorine atoms.
Claim 5
Dependent Claim
17 words
The composition of claim 2 wherein (a) is a diene rubber grafted with styrene and acrylonitrile monomer.
Claim 6
Dependent Claim
10 words
The composition of claim 3 wherein (b) is poly(vinyl chloride).
Claim 7
Dependent Claim
21 words
The composition of claim 1 wherein said conductive carbon black (c) has a BET surface area of 500-1500 m 2 /g.
Claim 8
Dependent Claim
33 words
The composition of claim 1, wherein the ratio of (a)/(b) is from 1.5:1-2.3:1 and the percentage weight of (c) is from 5-7.5%, and the surface resistivity is from 10 5 -10 8 .
References Cited (Backward Citations)
US3053800A
Cited
US3877605A
Cited
US4129608A
Cited
US4128539A
Cited
US4228050A
Cited
US4386175A
Cited
US4280941A
Cited
US4351747A
Cited
US4299736A
Cited
US4378310A
Cited
US4329276A
Cited
US4329278A
Cited
US4396660A
Cited
US4465615A
Cited
JPS57200435A
Cited
US4412941A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-02 | 1989-12-02 | 1990-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-02 | 1993-12-02 | 1994-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-02 | 1997-12-02 | 1998-06-03 | $7700.00 | Window Closed / Lapsed |