Method for making a fine powder of a metal compound having ceramic coatings thereon
Assignee: Toyota Motor Corp
•
Filing: 1985-01-18
•
Granted: 1986-12-30
•
Expires: 2005-01-18
Abstract
Abstract A method for making fine powder of a metallic compound coated with ceramics is described. In the method, a gaseous mixture of at least one metal vapor constituting one component of a metallic compound and a carrier gas for the at least one metal vapor is passed at a speed of 50 to 2000 m/second into another element constituting the other element of the metallic compound or in an atmosphere of a gas containing the other element, which is heated to a temperature of not larger than 0.8 time as low as a melting point of the at least one metal so that the metal vapor and another element are reacted with each other while rapidly cooling, thereby obtaining a fine powder of a metallic compound. The metallic compound fine powder is further passed into other metal vapor or other metallic compound vapor to cover the metallic compound fine powder with the film of the other metal or metallic compound.
Inventors
- 👤 Masahiro Ogawa
- 👤 Susumu Abe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:59
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/223; B; B22; B22F; B22F1/00; B22F1/16; B22F9/00; B22F9/02; B22F9/12; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/622; C04B35/64
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
201 words
A method for preparing a finely powdered product of a metallic compound coated with a ceramic, comprising the steps of: (a) providing a gaseous mixture of at least one metal vapor, which constitutes one element of said metallic compound, in a carrier gas; (b) passing said gaseous mixture through a nozzle, thereby rapidly cooling said gaseous mixture by adiabatic expansion of the mixture, into an atmosphere comprising a gas containing the other element of said metallic compound by utilizing the pressure difference between the gaseous mixture and said atmosphere, said atmosphere being heated to a temperature not greater than 0.8 times as low as the melting point of the metal of said metal vapor so that both of said elements react with each other as the rapid cooling of the mixed gases occurs, thereby forming a vapor containing said metallic compound in a fine powder form; (c) passing the vapor of finely divided metallic compound through a second vapor of a metal or metal compound of said ceramic, thereby resulting in deposition of the metal or metal compound of the ceramic on the finely powdered metallic compound; and (d) oxidizing the deposited second metal or metal compound to a ceramic coating.
Claim 2
Independent Claim
201 words
A method for preparing a finely powdered product of a metallic compound coated with a ceramic, comprising the steps of: (a) providing a gaseous mixture of at least one metal vapor, which constitutes one element of said metallic compound, in a carrier gas; (b) passing said gaseous mixture through a nozzle, thereby rapidly cooling said gaseous mixture by adiabatic expansion of the mixture, into an atmosphere comprising a gas containing the other element of said metallic compound by utilizing the pressure difference between the gaseous mixture and said atmosphere, said atmosphere being heated to a temperature not greater than 0.8 times as low as the melting point of the metal of said metal vapor so that both of said elements react with each other as the rapid cooling of the mixed gases occurs, thereby forming a vapor containing said metallic compound in a fine powder form; (c) passing the vapor of finely divided metallic compound through a second vapor of a metal or metal compound of said ceramic, thereby resulting in deposition of the metal or metal compound of the ceramic on the finely powdered metallic compound; and (d) oxidizing the deposited second metal or metal compound to a ceramic coating.
Claim 3
Dependent Claim
22 words
The method of claim 1, wherein said gaseous mixture is passed into said atmosphere at a speed of 50 to 2000 m/second.
Claim 4
Dependent Claim
18 words
The method of claim 1, wherein said metal or metal compound of the ceramic is a sintering aid.
Claim 5
Dependent Claim
13 words
The method of claim 1, wherein said carrier gas is an inert gas.
Claim 6
Independent Claim
150 words
A method of preparing a finely powdered product of a metallic compound coated with a ceramic, comprising the steps of: (a) providing a gaseous mixture of at least metal vapor, which constitutes one element of said metallic compound, in a carrier gas constituted of the other element of said metallic compound under conditions which provide for the rapid cooling of said gaseous mixture by adiabatic expansion, thereby allowing said elements to react with each other; (b) obtaining said metallic compound in the vapor state in finely powdered form as a result of said reaction; (c) passing the vapor containing said finely powdered metallic compound through a second vapor of a metal or metal compound of said ceramic, thereby resulting in deposition of the metal or metal compound of the ceramic on the finely powdered metallic compound; and (d) oxidizing the deposited second metal or metal compound to a ceramic coating.
Claim 7
Independent Claim
150 words
A method of preparing a finely powdered product of a metallic compound coated with a ceramic, comprising the steps of: (a) providing a gaseous mixture of at least metal vapor, which constitutes one element of said metallic compound, in a carrier gas constituted of the other element of said metallic compound under conditions which provide for the rapid cooling of said gaseous mixture by adiabatic expansion, thereby allowing said elements to react with each other; (b) obtaining said metallic compound in the vapor state in finely powdered form as a result of said reaction; (c) passing the vapor containing said finely powdered metallic compound through a second vapor of a metal or metal compound of said ceramic, thereby resulting in deposition of the metal or metal compound of the ceramic on the finely powdered metallic compound; and (d) oxidizing the deposited second metal or metal compound to a ceramic coating.
Claim 8
Dependent Claim
53 words
The method of claim 5, wherein said metal vapor of said gaseous mixture is silicon vapor, the remaining element of said metallic compound is nitrogen, and said gaseous mixture is heated to a temperature not less than 2000° C. with the pressure of said gaseous mixture being not more than 10 -1 atmospheres.
Claim 9
Dependent Claim
23 words
The method of claim 5, wherein said metal vapor is passed into said carrier gas at a speed of 50 to 2000 m/second.
Claim 10
Dependent Claim
22 words
The method of claim 5, wherein said carrier gas constitutes a gaseous compound containing the element which reacts with said metal vapor.
Claim 11
Dependent Claim
44 words
The method of claim 5, wherein said at least one metal vapor is silicon vapor, the carrier gas containing the element which reacts with said metal vapor being ammonia gas, said metallic compound product being silicon nitride, and said ceramic coating being yttrium oxide.
Claim 12
Dependent Claim
13 words
The method of claim 5, wherein said carrier gas is an inert gas.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-29 | 1990-06-30 | 1990-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-29 | 1994-06-30 | 1994-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-29 | 1998-06-30 | 1998-12-30 | $7700.00 | Window Closed / Lapsed |