Thermostable polycrystalline diamond body, method and mold for producing same
Assignee: ZHENGZHOU RESEARCH INSTITUTE FOR ABRASIVES & GRINDING STATE COMMISSIONOF MACHINERY INDUSTRY
•
Filing: 1984-12-14
•
Granted: 1987-02-17
•
Expires: 2004-12-14
Abstract
Abstract A thermostable polycrystalline diamond body is produced by pre-treating the diamond crystals with molten base or salt, mixing the pre-treated diamond crystals with silicon powder or a blend of silicon and one or more substances, subjecting the mixture to a combination of high-pressure and high-temperature and maintaining the pressure and temperature for a period of time. The thermostable polycrystalline diamond body is characterized in having diamond crystals uniformly distributed in the body. The diamond crystals are covered by beta -silicon carbide and that the diamond crystals together with beta -silicon carbide form an uninterrupted framework throughout the entire body, the interstices of which are filled with elemental silicon or silicon-containing refractory phases. A polygonal graphite mold having walls of equal thickness useful in the production of said thermostable polycrystalline diamond body is also provided.
Inventors
- 👤 Hongchang Yu
- 👤 Zhen Yang
- 👤 Chaodong Wang
- 👤 Zhongqing Zai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:18
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; B; B01; B01J; B01J3/00; B01J3/06; B01J3/062; B22; B22F; B22F3/00; B22F3/12; B22F3/14; B22F3/15; B24; B24D; B24D18/00; B24D18/0009; B24D3/00; B24D3/02; B24D3/04; B24D3/06; B30; B30B; B30B11/00; B30B11/004; B30B11/007; B30B15/00; B30B15/34; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/6316; C04B35/64; C04B35/645; C22; C22C; C22C26/00; B01J2203/00; B01J2203/06; B01J2203/0605; B01J2203/062; B01J2203/065; B01J2203/0655; B01J2203/0675; B01J2203/0685; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/38; C04B2235/3817; C04B2235/3821; C04B2235/3826; C04B2235/3834; C04B2235/40; C04B2235/404; C04B2235/405; C04B2235/42; C04B2235/421; C04B2235/422; C04B2235/427; C04B2235/428; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/5463; C04B2235/5472; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2235/70; C04B2235/80; C04B2235/96
Claims Analysis
Total Claims: 53
Claim 1
Independent Claim
73 words
A thermostable polycrystalline diamond body comprising about 70% to 99% by weight of diamond crystals with a grit size in the range of about 1 to about 150 microns uniformly distributed therein, the surface of said diamond crystals being covered with β-silicon carbide, and chemically and adherently bonded therewith to form an uninterrupted framework, the interstices of which are filled with elemental silicon which is chemically and adherently bonded to said β-silicon carbide.
Claim 2
Dependent Claim
73 words
A thermostable polycrystalline diamond body comprising about 70% to 99% by weight of diamond crystals with a grit size in the range of about 1 to about 150 microns uniformly distributed therein, the surface of said diamond crystals being covered with β-silicon carbide, and chemically and adherently bonded therewith to form an uninterrupted framework, the interstices of which are filled with elemental silicon which is chemically and adherently bonded to said β-silicon carbide.
Claim 3
Dependent Claim
176 words
A thermostable polycrystalline diamond body comprising about 70% to about 99% by weight of diamond crystals with a grit size in the range of about 1 to about 150 microns uniformly distributed therein, the surface of said diamond crystals being covered with β-silicon carbide and chemically and adherently bonded therewith to form an uninterrupted framework, the interstices of which are filled with a silicon-containing refractory phase chemically and adherently bonded to β-silicon carbide, said silicon-containing refractory phase consisting essentially of elemental silicon and one or more substances selected from the group consisting of a silicide of one or more elemental materials, a solution of one or more elemental materials in silicon, boron carbide and silicon carbide, said elemental material being selected from the group consisting of boron, titanium, nickel, cobalt, zirconium, niobium, molybdenum, vanadium, hafnium, chromium, an element of the lanthanum series of the periodic table and alloys thereof, the total amount of the elemental materials, boron carbide or silicon carbide being less than the content of silicon either in elemental form or in combined form.
Claim 4
Dependent Claim
176 words
A thermostable polycrystalline diamond body comprising about 70% to about 99% by weight of diamond crystals with a grit size in the range of about 1 to about 150 microns uniformly distributed therein, the surface of said diamond crystals being covered with β-silicon carbide and chemically and adherently bonded therewith to form an uninterrupted framework, the interstices of which are filled with a silicon-containing refractory phase chemically and adherently bonded to β-silicon carbide, said silicon-containing refractory phase consisting essentially of elemental silicon and one or more substances selected from the group consisting of a silicide of one or more elemental materials, a solution of one or more elemental materials in silicon, boron carbide and silicon carbide, said elemental material being selected from the group consisting of boron, titanium, nickel, cobalt, zirconium, niobium, molybdenum, vanadium, hafnium, chromium, an element of the lanthanum series of the periodic table and alloys thereof, the total amount of the elemental materials, boron carbide or silicon carbide being less than the content of silicon either in elemental form or in combined form.
Claim 5
Dependent Claim
53 words
A thermostable polycrystalline diamond body according to claim 2, wherein the grit size of the diamond crystals is in the range of from about 1 to about 100 microns, and the diamond crystals are present in an amount of about 85% to about 95% by weight of the total weight of said body.
Claim 6
Dependent Claim
29 words
A thermostable polycrystalline diamond body according to claim 2, wherein said elemental materials are selected from the group consisting of boron, nickel, cobalt, titanium, zirconium, niobium, molybdenum and vanadium.
Claim 7
Independent Claim
143 words
A method for preparing a thermostable polycrystalline diamond body comprising the steps of: (1) pre-treating diamond crystals with a molten base or a molten salt; (2) mixing the pre-treated diamond crystals uniformly with silicon powder or a blend of silicon powder and a material which will form a refractory phase with silicon; (3) placing the mixture into a mold, with a predetermined cavity shape; (4) placing the mold into a pre-formed pyrophyllite sample cube; (5) placing the sample cube into an apparatus capable of simultaneously producing high pressure along three axes and high temperature; (6) subjecting the mixture in the mold to a temperature in the range of about 1400° C. to about 2000° C. and a pressure of at least 50 kilobars; (7) maintaining the pressure and temperature for a period of time; (8) cooling the apparatus; and (9) releasing the pressure.
Claim 8
Independent Claim
143 words
A method for preparing a thermostable polycrystalline diamond body comprising the steps of: (1) pre-treating diamond crystals with a molten base or a molten salt; (2) mixing the pre-treated diamond crystals uniformly with silicon powder or a blend of silicon powder and a material which will form a refractory phase with silicon; (3) placing the mixture into a mold, with a predetermined cavity shape; (4) placing the mold into a pre-formed pyrophyllite sample cube; (5) placing the sample cube into an apparatus capable of simultaneously producing high pressure along three axes and high temperature; (6) subjecting the mixture in the mold to a temperature in the range of about 1400° C. to about 2000° C. and a pressure of at least 50 kilobars; (7) maintaining the pressure and temperature for a period of time; (8) cooling the apparatus; and (9) releasing the pressure.
Claim 9
Dependent Claim
39 words
A method acording to claim 5, wherein the diamond crystals are made of synthetic diamond, boron-doped synthetic diamond, natural diamond or a mixture thereof, and has a grit size of which ranges from about 1 to about 150 microns.
Claim 10
Dependent Claim
32 words
A method according to claim 5, wherein said molten base or salt is selected from the group consisting of sodium hydroxide, potassium hydroxide, sodium carbonate, sodium nitrate, potassium nitrate and mixtures thereof.
Claim 11
Dependent Claim
26 words
A method according to claim 7, wherein the molten base or salt is sodium hydroxide, potassium hydroxide, or a mixture of sodium carbonate and sodium nitrate.
Claim 12
Dependent Claim
100 words
A method according to claim 5, wherein the step of pre-treating said diamond crystals consists essentially of following steps: (1) treating said diamond crystals in the molten base or salt for about 5 minutes to about 1 hour; (2) cooling the mixture of the diamond and the base or salt to solid state; (3) dissolving the mixture with hot water; (4) removing the diamond crystals from the solution; (5) washing the diamond crystals with a dilute acid; (6) rinsing the diamond crystals with hot water several times; (7) removing the diamond crystals from water; and (8) drying the diamond crystals.
Claim 13
Dependent Claim
13 words
A method according to claim 9, wherein the acid is dilute hydrochloric acid.
Claim 14
Dependent Claim
55 words
A method according to claim 5, wherein the amount of the diamond crystals in the mixture is in the range of from about 70% to about 99% by weight of the total weight of the mixture, and the balance as silicon powder with a particle size which is finer than that of the diamond crystals.
Claim 15
Dependent Claim
20 words
A method according to claim 11, wherein the grit size of said silicon powder ranges from 1 to 50 microns.
Claim 16
Dependent Claim
122 words
A method according to claim 5, wherein the amount of the diamond crystals in the mixture is in the range of from about 70% to less than 99% by weight of the total weight of the mixture, with the balance a blend of silicon powder and a powder of one or more substances selected from the group consisting of boron carbide, silicon carbide, boron, titanium, nickel, cobalt, zirconium, niobium, molybdenum, vanadium, hafnium, chromium, an element of the lanthanum series of the periodic table and alloys thereof, the total amount of the substance being less than the amount of silicon in the mixture, and the grit size of the silicon powder and said powder substance being finer than that of the diamond crystals.
Claim 17
Dependent Claim
30 words
A method according to claim 13, wherein said powder substance is selected from the group consisting of boron carbide, silicon carbide, boron, titanium, nickel, cobalt, zirconium, niobium, molybdenum and vanadium.
Claim 18
Dependent Claim
24 words
A method according to claim 14, wherein the grit size of said silicon powder and the powder substance ranges from 1 to 50 microns.
Claim 19
Dependent Claim
54 words
A method according to claim 13, wherein the amount of diamond crystals is in the range of from about 85% to less than about 95% by weight of the mixture, and the amount of silicon powder is in the range of from about 5% to less than about 15% by weight of the mixture.
Claim 20
Dependent Claim
20 words
A method according to claim 5, wherein the pressure is in the range of from 50 to about 80 kilobars.
Claim 21
Dependent Claim
41 words
A method according to claim 5, wherein the pressure is raised to the highest level desired, followed by raising the temperature to the highest level desired, and maintaining the pressure and temperature for from about 10 seconds to about 10 minutes.
Claim 22
Dependent Claim
59 words
A method according to claim 5, wherein the pressure is raised to a level of about 90% of the highest level desired, followed by raising the temperature to the highest level desired and followed by raising the pressure to the highest level desired, maintaining the desired pressure and the temperature for from about 10 seconds to about 10 minutes.
Claim 23
Dependent Claim
50 words
A method according to claim 5, wherein the pressure is raised to a level of about 90% of the highest level desired followed by raising the temperature and pressure to the highest level simultaneously, and maintaining the pressure and temperature for a period of time up to about 10 minutes.
Claim 24
Dependent Claim
13 words
A thermostable polycrystalline diamond body prepared according to the method of claim 5.
Claim 25
Dependent Claim
17 words
An article prepared from a polycrystalline diamond body according to claims 1, 2, 3, 4 or 21.
Claim 26
Dependent Claim
36 words
A thermostable polycrysalline diamond body according to claim 4 wherein the elemental material is boron and is present in an amount up to about 5% by weight of the total weight of the polycrystalline diamond body.
Claim 27
Dependent Claim
36 words
A thermostable polycrysalline diamond body according to claim 4 wherein the elemental material is nickel and is present in an amount up to about 5% by weight of the total weight of the polycrystalline diamond body.
Claim 28
Dependent Claim
36 words
A thermostable polycrysalline diamond body according to claim 4 wherein the elemental material is cobalt and is present in an amount up to about 5% by weight of the total weight of the polycrystalline diamond body.
Claim 29
Dependent Claim
36 words
A thermostable polycrysalline diamond body according to claim 4 wherein the elemental material is titanium and is present in an amount up to about 15% by weight of the total weight of the polycrystalline diamond body.
Claim 30
Dependent Claim
36 words
A thermostable polycrysalline diamond body according to claim 4 wherein the elemental material is zirconium and is present in an amount up to about 2% by weight of the total weight of the polycrystalline diamond body.
Claim 31
Dependent Claim
36 words
A thermostable polycrysalline diamond body according to claim 4 wherein the elemental material is niobium and is present in an amount up to about 2% by weight of the total weight of the polycrystalline diamond body.
Claim 32
Dependent Claim
36 words
A thermostable polycrysalline diamond body according to claim 4 wherein the elemental material is molybdenum and is present in an amount up to about 2% by weight of the total weight of the polycrystalline diamond body.
Claim 33
Dependent Claim
36 words
A thermostable polycrysalline diamond body according to claim 4 wherein the elemental material is vanaduim and is present in an amount up to about 2% by weight of the total weight of the polycrystalline diamond body.
Claim 34
Dependent Claim
32 words
A method according to claim 14, wherein the powder is boron carbide and is present in an amount of up to about 5% by weight of the total weight of the mixture.
Claim 35
Dependent Claim
32 words
A method according to claim 14, wherein the powder is silicon carbide and is present in an amount of up to about 5% by weight of the total weight of the mixuture.
Claim 36
Dependent Claim
31 words
A method according to claim 14, wherein the powder is boron and is present in an amount of up to about 5% by weight of the total weight of the mixture.
Claim 37
Dependent Claim
31 words
A method according to claim 14, wherein the powder is titanium and is present in an amount of up to about 15% by weight of the total weight of the mixture.
Claim 38
Dependent Claim
31 words
A method according to claim 14, wherein the powder is nickel and is present in an amount of up to about 5% by weight of the total weight of the mixture.
Claim 39
Dependent Claim
31 words
A method according to claim 14, wherein the powder is cobalt and is present in an amount of up to about 5% by weight of the total weight of the mixture.
Claim 40
Dependent Claim
31 words
A method according to claim 14, wherein the powder is zirconium and is present in an amount of up to about 2% by weight of the total weight of the mixture.
Claim 41
Dependent Claim
31 words
A method according to claim 14, wherein the powder is niobium and is present in an amount of up to about 2% by weight of the total weight of the mixture.
Claim 42
Dependent Claim
31 words
A method according to claim 14, wherein the powder is molybdenum and is present in an amount of up to about 2% by weight of the total weight of the mixture.
Claim 43
Dependent Claim
34 words
A method according to claim 14, wherein the powder of boron substance is vanadium and is present in an amount of up to about 2% by weight of the total weight of the mixture.
Claim 44
Dependent Claim
31 words
A method according to claim 16 wherein the powder is boron carbide and is present in an amount up to about 5% by weight of the total weight of the mixture.
Claim 45
Dependent Claim
31 words
A method according to claim 16 wherein the powder is silicon carbide and is present in an amount up to about 5% by weight of the total weight of the mixture.
Claim 46
Dependent Claim
30 words
A method according to claim 16 wherein the powder is boron and is present in an amount up to about 5% by weight of the total weight of the mixture.
Claim 47
Dependent Claim
30 words
A method according to claim 16 wherein the powder is titanium and is present in an amount up to about 5% by weight of the total weight of the mixture.
Claim 48
Dependent Claim
30 words
A method according to claim 16 wherein the powder is nickel and is present in an amount up to about 3% by weight of the total weight of the mixture.
Claim 49
Dependent Claim
30 words
A method according to claim 16 wherein the powder is cobalt and is present in an amount up to about 3% by weight of the total weight of the mixture.
Claim 50
Dependent Claim
30 words
A method according to claim 16 wherein the powder is zirconium and is present in an amount up to about 2% by weight of the total weight of the mixture.
Claim 51
Dependent Claim
30 words
A method according to claim 16 wherein the powder is niobium and is present in an amount up to about 2% by weight of the total weight of the mixture.
Claim 52
Dependent Claim
30 words
A method according to claim 16 wherein the powder is molybdenum and is present in an amount up to about 2% by weight of the total weight of the mixture.
Claim 53
Dependent Claim
30 words
A method according to claim 16 wherein the powder is vanadium and is present in an amount up to about 2% by weight of the total weight of the mixture.
References Cited (Backward Citations)
US3306705A
Cited
US3520667A
Cited
US3684004A
Cited
US3911994A
Cited
US4171339A
Cited
US4469655A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-16 | 1990-08-18 | 1991-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-16 | 1994-08-18 | 1995-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-16 | 1998-08-18 | 1999-02-17 | $7700.00 | Window Closed / Lapsed |