System for selective metallization of electronic interconnection boards
Assignee: MECHATRONICS LLC
•
Filing: 1984-09-04
•
Granted: 1987-05-26
•
Expires: 2004-09-04
Abstract
Abstract An improved process for selective metallization of insulating substrates, as for example in the manufacture of wire scribed interconnection boards, is provided. The substrates optionally include one or more holes or cavities for electrical connections. The process comprises applying an insulating, hydrophobic mask onto the surface of a suitable insulating substrate so as to leave exposed selected areas to be metallized, contacting the substrate with an activator solution for a sufficient time to deposit a catalytic species onto the exposed areas of the substrate and the mask and on the walls of the holes or cavities and thereby render them catalytic to the reception of metal, accelerating the catalytic species and preferentially removing essentially all of the catalytic species from the hydrophobic mask by contacting the substrate with a chelating agent in an alkaline solution having a pH between about 10 and about 14 for a time period sufficient to remove essentially all of said catalytic species from the mask, and then contacting the substrate with a metal deposition solution to metallize only the exposed catalytic areas of the substrate not protected by the hydrophobic mask.
Inventors
- 👤 Michael P. Moisan
- 👤 Joseph P. Cook
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:05
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/182; H05K3/184; C; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1603; C23C18/1605; C23C18/1607; C23C18/1608; C23C18/1633; C23C18/1635; C23C18/1639; C23C18/1641; C23C18/18; C23C18/20; C23C18/2006; C23C18/2046; C23C18/2073; C23C18/208; C23C18/2086; C23C18/28; C23C18/285; C23C18/30; C23C18/31; C23C18/38; C23C18/40; C23C18/405; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0706; H05K2203/14; H05K2203/1415; H05K3/40; H05K3/42; H05K3/425; H05K3/426; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T29/49165
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
183 words
In a process for depositing metal on a wire scribed circuit board having at least one insulated wire affixed to a surface of a substrate or imbedded therein and having at least a portion of the surfaces of the substrate covered with a hydrophobic mask and having at least one hole or at least one blind via in the substrate and intersecting the wire, wherein the walls of the hole or blind via and the intersected wire are metallized by metal deposition, the improvement which comprises: contacting the surface of the substrate including said walls with an activator solution comprising an agent suitable for rendering exposed surfaces receptive to metal deposition; contacting the entire surface including said walls and said hydrophobic mask with an accelerator solution comprised of a chelating agent in an alkaline solution for a time period sufficient to selectively remove essentially all of the activator from the hydrophobic mask while accelerating the activator on said walls, the accelerator solution having a pH between about 10 and about 14; and depositing a metal layer on the catalyzed surface of said walls.
Claim 2
Dependent Claim
183 words
In a process for depositing metal on a wire scribed circuit board having at least one insulated wire affixed to a surface of a substrate or imbedded therein and having at least a portion of the surfaces of the substrate covered with a hydrophobic mask and having at least one hole or at least one blind via in the substrate and intersecting the wire, wherein the walls of the hole or blind via and the intersected wire are metallized by metal deposition, the improvement which comprises: contacting the surface of the substrate including said walls with an activator solution comprising an agent suitable for rendering exposed surfaces receptive to metal deposition; contacting the entire surface including said walls and said hydrophobic mask with an accelerator solution comprised of a chelating agent in an alkaline solution for a time period sufficient to selectively remove essentially all of the activator from the hydrophobic mask while accelerating the activator on said walls, the accelerator solution having a pH between about 10 and about 14; and depositing a metal layer on the catalyzed surface of said walls.
Claim 3
Dependent Claim
19 words
A process as defined in claim 1 wherein the alkaline acclerator solution is agitated when contacted with the substrate.
Claim 4
Dependent Claim
35 words
A process as defined in claim 1 further including the step of contacting the mask and the surfaces of the substrate including said walls with a cleaner/conditioner solution prior to contacting them with the activator.
Claim 5
Dependent Claim
27 words
A process as defined in claim 1 wherein said chelating agent is selected from the group consisting of an amino acid, an alkanolamine and a polyfunctional carboxylate.
Claim 6
Dependent Claim
15 words
A process as defined in claim 4 wherein said chelating agent comprises an amino acid.
Claim 7
Dependent Claim
29 words
A process as defined in claim 5 wherein said amino acid is selected from the group consisting of hydroxy ethylenediamine triacetic acid and salts thereof, glycine, and nitrilotriacetic acid.
Claim 8
Dependent Claim
14 words
A process as defined in claim 4 wherein said chelating agent comprises an alkanolamine.
Claim 9
Dependent Claim
27 words
A process as defined in claim 7 wherein said alkanolamine is selected from the group consisting of hydroxyethylenediamine tetraacetic acid and salts thereof, and ethylene diamine tetrapropanol.
Claim 10
Dependent Claim
15 words
A process as defined in claim 4 wherein said chelating agent comprises a polyfunctional carboxylate.
Claim 11
Dependent Claim
17 words
A process as defined in claim 9 wherein said polyfunctional carboxylate comprises a citrate or a tartrate.
Claim 12
Dependent Claim
19 words
A process as defined in claim 1 wherein the activator solution comprises a solution of palladium, tin and chloride.
Claim 13
Dependent Claim
26 words
A process as defined in claim 1 wherein the activator is removed to leave a concentration thereof on the mask below about 0.002 mg/cm 2 .
Claim 14
Dependent Claim
18 words
A process as defined in claim 1 wherein the alkaline accelerator solution is agitated at a predetermined rate.
Claim 15
Dependent Claim
24 words
A process as defined in claim 11 wherein said metal layer is deposited on the activated surface of said walls by electroless metal deposition.
Claim 16
Dependent Claim
202 words
An improved process for producing a printed circuit on surfaces of an insulating substrate by electroless metal plating, said process including the steps of: applying a negative, hydrophobic and insulating mask onto a surface of the substrate whereby portions of the surface are unmasked and exposed, the surface of the mask material being resistant to the deposition of a catalytic species capable of catalyzing an electroless metal deposition; contacting with a catalyst comprising an agent capable of promoting metal deposition, the mask and any unmasked portion of the substrate surface; contacting the entire surface of the substrate and mask with an accelerator solution; removing the catalytic species from the surface of the mask; and contacting the substrate surface with an electroless metal plating solution to form an electroless metal layer on the unmasked portion of the substrate surface; the improvement which comprises: using as the accelerator solution a chelating agent in an alkaline solution having a pH between about 10 and about 14, and contacting the substrate surface with such alkaline accelerator for a time period sufficient to remove essentially all the catalytic species from the surface of the mask and leave catalytic species on the unmasked portion of the substrate surface.
Claim 17
Dependent Claim
202 words
An improved process for producing a printed circuit on surfaces of an insulating substrate by electroless metal plating, said process including the steps of: applying a negative, hydrophobic and insulating mask onto a surface of the substrate whereby portions of the surface are unmasked and exposed, the surface of the mask material being resistant to the deposition of a catalytic species capable of catalyzing an electroless metal deposition; contacting with a catalyst comprising an agent capable of promoting metal deposition, the mask and any unmasked portion of the substrate surface; contacting the entire surface of the substrate and mask with an accelerator solution; removing the catalytic species from the surface of the mask; and contacting the substrate surface with an electroless metal plating solution to form an electroless metal layer on the unmasked portion of the substrate surface; the improvement which comprises: using as the accelerator solution a chelating agent in an alkaline solution having a pH between about 10 and about 14, and contacting the substrate surface with such alkaline accelerator for a time period sufficient to remove essentially all the catalytic species from the surface of the mask and leave catalytic species on the unmasked portion of the substrate surface.
Claim 18
Dependent Claim
109 words
A process as defined in claim 15 which further includes the steps of: providing one or more holes in the insulating substrate at preselected points; leaving the holes exposed during the application of the mask; adhesion promoting walls of the holes; activating the walls of the holes to form the catalytic species thereon; contacting the catalyst species on the hole walls with the accelerator solution; and contacting the hole walls with the electroless metal plating solution to form the electroless metal layer on the hole walls which, in conjunction with the electroless metal layer on the positive pattern of the substrate surface, forms a plated through-hole printed circuit board.
Claim 19
Dependent Claim
56 words
A process as defined in claim 16 wherein the insulating substrate comprises a resinous material, the holes are provided by a drilling step which also smears resin on the walls of the hole, and wherein the walls of the holes are adhesion promoted with an oxidizing solution to remove any resin smears from the hole walls.
Claim 20
Dependent Claim
25 words
A process as defined in claim 15 wherein the activating step uses an activator solution comprised of stannous ions and precious metal ions in solution.
Claim 21
Dependent Claim
37 words
A process as defined in claim 17 wherein the mask comprises a material selected from the group consisting of epoxy novolak resin, silicone resin, polyethylene resin, fluorocarbon resin, polyurethane resin, acrylic resin and mixtures of the foregoing.
Claim 22
Dependent Claim
13 words
A process as defined in claim 15 wherein the electroless metal comprises copper.
Claim 23
Dependent Claim
191 words
An improved process for producing a printed circuit on surfaces of an insulating substrate, said process including the steps of: providing a circuit pattern on a surface of the substrate; unselectively applying a nonregistered, hydrophobic and insulating mask over the circuit pattern; subsequently forming a hole through the nonregistered insulating mask and into the insulating substrate; contacting the surface of the substrate including the wall of said hole with a catalyst solution comprising an agent capable of promoting metal deposition; contacting the entire surface of the substrate and mask with an accelerator solution; removing the catalytic species from the surface of the mask; and contacting the entire surface of the substrate and mask with an electroless metal plating solution to form an electroless metal layer on the hole wall; the improvement which comprises: using as the accelerator solution a chelating agent in an alkaline solution having a pH between about 10 and about 14, and contacting the substrate surface with such alkaline accelerator for a time period sufficient to remove essentially all the catalytic species from the surface of the mask and leave catalytic species on the wall of the hole.
Claim 24
Dependent Claim
191 words
An improved process for producing a printed circuit on surfaces of an insulating substrate, said process including the steps of: providing a circuit pattern on a surface of the substrate; unselectively applying a nonregistered, hydrophobic and insulating mask over the circuit pattern; subsequently forming a hole through the nonregistered insulating mask and into the insulating substrate; contacting the surface of the substrate including the wall of said hole with a catalyst solution comprising an agent capable of promoting metal deposition; contacting the entire surface of the substrate and mask with an accelerator solution; removing the catalytic species from the surface of the mask; and contacting the entire surface of the substrate and mask with an electroless metal plating solution to form an electroless metal layer on the hole wall; the improvement which comprises: using as the accelerator solution a chelating agent in an alkaline solution having a pH between about 10 and about 14, and contacting the substrate surface with such alkaline accelerator for a time period sufficient to remove essentially all the catalytic species from the surface of the mask and leave catalytic species on the wall of the hole.
References Cited (Backward Citations)
US3443988A
Cited
US3562038A
Cited
US3799816A
Cited
US4293592A
Cited
US4151313A
Cited
US4181750A
Cited
US4388351A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-25 | 1990-11-24 | 1991-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-25 | 1994-11-24 | 1995-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-25 | 1998-11-24 | 1999-05-26 | $7700.00 | Window Closed / Lapsed |