Patent US4678718A successfully refreshed from Google Patents.
US4678718A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process and usage of ceriated tungsten electrode material
Assignee: Shanghai Lamp Factory
•
Filing: 1985-09-03
•
Granted: 1987-07-07
•
Expires: 2005-09-03
Abstract
Abstract The mentioned ceriated tungsten material is a non-radioactive, hardly consumable or nonconsumable matallic electrode material, utilized in the inert gas shield arc welding, plasma welding, cutting, spray coating and smelting. It can also be used as electrodes for laser transmitting source and gas discharging light source. Moreover, the said material can be utilized to make as the cathodic filament used in film deposition by electronic beam under vacuum, etc. This invention employs the technique of powder metallurgy, by strictly controlling the processing parameters to fabricate the ceriated-tungsten material, containing 1.0-4.5%* ceric oxide. Thereby, the difficulties, that had been existed for quite a long time of its processing brittleness in forging the ceriated tungsten material over 1.0%, have now been satisfactorily overcome. * ceric oxide=ceria +PG]
Inventors
- 👤 Ju-Zhen Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:17
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/222; B23K35/40; B23K35/402; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12104; Y10T428/12111
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
118 words
A process utilizing a powder metallurgical technique in forming a ceriated-tungsten electrode including the steps of (a) preparing a quantity of tungsten trioxide, (b) preparing a cerium nitrate solution, (c) adding a sufficient quantity of cerium nitrate solution to the tungsten trioxide to provide 1-4.5% by weight cerium oxide to the ceriated-tungsten electrode material, (d) drying and calcining the resulting mixture, then reducing the dried and calcined mixture in a reducing atmosphere, (e) pressing the reduced product into bar form, (f) presintering and sintering the bar under reducing conditions, (g) forging and annealing the bar, (h) preparing a wire by drawing the bar to a diameter of less than 3.0 mm, and (i) recovering the ceriated tungsten product.
Claim 2
Dependent Claim
118 words
A process utilizing a powder metallurgical technique in forming a ceriated-tungsten electrode including the steps of (a) preparing a quantity of tungsten trioxide, (b) preparing a cerium nitrate solution, (c) adding a sufficient quantity of cerium nitrate solution to the tungsten trioxide to provide 1-4.5% by weight cerium oxide to the ceriated-tungsten electrode material, (d) drying and calcining the resulting mixture, then reducing the dried and calcined mixture in a reducing atmosphere, (e) pressing the reduced product into bar form, (f) presintering and sintering the bar under reducing conditions, (g) forging and annealing the bar, (h) preparing a wire by drawing the bar to a diameter of less than 3.0 mm, and (i) recovering the ceriated tungsten product.
Claim 3
Dependent Claim
25 words
The process of claim 1 wherein the dried and calcined mixture is reduced in a reducing atmosphere at a temperature of less than 750° C.
Claim 4
Dependent Claim
40 words
The process of claim 2 wherein the resulting mixture is reduced a second time in a reducing atmosphere at a temperature of less than 900° C., and wherein the tungsten powder obtained has a grain size of less than 8μ.
Claim 5
Dependent Claim
22 words
The process of claim 1 wherein the reduced product is pressed into bar form at a pressure of 1.5-3.5 ton/cm 2 .
Claim 6
Dependent Claim
33 words
The process of claim 1 wherein said bar is presintered at a temperature of 1100°-1250° C., and said bar is sintered through a current not greater than 85% of a cut-off fuse current.
Claim 7
Dependent Claim
33 words
The process of claim 1 wherein the amount of cerium nitrate solution added to the tungsten trioxide is sufficient to provide 88% of the amount of cerium required by the ceriated tungsten product.
Claim 8
Dependent Claim
32 words
The process of claim 6 wherein the cerium nitrate solution is doped into the tungsten trioxide, and wherein the doped tungsten trioxide is dried and calcined at a temperature of 300°-800° C.
Claim 9
Dependent Claim
47 words
The process of claim 1 wherein the bar of substantially square outline is rotary forged at a temperature which decreases from 1750° C. to about 1300° C. as the bar of substantially square outline is formed to a rod of substantially round outline of about 3.0 mm.
Claim 10
Dependent Claim
12 words
The process of claim 8 including annealing the bar during rotary forging.
Claim 11
Dependent Claim
44 words
The process of claim 9 wherein the rotary forged bar is drawn at a temperature which decreases from 1300° C. to about 700° C. as the diameter of the bar is reduced to less than 3.0 mm, and including annealing the bar during drawing.
Claim 12
Dependent Claim
20 words
A non-consumable electrode material of a tungsten-base material formed by the powder metallurgical technique of the process of claim 1.
Claim 13
Dependent Claim
13 words
The non-consumable electrode material of claim 11 including 2-4.5% by weight cerium oxide.
Claim 14
Dependent Claim
13 words
The non-consumable electrode material of claim 12 including 3-4.5% by weight cerium oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-06 | 1991-01-05 | 1991-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-06 | 1995-01-05 | 1995-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-06 | 1999-01-05 | 1999-07-07 | $7700.00 | Window Closed / Lapsed |