US4726104A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Methods for weld repairing hollow, air cooled turbine blades and vanes
Assignee: RTX Corp
•
Filing: 1986-11-20
•
Granted: 1988-02-23
•
Expires: 2006-11-20
Abstract
Abstract A mask particularly useful in the weld repair of air cooled gas turbine blades and vanes contains a mixture of ceramic particles in a liquid carrier. The mask is applied onto the surface of the blade or vane, and into the cooling holes. Following a sintering treatment, an inert, thermally stable, electrically nonconductive ceramic mask is produced, which is easily removed after welding.
Inventors
- 👤 Michael F. Foster
- 👤 Thomas A. Ferguson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:25
CPC Classifications
F; F01; F01D; F01D5/00; F01D5/12; F01D5/14; F01D5/20; B; B23; B23K; B23K35/00; B23K35/22; B23K35/224; B23K37/00; B23K37/06; B23P; B23P6/00; B23P6/002; B23P6/007; F01D5/005; B23K2101/00; B23K2101/001; Y; Y10; Y10S; Y10S29/00; Y10S29/048; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/49318; Y10T29/49718; Y10T29/49746
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
95 words
A method for keeping a portion of a metal article substantially free from molten weld filler metal during welding, comprising the steps of applying a compound containing ceramic particles in a liquid carrier to the portion of the article to be kept free of the filler metal, and heating the article to remove the liquid carrier from the mixture and to sinter the ceramic particles to each other to form a thermally stable ceramic mask which is nonreactive with the metal article and with the molten filler metal, and readily removable from the welded article.
Claim 2
Independent Claim
95 words
A method for keeping a portion of a metal article substantially free from molten weld filler metal during welding, comprising the steps of applying a compound containing ceramic particles in a liquid carrier to the portion of the article to be kept free of the filler metal, and heating the article to remove the liquid carrier from the mixture and to sinter the ceramic particles to each other to form a thermally stable ceramic mask which is nonreactive with the metal article and with the molten filler metal, and readily removable from the welded article.
Claim 3
Dependent Claim
12 words
The method of claim 1, wherein the ceramic mask is electrically nonconductive.
Claim 4
Independent Claim
111 words
A method for the arc weld repair of a hollow, air cooled metal article having a plurality of small diameter cooling holes, the method comprising the steps of filling the holes with a compound containing ceramic particles in a liquid carrier, the mixture having a paste-like consistency; heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable, electrically nonconductive, nonreactive ceramic mask which fills the cooling holes after sintering; welding the metal article, wherein the ceramic mask prevents molten weld metal from entering and solidifying in the holes; and removing the ceramic mask from the holes.
Claim 5
Independent Claim
111 words
A method for the arc weld repair of a hollow, air cooled metal article having a plurality of small diameter cooling holes, the method comprising the steps of filling the holes with a compound containing ceramic particles in a liquid carrier, the mixture having a paste-like consistency; heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable, electrically nonconductive, nonreactive ceramic mask which fills the cooling holes after sintering; welding the metal article, wherein the ceramic mask prevents molten weld metal from entering and solidifying in the holes; and removing the ceramic mask from the holes.
Claim 6
Independent Claim
207 words
A method for arc weld repairing an air cooled, hollow turbine blade having a tip portion, a squealer pocket, and an airfoil portion, wherein the blade has a plurality of small diameter cooling holes in the tip portion, the squealer pocket, and the airfoil portion, and wherein some of the holes are shaped holes, the method comprising the steps of filling the squealer pocket and the cooling holes and coating the airfoil portion with compound containing ceramic particles in a liquid carrier, the mixture having a paste-like consistency; heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable, nonreactive, electrically nonconductive ceramic mask which fills the squealer and the cooling holes after sintering; arc weld repairing the tip portion of the blade by depositing a layer of filler metal on the blade tip surface, wherein the ceramic mask in the squealer pocket prevents the weld metal from solidifying in the squealer, the ceramic mask in the cooling holes prevents the weld metal from solidifying in the holes and the ceramic mask on the airfoil portion prevents the weld metal from solidifying on the airfoil; and removing the ceramic mask from the blade.
Claim 7
Independent Claim
207 words
A method for arc weld repairing an air cooled, hollow turbine blade having a tip portion, a squealer pocket, and an airfoil portion, wherein the blade has a plurality of small diameter cooling holes in the tip portion, the squealer pocket, and the airfoil portion, and wherein some of the holes are shaped holes, the method comprising the steps of filling the squealer pocket and the cooling holes and coating the airfoil portion with compound containing ceramic particles in a liquid carrier, the mixture having a paste-like consistency; heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable, nonreactive, electrically nonconductive ceramic mask which fills the squealer and the cooling holes after sintering; arc weld repairing the tip portion of the blade by depositing a layer of filler metal on the blade tip surface, wherein the ceramic mask in the squealer pocket prevents the weld metal from solidifying in the squealer, the ceramic mask in the cooling holes prevents the weld metal from solidifying in the holes and the ceramic mask on the airfoil portion prevents the weld metal from solidifying on the airfoil; and removing the ceramic mask from the blade.
Claim 8
Dependent Claim
32 words
The method of claim 4, wherein the ceramic particles are selected from the group consisting essentially of simple and complex oxides of Group IIA, IIIA, IVA, IIIB, IVB and rare earth elements.
Claim 9
Dependent Claim
25 words
The method of claim 5, wherein the mixture of ceramic particles consists essentially of silica, zircon, and alumina, and the liquid carrier is colloidal silica.
Claim 10
Independent Claim
89 words
A method for the arc weld repair of a defect in a metal article having an internal cavity, comprising the steps of inserting a paste-like compound containing ceramic particles in a liquid carrier in the cavity; heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable nonreactive ceramic mask in the internal cavity; machining away the defect without removing a substantial amount of the mask; weld repairing the defect; and removing the ceramic mask.
Claim 11
Independent Claim
89 words
A method for the arc weld repair of a defect in a metal article having an internal cavity, comprising the steps of inserting a paste-like compound containing ceramic particles in a liquid carrier in the cavity; heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable nonreactive ceramic mask in the internal cavity; machining away the defect without removing a substantial amount of the mask; weld repairing the defect; and removing the ceramic mask.
Claim 12
Dependent Claim
38 words
A mixture sinterable to form a mask used during the weld repair of a metal article, consisting essentially of a mixture of silica, zircon, and alumina fiber, and an amount of colloidal silica to form a paste-like consistency.
Claim 13
Dependent Claim
38 words
A mixture sinterable to form a mask used during the weld repair of a metal article, consisting essentially of a mixture of silica, zircon, and alumina fiber, and an amount of colloidal silica to form a paste-like consistency.
Claim 14
Dependent Claim
14 words
The mixture of claim 8, containing about 10-50% zircon, 1-20 percent alumina, balance silica.
References Cited (Backward Citations)
US2641439A
Cited
US2679669A
Cited
US3014269A
Cited
US2972806A
Cited
US3014270A
Cited
US3196043A
Cited
US3576065A
Cited
US3629116A
Cited
US3994740A
Cited
US4028787A
Cited
US4141127A
Cited
US4050133A
Cited
US4128929A
Cited
US4176433A
Cited
US4379111A
Cited
US4611744A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-22 | 1991-08-24 | 1992-02-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-22 | 1995-08-24 | 1996-02-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-22 | 1999-08-24 | 2000-02-23 | $7700.00 | Window Closed / Lapsed |