Flowing (free-flowing) granular compositions based on fluorinated elastomers

Claim 2

A free-flowing granular composition based on fluoroelastomers containing dispersed on their surface an anti-caking agent, characterized in that said anti-caking agent is a polyolefin in a powdery form, in quantities between 5% and 70% by weight.

Claim 3

A granular composition according to claim 1, characterized in that the fluoroelastomer has a fluorine content greater than 65% by weight.

Claim 4

Granular compositions according to either claim 1 or claim 2, characterized in that the fluoroelastomer is selected from the class consisting of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene terpolymers; vinylidene fluoride, tetrafluoroethylene and perfluoromethyl-vinyl-ether terpolymers; tetrafluoroethylene and propylene copolymers; vinylidene fluoride and chloro-trifluoroethylene copolymers; vinylidene fluoride hydropentafluoropropylene copolymers; and vinylidene fluoride, hydropentafluoropropylene and tetrafluorethylene terpolymers, and the corresponding products containing in the chain small quantities of bromine.

Claim 5

A granular composition according to claim 1, characterized in that the polyolefin is selected from the class consisting of low, medium and high-density polyethylene; prevailingly isotactic macromolecules with polypropylene; propylene-ethylene copolymers with a predominant content in propylene, both "random" and "block"; and mixtures thereof.

Claim 6

A granular composition according to claim 4, characterized in that the polyolefin is a low-density polyethylene.

Claim 7

A granular composition according to claim 4, characterized in that the polyolefin is polypropylene.

Claim 8

A granular composition according to claim 1 or claim 2, characterized in that besides the polyolefin, there is present a per se known anti-caking agent selected from barium sulphate, calcium stearate, and talc.

Claim 9

A process for preparing a free-flowing granular fluoroelastomer comprising admixing said fluoroelastomer with from 5 to 70% by weight of a polyolefin in the form of a powder, thereby providing a coating of polyolefin powder on the surface of the fluoroelastomer granules.

Claim 10

A process for preparing a free-flowing granular fluoroelastomer comprising admixing said fluoroelastomer with from 5 to 70% by weight of a polyolefin in the form of a powder, thereby providing a coating of polyolefin powder on the surface of the fluoroelastomer granules.

Claim 11

A process according to claim 8, wherein the fluoroelastomer is admixed with from 10 to 30% by weight of the polyolefin.

Claim 12

A process according to claim 8 or 9 characterized in that the fluoroelastomer has a fluorine content greater than 65% by weight.

Claim 13

A process according to claim 8 or 9, characterized in that the fluoroelastomer is selected from the class consisting of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene terpolymers; vinylidene fluoride, tetrafluoroethylene and perfluoromethyl-vinyl-ether terpolymers; tetrafluoroethylene and propylene copolymers; vinylidene fluoride and chloro-trifluoroethylene copolymers; vinylidene fluoride and hydropentafluoropropylene copolymers; and vinylidene fluoride, hydropentafluoropropylene and tetrafluoroethylene terpolymers, and the corresponding products containing in the chain small quantities of bromine.

Claim 14

A process according to claim 8 or 9, characterized in that the polyolefin is selected from the class consisting of low, medium and high-density polyethylene; polypropylene having prevailingly isotactic macromolecules; propylene-ethylene copolymers with a predominant content of propylene, either with a random or a block distribution; and mixtures thereof.

Claim 15

A process according to claim 12, characterized in that the polyolefin is a low-density polyethylene.

Claim 16

A process according to claim 12, characterized in that the polyolefin is polypropylene having prevailingly isotactic macromolecules.