Decorative black wear protection coating
Assignee: OC Oerlikon Balzers AG
•
Filing: 1987-01-13
•
Granted: 1988-07-19
•
Expires: 2007-01-13
Abstract
Abstract Conventional black coatings for objects of common use usually formed as a carbon layer or porous metal layers, have a deficient wear resistance and surface quality. The resistant high gloss black coatings according to the invention comprise oxycarbonitrides, the proportion of carbon. Preferably the layer comprises an oxycarbonitride of an alloy of Ti, Zr and Hf, the oxygen component between 40 and 60 atom percent. Use of the invention is mainly for decorative utility objects, e.g. watch cases.
Inventors
- 👤 Erich Bergmann
- 👤 Peter Nuesch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:46
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/0015; C23C14/06; C23C30/00; C23C30/005; G; G04; G04B; G04B37/00; G04B37/22
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
40 words
Decorative black wear protection coating, comprising of oxycarbonitrides of metals of Group 4 of the Periodic Table of chemical elements having an Oxygen component measured in atom percent which outweighs the proportion of nitrogen and of carbon in the coating.
Claim 2
Dependent Claim
40 words
Decorative black wear protection coating, comprising of oxycarbonitrides of metals of Group 4 of the Periodic Table of chemical elements having an Oxygen component measured in atom percent which outweighs the proportion of nitrogen and of carbon in the coating.
Claim 3
Dependent Claim
40 words
A decorative black wear protection coating, comprising an oxycarbonitride of a titanium metal having an oxygen component which is measured in atom percent of from 40-60 percent of the entire coating and of from 95-150 percent in respect to titanium.
Claim 4
Dependent Claim
40 words
A decorative black wear protection coating, comprising an oxycarbonitride of a titanium metal having an oxygen component which is measured in atom percent of from 40-60 percent of the entire coating and of from 95-150 percent in respect to titanium.
Claim 5
Dependent Claim
27 words
A wear protection coating according to claim 1, wherein said metal of said Periodic Table comprises an alloy of at least one of titanium, zirconium and hafnium.
Claim 6
Dependent Claim
13 words
A wear protection coating according to claim 1, wherein said metal is titanium.
Claim 7
Dependent Claim
25 words
A wear protection coating according to claim 1, wherein said oxygen content measured in atom percent is from 0.95 to 1.5 times the metal content.
Claim 8
Dependent Claim
31 words
A wear protection coating according to claim 1, wherein the ratio of the number of nitrogen atoms to the number of oxygen in said coating is from between 0.1 and 0.4.
Claim 9
Dependent Claim
30 words
A wear protection coating according to claim 1, wherein a ratio of the number of carbon atoms to the number of nitrogen atoms in said coating is 0.6 to 2.
Claim 10
Dependent Claim
169 words
A product made from a process in which a vaporization crucible is filled with hafnium pellets and a watchband is first ion etched in a low voltage arc in an argon gas at a pressure of 0.08 Pa, actuating an electron beam vaporizer so as to melt the hafnium and during melting maintaining a low volt arc discharge used for the ion etching and after the metal melt reaches a stable rate of vaporization out of the crucible of approximately 50 g/min admitting oxygen and carbon monoxide into the chamber in a ratio of a partial pressure of 8:1:1, adjusting the gas flow to a 190 standard cubic centimeters per minute and a total pressure in the vapor deposition chamber about 0.12 Pascal by continuous pumping and wherein, after one hour the electron beam vaporizer and then the low-volt arc are turned off and the gas admission is interrupted causing the articles to pick up a pitch black coating which shows a very good resistance to corrosion and wear.
Claim 11
Dependent Claim
169 words
A product made from a process in which a vaporization crucible is filled with hafnium pellets and a watchband is first ion etched in a low voltage arc in an argon gas at a pressure of 0.08 Pa, actuating an electron beam vaporizer so as to melt the hafnium and during melting maintaining a low volt arc discharge used for the ion etching and after the metal melt reaches a stable rate of vaporization out of the crucible of approximately 50 g/min admitting oxygen and carbon monoxide into the chamber in a ratio of a partial pressure of 8:1:1, adjusting the gas flow to a 190 standard cubic centimeters per minute and a total pressure in the vapor deposition chamber about 0.12 Pascal by continuous pumping and wherein, after one hour the electron beam vaporizer and then the low-volt arc are turned off and the gas admission is interrupted causing the articles to pick up a pitch black coating which shows a very good resistance to corrosion and wear.
References Cited (Backward Citations)
US3492100A
Cited
US3872136A
Cited
US4212670A
Cited
US4357382A
Cited
US4476102A
Cited
US4643952A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-19 | 1992-01-18 | 1992-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-19 | 1996-01-18 | 1996-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-19 | 2000-01-18 | 2000-07-19 | $7700.00 | Window Closed / Lapsed |