Curable composition of elastomeric vinylidene fluoride copolymer
Assignee: AGC Inc
•
Filing: 1986-09-03
•
Granted: 1988-07-19
•
Expires: 2006-09-03
Abstract
Abstract A curable composition comprising an elastomeric vinylidene fluoride copolymer, a polyhydroxy compound and a vulcanization accelerator, characterized in that said copolymer contains from 2 to 50 mol % of vinylidene fluoride units and unsaturated bonds introduced by reacting an untreated elastomeric vinylidene fluoride copolymer dispersed in an aqueous medium, with an aqueous alkaline solution containing an onium compound.
Inventors
- 👤 Yasumichi Ito
- 👤 Hiroshi Wachi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:24
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/13; C08F; C08F8/00; C08F8/26
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
107 words
A curable composition comprising an elastomeric vinylidene fluoride copolymer, a polyhydroxy compound selected from the group consisting of polyhydroxy aromatic compounds and fluorine-containing fatty acids diols and a vulcanization accelerator selected from the group consisting of quaternary ammonium compounds, quaternary immonium compounds and quaternary phosphonium compounds, said copolymer containing from 2 to 50 mol % of vinylidene fluoride units and containing unsaturated bonds in an amount ranging from 0.1 to 15, per 100 monomer units in the copolymer, said unsaturated bonds introduced into said copolymer by reacting an untreated elastomeric vinylidene fluoride copolymer dispersed in an aqueous solution with an aqueous alkaline solution containing an onium compound.
Claim 2
Dependent Claim
107 words
A curable composition comprising an elastomeric vinylidene fluoride copolymer, a polyhydroxy compound selected from the group consisting of polyhydroxy aromatic compounds and fluorine-containing fatty acids diols and a vulcanization accelerator selected from the group consisting of quaternary ammonium compounds, quaternary immonium compounds and quaternary phosphonium compounds, said copolymer containing from 2 to 50 mol % of vinylidene fluoride units and containing unsaturated bonds in an amount ranging from 0.1 to 15, per 100 monomer units in the copolymer, said unsaturated bonds introduced into said copolymer by reacting an untreated elastomeric vinylidene fluoride copolymer dispersed in an aqueous solution with an aqueous alkaline solution containing an onium compound.
Claim 3
Dependent Claim
24 words
The composition according to claim 1, wherein the average particle size of the copolymer dispersed in the aqueous medium is at most 10 mm.
Claim 4
Dependent Claim
28 words
The composition according to claim 1, wherein the amount of the onium compound is at most 30 parts by weight per 100 parts by weight of the copolymer.
Claim 5
Dependent Claim
28 words
The composition according to claim 1, wherein the onium compound is at least one member selected from the group consisting of quaternary ammonium salts and quaternary phosphonium salts.
Claim 6
Dependent Claim
21 words
The composition according to claim 1, wherein the reaction temperature of the aqueous alkaline solution is from 50° to 100° C.
Claim 7
Dependent Claim
30 words
The composition of claim 1, wherein said onium compound is tetrabutylammonium bromide, tetrabutylammonium chloride, benzyltributylammonium chloride, benzyltriethylammonium bromide, tetrabutylammonium hydrogen sulfate, tetrabutylammonium hydroxide, benzyltriethylammonium chloride, tetrabutylphosphonium bromide or tetrapropylphosphonium bromide.
Claim 8
Dependent Claim
36 words
The composition according to claim 1, wherein said vinylidene fluoride copolymer is a member selected from the group consisting of vinylidene fluoride-tetrafluoroethylene-propylene terpolymer, vinylidene fluoride-tetrafluoroethylene-ethylene-isobutylene copolymer, vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene terpolymer, vinylidene fluoride-tetrafluoroethylene-perfluoro (alkylvinylether), and vinylidene fluoride-tetrafluoroethylene-perfluor(alkoxyalkylvinylether) terpolymer.
Claim 9
Dependent Claim
20 words
The composition according to claim 1, wherein said copolymer contains from 10 to 40 mol % of vinylidene fluoride units.
Claim 10
Dependent Claim
26 words
The composition according to claim 1, wherein the amount of said unsaturated bonds ranges from 0.5 to 10 per 100 units of monomer in said copolymer.
Claim 11
Dependent Claim
31 words
The composition according to claim 1, wherein the amount of said vulcanization accelerator ranges from 0.2 to 10 parts by weight per 100 parts by weight of said vinylidene fluoride copolymer.
Claim 12
Dependent Claim
34 words
The composition according to claim 1, wherein said vulcanization accelerator is a member selected from the group consisting of methyltrioctylammonium chloride, benzyltriethylammonium chloride, tetrahexylammonium tetrafluoroborate, 8-methyl-1,8-diazacyclo(5,4,0)-7-undecenium chloride, benzyltriphenylphosphonium chloride, m-trifluoromethylbenzyltrioctylphosphonium chloride and benzyltrioctylphosphonium bromide.
Claim 13
Dependent Claim
31 words
The composition according to claim 1, wherein the amount of said polyhydroxy compound ranges from 0.1 to 20 parts by weight per 100 parts by weight of said vinylidene fluoride copolymer.
Claim 14
Dependent Claim
32 words
The composition according to claim 1, which further comprises at least one additive selected from the group consisting of metal oxides, metal hydroxides, a filler, a pigment, an antioxidant and a stabilizer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-19 | 1992-01-18 | 1992-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-19 | 1996-01-18 | 1996-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-19 | 2000-01-18 | 2000-07-19 | $7700.00 | Window Closed / Lapsed |