Method for making planar lightwave guides
Assignee: Schott AG
•
Filing: 1986-10-16
•
Granted: 1988-08-23
•
Expires: 2006-10-16
Abstract
Abstract A planar lightwave guide with light-conducting core zones in light conducting strips is made by the precipitation out of a gaseous phase onto a substrate a thin, glass-like strata in accordance with a programmed schedule so as to allow a predetermined refractive index curve to be obtained to thereby form a light-conducting core zone and protective sheathing layers adjacent to the core zone. The improvement in the method is characterized in that the precipitation out of the gaseous phase is obtained by application of a heterogeneous reaction and in that after the formation of the light-conducting strips, the refractive index of the core-forming strata is modified in a targeted manner in a lateral marginal region of the strips by diffusing out the doping substance which determines the refractive index curve in the core zones. Subsequently these strips and the substrate are coated with a covering layer of a material having a lower refractive index than that of the core zone material.
Inventors
- 👤 Ralf T. Kersten
- 👤 Wolfgang Siefert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:42
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/10; G02B6/12; G02B6/13; G02B6/132
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
241 words
A method of making a planar lightwave-guide with light-conducting core zones, the method comprising the steps of: depositing an initial sheathing layer of glassy material on a substrate by precipitating the glass material directly out of a cold plasma onto the substrate in thin glassy strata using a heterogeneous reaction; depositing a light-conducting core zone over the first sheathing layer by precipitating glassy material out of a cold plasma containing a doping material onto the first sheathing layer in thin glassy strata using a heterogenous reaction to form doped, core strata for conducting light wave energy; depositing a subsequent sheathing layer of glassy material over the core zone by precipitating the glassy material out of a cold plasma onto the core zone in thin glassy strata using a heterogeneous reaction; thereby fabricating a lamination of a light conducting core zone sandwiched between a pair of sheathing layers; delineating opposed marginal surfaces in the core zone and sheathing layers, the opposed marginal surface extending transverse with respect to the layers to define light conducting strips each having a core zone sandwiched between a pair of sheathing layers; diffusing doping material out of the core zones of the strips in portions of the core zones adjacent to the delineated marginal surfaces to modify the refractive index curve of the core zones, and covering the strips and substrate with a layer of material having a lower refractive index than that of the core zone.
Claim 2
Independent Claim
241 words
A method of making a planar lightwave-guide with light-conducting core zones, the method comprising the steps of: depositing an initial sheathing layer of glassy material on a substrate by precipitating the glass material directly out of a cold plasma onto the substrate in thin glassy strata using a heterogeneous reaction; depositing a light-conducting core zone over the first sheathing layer by precipitating glassy material out of a cold plasma containing a doping material onto the first sheathing layer in thin glassy strata using a heterogenous reaction to form doped, core strata for conducting light wave energy; depositing a subsequent sheathing layer of glassy material over the core zone by precipitating the glassy material out of a cold plasma onto the core zone in thin glassy strata using a heterogeneous reaction; thereby fabricating a lamination of a light conducting core zone sandwiched between a pair of sheathing layers; delineating opposed marginal surfaces in the core zone and sheathing layers, the opposed marginal surface extending transverse with respect to the layers to define light conducting strips each having a core zone sandwiched between a pair of sheathing layers; diffusing doping material out of the core zones of the strips in portions of the core zones adjacent to the delineated marginal surfaces to modify the refractive index curve of the core zones, and covering the strips and substrate with a layer of material having a lower refractive index than that of the core zone.
Claim 3
Dependent Claim
24 words
The method according to claim 1, wherein the precipitation of the glassy strata is carried out by means of a non-isothermic plasma CVD process.
Claim 4
Dependent Claim
19 words
The method according to claim 1 wherein the light-conducting core zone is formed of SiO 2 doped with Germanium.
Claim 5
Dependent Claim
34 words
The method according to claim 1 wherein the refractive index profile, the numerical aperture and the dimensions of the core zone are selected so as to form a mono-mode wave guide with predetermined properties.
Claim 6
Dependent Claim
33 words
The method according to claim 1 wherein the refractive index profile, the numerical aperture and the dimensions of the core zone are selected so as to form a multi-mode, wave-guide with predetermined properties.
Claim 7
Dependent Claim
29 words
The method according to claim 1 wherein the refractive index profile, the numerical aperture and the dimensions of the core zone are selected to form a polarizing lightwave guide.
Claim 8
Dependent Claim
36 words
The method according to claim 1 wherein the thickness of the initial sheathing layer between the substrate and the core zone is selected to completely isolate the substrate from light wave energy in the core zone.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-23 | 1992-02-22 | 1992-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-23 | 1996-02-22 | 1996-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-23 | 2000-02-22 | 2000-08-23 | $7700.00 | Window Closed / Lapsed |