Process for producing transparent glass product having refractive index gradient
Assignee: Hoya Corp
•
Filing: 1986-12-02
•
Granted: 1988-08-30
•
Expires: 2006-12-02
Abstract
Abstract A process for producing a transparent glass product having a refractive index gradient by the molecular stuffing method is described. A thallium compound is used as a dopant and, after a concentration gradient of the thallium dopant is formed, the porous glass product is heated up to the temperature region of 350° to 550° C. at a temperature-rising rate of 25° to 150° C./hour in a reducing gas atmosphere and then heat treated above 550° C. in an inert gas atmosphere to collapse micropores in the porous glass product, thereby obtaining a glass product having a refractive index gradient which is transparent and free of light-scattering and coloration. The glass product is suitable as materials (preforms) for optical fibers or materials for rod-shaped lenses, particularly rod-shaped microlenses for microlens arrays and microlenses for coupling an optical fiber and a light source.
Inventors
- 👤 Shigeaki Omi
- 👤 Yoshiyuki Asahara
- 👤 Seiichi Shingaki
- 👤 Shin Nakayama
- 👤 Kenji Nakagawa
- 👤 Tetsuro Izumitani
- 👤 Hiroyuki Sakai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:39
CPC Classifications
C; C03; C03C; C03C23/00; C03C23/0095; Y; Y10; Y10S; Y10S65/00; Y10S65/90
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
158 words
A process for producing a transparent glass product free from bluish white turbidity having a refractive index gradient comprising the steps of: (a) permeating a solution of thallium nitrate or thallium nitrite into the micropores of a porous glass product; (b) leaching out a part of the thallium nitrate or thallium nitrite in the micropores to form a concentration gradient thereof in the porous glass product; (c) precipitating the thallium nitrate or thallium nitrite remaining in the mircopores; (d) drying the porous glass product; (e) heating the dried porous glass product to the temperature region of 350° to 550° C. at a temperature-rising rate of 25° to 150° C./hour in a reducing gas atmosphere whereby the thallium is present as monovalent thallium; and (f) heat treating the porous glass product above 550° C. in an inert gas atmosphere to collapse the micropores thereby producing a transparent glass product free from bluish white turbidity having a refractive index gradient.
Claim 2
Dependent Claim
158 words
A process for producing a transparent glass product free from bluish white turbidity having a refractive index gradient comprising the steps of: (a) permeating a solution of thallium nitrate or thallium nitrite into the micropores of a porous glass product; (b) leaching out a part of the thallium nitrate or thallium nitrite in the micropores to form a concentration gradient thereof in the porous glass product; (c) precipitating the thallium nitrate or thallium nitrite remaining in the mircopores; (d) drying the porous glass product; (e) heating the dried porous glass product to the temperature region of 350° to 550° C. at a temperature-rising rate of 25° to 150° C./hour in a reducing gas atmosphere whereby the thallium is present as monovalent thallium; and (f) heat treating the porous glass product above 550° C. in an inert gas atmosphere to collapse the micropores thereby producing a transparent glass product free from bluish white turbidity having a refractive index gradient.
Claim 3
Dependent Claim
17 words
Process according to claim 1, wherein said reducing gas atmosphere consists essentially of hydrogen or carbon monoxide.
Claim 4
Dependent Claim
22 words
The process as claimed in claim 1, wherein the dried glass is heated in step (e) up to 400° to 500° C.
Claim 5
Dependent Claim
45 words
The process as claimed in claim 1, wherein prior to the heat treatment in the inert gas atmosphere in step (f), the porous glass product is maintained at the temperature used in step (e) for 2 to 24 hours in the same reducing gas atmosphere.
Claim 6
Dependent Claim
23 words
The process according to claim 1, wherein in said step (e) of said process the temperature rising rate is at least 50° C./hour.
References Cited (Backward Citations)
US4110093A
Cited
US4110096A
Cited
US4225330A
Cited
US4224177A
Cited
US4302231A
Cited
US4528010A
Cited
US4389233A
Cited
US4525189A
Cited
US4563205A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-30 | 1992-02-29 | 1992-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-30 | 1996-02-29 | 1996-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-30 | 2000-02-29 | 2000-08-30 | $7700.00 | Window Closed / Lapsed |