Patent US4769070A successfully refreshed from Google Patents.
US4769070A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High toughness cermet and a process for the production of the same
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1987-09-01
•
Granted: 1988-09-06
•
Expires: 2007-09-01
Abstract
Abstract High hardness and high toughness nitrogen-containing sintered hard alloys or cermets useful for cutting tools, in particular, high speed cutting are provided which comprises a hard dispersed phase consisting essentially of a mixed carbonitride of titanium and at least one element selected from the group consisting of Group IVa, Va, and VIa elements of Periodic Table, except titanium, and a binder metal phase consisting essentially of at least one metal selected from the group consisting of nickel and cobalt, and unavoidable impurities, the hard dispersed phase having previously been subjected to a solid solution forming treatment at a temperature of at least the sintering temperature before sintering.
Inventors
- 👤 Masaaki Tobioka
- 👤 Yasuhiro Shimizu
- 👤 Kazutaka Isobe
- 👤 Nobuyuki Kitagawa
- 👤 Toshio Nomura
- 👤 Kunihiro Takahashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:10
CPC Classifications
C; C22; C22C; C22C29/00; C22C29/02; C22C29/04; B; B22; B22F; B22F1/00; B22F1/09; B22F1/14; B22F1/142; B22F1/148; B22F3/00; B22F3/10; C22C1/00; C22C1/04; C22C1/05; C22C1/051
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
129 words
A high toughness cermet comprising a hard phase consisting essentially of a mixed carbide represented by the general formula (Ti x M y W z ) (C A N b )m in which, in terms of atomic ratios, x+y+z=1, A+B=1, 0.5≦x≦0.95, 0.01≦y≦0.4, 0.01≦z≦0.4, 0.1≦A≦0.9, 0.1≦B≦0.9, 0.85≦m≦1.05 and M is at least one element selected from the group consisting of Ta and Nb and a binder phase consisting essentially of at least one metal selected from the group consisting of Ni and Co, and unavoidable impurities, the atomic ratio of nitrogen and carbon contained in the cermet, N/(C+N) is in the range of 0.3 to 0.6, said hard phase having previously been subjected to a solid solution forming treatment at a temperature of at least the sintering temperature before sintering.
Claim 2
Dependent Claim
129 words
A high toughness cermet comprising a hard phase consisting essentially of a mixed carbide represented by the general formula (Ti x M y W z ) (C A N b )m in which, in terms of atomic ratios, x+y+z=1, A+B=1, 0.5≦x≦0.95, 0.01≦y≦0.4, 0.01≦z≦0.4, 0.1≦A≦0.9, 0.1≦B≦0.9, 0.85≦m≦1.05 and M is at least one element selected from the group consisting of Ta and Nb and a binder phase consisting essentially of at least one metal selected from the group consisting of Ni and Co, and unavoidable impurities, the atomic ratio of nitrogen and carbon contained in the cermet, N/(C+N) is in the range of 0.3 to 0.6, said hard phase having previously been subjected to a solid solution forming treatment at a temperature of at least the sintering temperature before sintering.
Claim 3
Dependent Claim
21 words
The high toughness cermet as claimed in claim 1, wherein a substantial quantity of Mo is not contained in the cermet.
Claim 4
Dependent Claim
25 words
The high toughness cermet as claimed in claim 1, wherein Mo is contained in a proportion of 0 to 1% by weight in the cermet.
Claim 5
Dependent Claim
29 words
The high toughness cermet as claimed in claim 1, wherein at least one element selected from the group consisting of Ti and W is dissolved in the binder phase.
Claim 6
Dependent Claim
31 words
The high toughness cermet as claimed in claim 2, wherein the atomic ratio of nitrogen and carbon contained in the hard phase, N/(C+N) is in the range of 0.3 to 0.6.
Claim 7
Dependent Claim
28 words
The high toughness cermet as claimed in claim 1, wherein the binder phase consists of Ni and Co in a Ni/(Ni+Co) ratio by weight of 0.3 to 0.8.
Claim 8
Dependent Claim
24 words
The high toughness cermet as claimed in claim 1, wherein the mixed carbonitride of the hard phase contains Ti and W as essential components.
Claim 9
Dependent Claim
50 words
The high toughness cermet as claimed in claim 7, wherein the atomic ratio of nitrogen and carbon contained in the hard phase, N/(N+C) is in the range of 0.3 to 0.6 and the binder phase consists of Ni and Co in a Ni/(Ni+Co) ratio by weight of 0.3 to 0.8.
Claim 10
Dependent Claim
32 words
The high toughness cermet as claimed in claim 6, wherein the relationship of C≧0.73×(20.2×A+6.8×B) wherein A=weight % of Co, B=weight % of Ni and C=saturated magnetism (gauss cm 3 /g) is satisfied.
Claim 11
Dependent Claim
18 words
The high toughness cermet as claimed in claim 1, wherein A and B satisfy the relationship of 0.3≦B/(A+B)≦0.6.
Claim 12
Dependent Claim
41 words
The high toughness cermet as claimed in claim 1, wherein the hard phase is bonded with 3 to 40% by weight of a binder phase consisting essentially of at least one element selected from the group consisting of Ni and Co.
Claim 13
Dependent Claim
136 words
A process for the production of the high toughness cermet as claimed in claim 1, which comprises mixing at least one member selected from the group consisting of nitrides, carbides, carbonitrides of Ti and mixtures thereof with at least one member selected from the group consisting of nitrides, carbides, carbonitrides of at least one transition metal selected from the group consisting of Group IVa, Va and VIa metals of Periodic Table except Ti and mixtures, thereof, heating previously the mixed powders in a nitrogen atmosphere at a temperature of at least the sintering temperature to form a solid solution, then pulverizing the solid solution to obtain a carbonitride powder, mixing the carbonitride powder with at least one metal selected from the group consisting of Ni and Co and then sintering the mixture in a nitrogen atmosphere.
Claim 14
Dependent Claim
32 words
The process as claimed in claim 12, wherein the mixing and heating are carried out in such a manner that the solid solution has an N/(C+N) atomic ratio of 0.3 to 0.6.
Claim 15
Dependent Claim
21 words
The process as claimed in claim 12, wherein the mixed powders further contain 0.01 to 2% by weight of carbon powder.
Claim 16
Dependent Claim
26 words
The process as claimed in claim 12, wherein the carbonitride powder is mixed with Ni and Co in a Ni/(Ni+Co) weight ratio of 0.3 to 0.8.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-06 | 1992-03-07 | 1992-09-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-06 | 1996-03-07 | 1996-09-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-06 | 2000-03-07 | 2000-09-06 | $7700.00 | Window Closed / Lapsed |