Optical waveguides and methods for making same
Assignee: Verizon Laboratories Inc
•
Filing: 1986-04-16
•
Granted: 1988-11-08
•
Expires: 2006-04-16
Abstract
Abstract An optical waveguide made from a unitary organic film has a polydiacetylene core region and a diacetylene monomer cladding substrate region. The index of refraction of the polydiacetylene core region is greater than the index of refraction of the diacetylene monomer cladding substrate region. The method of fabricating the optical waveguide comprises depositing a diacetylene monomer film on a substrate. The diacetylene monomer film is polymerized by ion beam bombardment to a depth less than the thickness of the film. The depth of the polymerization is controlled by the ion mass and energy of the ion beam applied.
Inventors
- 👤 Boris S. Elman
- 👤 Mrinal K. Thakur
- 👤 Robert J. Seymour
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:03
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/10; G02B6/12; G02B6/13; G02B6/138
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
66 words
An optical waveguide comprising a unitary organic film having a first surface, an second surface, a thickness measured between said surfaces, a first region and a second region; said first region being a polydiacetylene film and said second region being a diacetylene monomer film; and said first region being contiguous with said second region and with said second region making up the totality of said thickness.
Claim 2
Dependent Claim
66 words
An optical waveguide comprising a unitary organic film having a first surface, an second surface, a thickness measured between said surfaces, a first region and a second region; said first region being a polydiacetylene film and said second region being a diacetylene monomer film; and said first region being contiguous with said second region and with said second region making up the totality of said thickness.
Claim 3
Dependent Claim
17 words
An optical waveguide in accordance with claim 1 wherein said diacetylene monomer film comprises bisphenylurethane of 5,7-dodecadiyne-1,12-diol.
Claim 4
Dependent Claim
32 words
An optical waveguide in accordance with claim 1 wherein said first region having an index of refraction of about 2.2 and said second region having an index of refraction of about 1.65.
Claim 5
Independent Claim
95 words
A method for making an optical waveguide comprising the following steps: Step 1--depositing a diacetylene monomer film on a substrate, said film having a thickness and a surface; and Step 2--polymerizing the diacetylene monomer film by ion beam bombarding the surface of said film with ions to a predetermined controlled depth less than the thickness of said film, said ion beam being characterized by an ion mass and an accelerating voltage (energy) said predetermined depth of said polymerization being controlled by said ion mass and said accelerating voltage (energy) of said ion beam being applied.
Claim 6
Independent Claim
95 words
A method for making an optical waveguide comprising the following steps: Step 1--depositing a diacetylene monomer film on a substrate, said film having a thickness and a surface; and Step 2--polymerizing the diacetylene monomer film by ion beam bombarding the surface of said film with ions to a predetermined controlled depth less than the thickness of said film, said ion beam being characterized by an ion mass and an accelerating voltage (energy) said predetermined depth of said polymerization being controlled by said ion mass and said accelerating voltage (energy) of said ion beam being applied.
Claim 7
Dependent Claim
33 words
A method for making an optical waveguide in accordance with claim 4 wherein said depositing being sufficient to obtain a diacetylene monomer film having a thickness of about 1 to about 10 microns.
Claim 8
Dependent Claim
42 words
A method of making an optical waveguide in accordance with claim 4 wherein said ion beam comprises an arsenic ion beam having an energy from about 30 keV to about 150 keV at a fluence of about 1×10 12 cm -2 .
Claim 9
Dependent Claim
38 words
A method of making an optical waveguide in accordance with claim 4 wherein said ion beam comprises a boron ion beam having an energy of about 30 keV at a fluence of about 1×10 12 cm -2 .
Claim 10
Dependent Claim
21 words
A method of making an optical waveguide in accordance with claim 4 wherein said ion beam comprises a phosphorus ion beam.
Claim 11
Dependent Claim
37 words
A method of making an optical waveguide in accordance with claim 8 wherein said phosphorus ion beam energy comprises from about 30 keV to about 180 keV at a fluence of about 1×10 12 cm -2 .
Claim 12
Dependent Claim
34 words
A method of making an optical waveguide in accordance with claim 4 wherein said depth of polymerization is controlled to form a grating pattern at the interface between the two regions of the film.
References Cited (Backward Citations)
US4220747A
Cited
US4431263A
Cited
US4615962A
Cited
US4536450A
Cited
US4515429A
Cited
US4465336A
Cited
US4497535A
Cited
US4531809A
Cited
US4691982A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-08 | 1992-05-09 | 1992-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-08 | 1996-05-09 | 1996-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-08 | 2000-05-09 | 2000-11-08 | $7700.00 | Window Closed / Lapsed |