Dielectric inks for multilayer copper circuits
Assignee: Lockheed Martin Corp
•
Filing: 1987-08-20
•
Granted: 1989-02-28
•
Expires: 2007-08-20
Abstract
Abstract An improved dielectric ink for the fabrication of multilayer, integrated circuits is disclosed. The subject inks comprise a devitrifying zinc-magnesium-barium-aluminum-zirconium-phosphosilicate glass frit, a devitrifying zinc-magnesium-barium-aluminum-silicate glass frit, or a devitrifying zinc-magnesium-strotium-aluminum-silicate glass frit, an organic vehicle and, optionally, a suitable ceramic filler material. The subject glass frit containing a suitable ceramic filler can be fabricated into stand-alone substrates useful in a wide variety of electronic applications. The glass frit of the subject inks has a high softening temperature which facilitates complete removal of carbonaceous residues of the vehicle from the dried ink during firing. This is advantageous in that it eliminates the need to incorporate oxygen-generating additives, such as barium nitrate, in the ink or treatment of the ink in an oxidizing or reducing plasma prior to firing. The disclosed inks are particularly advantageous in the fabrication of multilayer integrated circuits based on copper conductors.
Inventors
- 👤 Kenneth W. Hang
- 👤 Ashok N. Prabhu
- 👤 Wayne M. Anderson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:21
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/02; H01B3/08; H01B3/087; C; C03; C03C; C03C10/00; C03C10/0036; C03C10/0045; C03C3/00; C03C3/04; C03C3/062; H01B3/085; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
142 words
A dielectric ink for mulitlayer integrated circuit fabrication consisting essentially of: (a) from about 50 to about 75 percent by weight of a devitrifying glass frit consisting essentially of, on a weight basis: from about 15 to about 25 percent of zinc oxide; from about 10 to about 25 percent of magnesium oxide; from about 3 to about 12 percent of an oxide selected from the group consisting of barium oxide and strontium oxide; from about 5 to about 20 percent of aluminum oxide; from about 35 to about 50 percent of silicon dioxide; from 0.5 to about 3 percent of phosphorus pentoxide; and from 1 to about 5 percent of zirconium silicate; (b) up to about 30 percent by weight of a suitable ceramic filler; and (c) from about 15 to about 30 percent by weight of a suitable organic vehicle.
Claim 2
Dependent Claim
142 words
A dielectric ink for mulitlayer integrated circuit fabrication consisting essentially of: (a) from about 50 to about 75 percent by weight of a devitrifying glass frit consisting essentially of, on a weight basis: from about 15 to about 25 percent of zinc oxide; from about 10 to about 25 percent of magnesium oxide; from about 3 to about 12 percent of an oxide selected from the group consisting of barium oxide and strontium oxide; from about 5 to about 20 percent of aluminum oxide; from about 35 to about 50 percent of silicon dioxide; from 0.5 to about 3 percent of phosphorus pentoxide; and from 1 to about 5 percent of zirconium silicate; (b) up to about 30 percent by weight of a suitable ceramic filler; and (c) from about 15 to about 30 percent by weight of a suitable organic vehicle.
Claim 3
Dependent Claim
23 words
A dielectric ink in accordance with claim 1, wherein the organic vehicle comprises a solution of an organic binder in a suitable solvent.
Claim 4
Dependent Claim
71 words
A dielectric ink in accordance with claim 1 wherein the glass frit consists essentially of, on a frit weight basis: from about 17 to about 23.5 percent of zinc oxide; from about 17 to about 23.5 percent of magnesium oxide; from about 5 to about 10 percent of barium oxide; from about 8 to about 11 percent of aluminum oxide; and from about 39 to about 43 percent of silicon dioxide.
Claim 5
Dependent Claim
88 words
A dielectric ink in accordance with claim 1 wherein the glass frit consists essentially of, on a weight basis: from about 17 to about 23.5 percent of zinc oxide; from about 17 to about 23.5 percent of magnesium oxide; from about 3 to about 10 percent of strontium oxide; from about 7 to about 11 percent of aluminum oxide; from about 38 to about 43 percent of silicon dioxide; from 0.5 to about 2 percent of phosphorus pentoxide and from 1 to about 2 percent of zirconium silicate.
Claim 6
Dependent Claim
24 words
A dielectric ink in accordance with claim 1, wherein the ink contains from about 5 to about 15 percent by weight of the filler.
Claim 7
Dependent Claim
36 words
A dielectric ink in accordance with claim 5, wherein the filler is selected from the group consisting of alumina, barium dimagnesium disilicate, dimagnesium borate, zirconium silicate, dimagnesia silicate, dimagnesia dialumina pentasilicate, magnesium aluminate and mixtures thereof.
Claim 8
Dependent Claim
21 words
A dielectric ink in accordance with claim 6, wherein the filler material is a mixture of alumina and barium dimagnesium disilicate.
Claim 9
Dependent Claim
23 words
A dielectric ink in accordance with claim 2, wherein the organic binder is selected from the group consisting of poly(isobutylmethacrylate) and ethyl cellulose.
Claim 10
Dependent Claim
132 words
A dielectric ink for multilayer integrated circuit fabrication consisting essentially of: (a) from about 50 to about 75 percent by weight of a glass frit consisting essentially of, on a weight basis: from about 15 to about 25 percent of zinc oxide; from about 10 to about 25 percent of magnesium oxide; from about 3 to about 12 percent of barium oxide; from about 5 to about 20 percent of aluminum oxide; from about 35 to about 50 percent of silicon dioxide; from about 0.5 to about 3 percent of phosphorus pentoxide; and from about 1 to about 5 percent of zirconium silicate; (b) up to about 30 percent by weight of a suitable ceramic filler; and (c) from about 15 to about 30 percent by weight of a suitable organic vehicle.
Claim 11
Dependent Claim
132 words
A dielectric ink for multilayer integrated circuit fabrication consisting essentially of: (a) from about 50 to about 75 percent by weight of a glass frit consisting essentially of, on a weight basis: from about 15 to about 25 percent of zinc oxide; from about 10 to about 25 percent of magnesium oxide; from about 3 to about 12 percent of barium oxide; from about 5 to about 20 percent of aluminum oxide; from about 35 to about 50 percent of silicon dioxide; from about 0.5 to about 3 percent of phosphorus pentoxide; and from about 1 to about 5 percent of zirconium silicate; (b) up to about 30 percent by weight of a suitable ceramic filler; and (c) from about 15 to about 30 percent by weight of a suitable organic vehicle.
Claim 12
Dependent Claim
90 words
A dielectric ink in accordance with claim 9, wherein the glass frit consists essentially of, on a weight basis: from about 16 to about 22 percent of zinc oxide; from about 16 to about 2 percent of magnesium oxide; from about 5 to about 10 percent of barium oxide; from about 8 to about 11 percent of aluminum oxide; from about 39 to about 43 percent of silicon dioxide; from about 1 to about 2 percent of phosphorus pentoxide; and from about 2 to about 3 percent of zirconium silicate.
Claim 13
Dependent Claim
24 words
A dielectric ink in accordance with claim 9, wherein the ink contains from about 5 to about 15 percent by weight of the filler.
Claim 14
Dependent Claim
36 words
A dielectric ink in accordance with claim 11, wherein the filler is selected from the group consisting of alumina, barium dimagnesium disilicate, dimagnesium borate, zirconium silicate, dimagnesia silicate, dimagnesia dialumina pentasilicte, mangesium aluminate and mixtures thereof.
Claim 15
Dependent Claim
21 words
A dielectric ink in accordance with claim 12, wherein the filler material is a mixture of alumina and barium dimagnesium disilicate.
Claim 16
Dependent Claim
23 words
A dielectric ink in accordance with claim 9, wherein the organic vehicle comprises a solution of an organic binder in a suitable solvent.
Claim 17
Dependent Claim
14 words
A dielectric ink in accordance with claim 14, wherein the organic binder is poly(isobutylmethacrylate).
References Cited (Backward Citations)
US3022179A
Cited
US3501322A
Cited
US3876407A
Cited
US4061584A
Cited
US4049872A
Cited
US4256796A
Cited
US4355115A
Cited
US4355114A
Cited
US4401709A
Cited
US4369220A
Cited
US4369254A
Cited
US4376725A
Cited
US4377642A
Cited
US4399320A
Cited
US4400214A
Cited
US4415624A
Cited
US4385127A
Cited
EP0084936A1
Cited
JPS59174544A
Cited
US4536535A
Cited
US4521329A
Cited
US4514321A
Cited
US4540604A
Cited
US4623482A
Cited
US4619836A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |