Method for the collective chemical cutting out of semiconductor devices, and a device cut out by this method
Assignee: Thomson Hybrides et Microondes
•
Filing: 1987-12-29
•
Granted: 1989-03-07
•
Expires: 2007-12-29
Abstract
Abstract The invention provides a method for cutting out very small sized semiconductor devices, mounted on a gold base, including the formation of depth indicators etched through the active layer, on a manufacturing wafer, and penetrating into the substrate, said indicators being metallized then, after masking, the gold bases are deposited. A mechanical metal support makes it possible to thin down the substrate and to etch the mesa diodes on their gold bases, the metal of the mechanical support then being etched by an acid solution which cuts out the diodes.
Inventors
- 👤 Nathalie M. Turina
- 👤 George Lleti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:12
CPC Classifications
H; H10; H10P; H10P54/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
242 words
A method for the collective chemical cutting out of semiconductor devices, fixed to a gold base of very small size (200 microns) including a preliminary step for forming at least one semiconductor layer on a semiconductor material substrate, forming a diode junction, said method further including the following steps: (1) etching depth indicators in the semiconductor layer, all the indicators having the same depth and penetrating into the substrate, at the rate of at least one indicator between two future diodes, (2) depositing, on the semiconductor layer and in the holes of the indicators, a metal layer for fixing to the semiconductor material, (3) masking on the fixing layer and etching of the mask for freeing the windows corresponding to the future gold bases, (4) electrolytic deposition of the gold bases in the windows of the mask, (5) dissolution of the mask and deposition of a metal diffusion arresting layer, on the gold bases and the visible parts of the fixing layer, (6) growth on the antidiffusion layer of a thick layer of a mechanical support metal etchable by a chemical solution which does not attack gold, (7) thinning of the semiconductor substrate until the depth indicators appear, (8) masking the semiconductor substrate, etching the mask and depositing contact making metallizations on the diodes, (9) etching of the mesas of the diodes, (10) collective chemical cutting out into discrete elements by chemically etching the mechanical support metal layer and the fixing layer.
Claim 2
Independent Claim
242 words
A method for the collective chemical cutting out of semiconductor devices, fixed to a gold base of very small size (200 microns) including a preliminary step for forming at least one semiconductor layer on a semiconductor material substrate, forming a diode junction, said method further including the following steps: (1) etching depth indicators in the semiconductor layer, all the indicators having the same depth and penetrating into the substrate, at the rate of at least one indicator between two future diodes, (2) depositing, on the semiconductor layer and in the holes of the indicators, a metal layer for fixing to the semiconductor material, (3) masking on the fixing layer and etching of the mask for freeing the windows corresponding to the future gold bases, (4) electrolytic deposition of the gold bases in the windows of the mask, (5) dissolution of the mask and deposition of a metal diffusion arresting layer, on the gold bases and the visible parts of the fixing layer, (6) growth on the antidiffusion layer of a thick layer of a mechanical support metal etchable by a chemical solution which does not attack gold, (7) thinning of the semiconductor substrate until the depth indicators appear, (8) masking the semiconductor substrate, etching the mask and depositing contact making metallizations on the diodes, (9) etching of the mesas of the diodes, (10) collective chemical cutting out into discrete elements by chemically etching the mechanical support metal layer and the fixing layer.
Claim 3
Dependent Claim
30 words
The method as claimed in claim 1, wherein said layer for fixing the gold base on the semiconductor material is formed by the metal chain Si Pt/Ti/Pt/Au or by Cr/Pt/Au.
Claim 4
Dependent Claim
26 words
The method as claimed in claim 1, wherein the mask for forming the gold bases is organic or mineral, made from silica, silicon nitride, aluminium nitride.
Claim 5
Dependent Claim
16 words
The method as claimed in claim 1, wherein said diffusion barrier layer is made from nickel.
Claim 6
Dependent Claim
36 words
The method as claimed in claim 1, wherein the thick metal mechanical supporting layer is made from a metal chemically etchable by a solution which does not attack gold, such as copper, or tin, or silver.
Claim 7
Dependent Claim
33 words
The method as claimed in claim 5, wherein the solution for chemically etching the thick layer is a normal nitric acid solution at 70° C., used for 30 minutes with activation by ultrasounds.
Claim 8
Dependent Claim
34 words
A semiconductor device fixed on a gold base, cut out chemically using the method of claim 1, wherein a curved surface joins the two main surfaces of the gold base together without sharp edges.
Claim 9
Dependent Claim
35 words
A semiconductor device fixed on a gold base, cut out chemically using the method of claim 1, wherein at least one angle of the gold base carries the trace of at least one depth indicator.
References Cited (Backward Citations)
US3288662A
Cited
US3973320A
Cited
US4029542A
Cited
US4304043A
Cited
EP0052309A1
Cited
US4499659A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-06 | 1992-09-05 | 1993-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-06 | 1996-09-05 | 1997-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-06 | 2000-09-05 | 2001-03-07 | $7700.00 | Window Closed / Lapsed |