Assignee: Advanced Tool Technologies Inc
•
Filing: 1987-10-13
•
Granted: 1989-04-04
•
Expires: 2007-10-13
Abstract
Abstract A method of forming a metal mold or die from a model of the mold contours. A workpiece for the mold is coated with a material which is resistant to an acidic etchant and which has a melting temperature sufficiently elevated such that the coating is generally solid. The coated workpiece is then immersed in an etchant, and a heated template is pressed against the coated workpiece, melting any portions of the coating contacted by the template. The melted portions of the coating are displaced until the template contacts the surface of the workpiece. The template is then withdrawn to permit solidification of the coating, the etchant etches any portions of the workpiece exposed by displacement of the coating, and the process is repeated until the surface of the workpiece conforms to any contouring of the surface of the template.
Inventors
- 👤 James J. Rossetti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:48
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/02; C23F1/04
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
232 words
A method of forming a contoured surface in a workpiece in the form of a metal mold or die by etching the surface thereof comprising the steps of; a. providing a template having a contoured surface which is a negative pattern of the contoured surface to be formed in the workpiece, b. applying a meltable coating to the workpiece, the coating being resistant to an etchant and having a melting temperature such that the coating is generally solid after application to the workpiece, c. immersing the coated workpiece in an etchant, d. heating the template to at least the melting temperature of the coating, e. pressing the heated template against the coated workpiece and melting any portions of said coating contacted by the template, f. only displacing the melted portions of said coating as the contoured surface of the template moves into contact with the workpiece, g. withdrawing the template from the coated workpiece to permit resolidification of any melted coating, while leaving any locations of the workpiece contacted by the contoured surface of the template essentially free of said coatings and exposing portions of the workpiece without withdrawing any coating with the template; h. permitting the etchant to etch said portions of the workpiece exposed by displacement of the coating and i. repeating steps (e) through (h) until the surface of the workpiece conforms to the contoured surface of the template.
Claim 2
Independent Claim
232 words
A method of forming a contoured surface in a workpiece in the form of a metal mold or die by etching the surface thereof comprising the steps of; a. providing a template having a contoured surface which is a negative pattern of the contoured surface to be formed in the workpiece, b. applying a meltable coating to the workpiece, the coating being resistant to an etchant and having a melting temperature such that the coating is generally solid after application to the workpiece, c. immersing the coated workpiece in an etchant, d. heating the template to at least the melting temperature of the coating, e. pressing the heated template against the coated workpiece and melting any portions of said coating contacted by the template, f. only displacing the melted portions of said coating as the contoured surface of the template moves into contact with the workpiece, g. withdrawing the template from the coated workpiece to permit resolidification of any melted coating, while leaving any locations of the workpiece contacted by the contoured surface of the template essentially free of said coatings and exposing portions of the workpiece without withdrawing any coating with the template; h. permitting the etchant to etch said portions of the workpiece exposed by displacement of the coating and i. repeating steps (e) through (h) until the surface of the workpiece conforms to the contoured surface of the template.
Claim 3
Dependent Claim
31 words
The method according to claim 1 in which the coating softens before melting, and including the step of heating the workpiece to the softening temperature of the coating before step (e).
Claim 4
Dependent Claim
58 words
The method according to claim 1 including forming the template by the steps of providing a model for the template, pouring a liquid material over the model which subsequently hardens to form a temporary mold for the template, removing the model from the temporary mold, and casting a hardenable material in the temporary mold to form the template.
Claim 5
Dependent Claim
27 words
The method according to claim 3 including the step of applying a release agent to the model before applying the liquid material to form the temporary mold.
Claim 6
Dependent Claim
39 words
The method according to claim 1 including forming the coating by the steps of melting a wax, melting a tar, and mixing the tar into the wax to form a mixture which, when hardened, can be softened before melting.
Claim 7
Independent Claim
246 words
A method of forming a contoured surface in a workpiece in the form of a metal mold or die by progressively etching the surface thereof, comprising the steps of; a. providing a template having a contoured surface which is a negative pattern of the contoured surface to be formed in the workpiece, b. applying a meltable coating to the workpiece, the coating being resistant to an etchant and having a melting temperature such that the coating is generally solid after application to the workpiece, the coating being capable of softening before melting, c. immersing the coated workpiece in an etchant, d. heating the template to at least the melting temperature of the coating, e. heating the workpiece until the coating softens, f. pressing the heated template against the coated workpiece and melting any portions of said coating contacted by the template, g. only displacing the melted portions of said coating until the contoured surface of the template contacts the workpiece, h. withdrawing the template from the coated workpiece to permit solidification of any melted coating while leaving any locations of the workpiece contacted by the contoured surface of the template essentially free of the coating and exposing portions of the workpiece without withdrawing any coating with the template, i. permitting the etchant to etch said portions of the workpiece exposed by displacement of the coating, and j. repeating steps (e) through (i) until the surface of the workpiece conforms to the contoured surface of the template.
Claim 8
Independent Claim
246 words
A method of forming a contoured surface in a workpiece in the form of a metal mold or die by progressively etching the surface thereof, comprising the steps of; a. providing a template having a contoured surface which is a negative pattern of the contoured surface to be formed in the workpiece, b. applying a meltable coating to the workpiece, the coating being resistant to an etchant and having a melting temperature such that the coating is generally solid after application to the workpiece, the coating being capable of softening before melting, c. immersing the coated workpiece in an etchant, d. heating the template to at least the melting temperature of the coating, e. heating the workpiece until the coating softens, f. pressing the heated template against the coated workpiece and melting any portions of said coating contacted by the template, g. only displacing the melted portions of said coating until the contoured surface of the template contacts the workpiece, h. withdrawing the template from the coated workpiece to permit solidification of any melted coating while leaving any locations of the workpiece contacted by the contoured surface of the template essentially free of the coating and exposing portions of the workpiece without withdrawing any coating with the template, i. permitting the etchant to etch said portions of the workpiece exposed by displacement of the coating, and j. repeating steps (e) through (i) until the surface of the workpiece conforms to the contoured surface of the template.
References Cited (Backward Citations)
US3290192A
Cited
US3891437A
Cited
US4028455A
Cited
US4035226A
Cited
US4210695A
Cited
US4325779A
Cited
US4579022A
Cited
US4594120A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-03 | 1992-10-03 | 1993-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-03 | 1996-10-03 | 1997-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-03 | 2000-10-03 | 2001-04-04 | $7700.00 | Window Closed / Lapsed |