Purification of condensation products

Claim 2

A process for removing color-formers from polymeric sulfonated phenol-formaldehyde condensation products so as to provide condensation products having reduced tendencies to turn yellow and which will provide stain-resistance to polyamide textile substrates which comprises (a) dissolving a polymeric sulfonated phenol-formaldehyde condensation product in an aqueous base, (b) acidifying the resulting aqueous solution so as to form a slurry, (c) heating the slurry so as to form a system having at least two phases comprising an aqueous solution and a water-insoluble taffy-like material, (d) separating the aqueous solution and the water-insoluble material from one another, and (e) dissolving the water-insoluble material in an aqueous base.

Claim 3

The process of claim 1 wherein said base used in steps (a) and (e) is NaOH.

Claim 4

The process of claim 1 wherein glacial acetic acid is used in step (b) to acidify said aqueous solution and thereby effect formation of said slurry.

Claim 5

A process for removing color-formers from polymeric sulfonated phenol-formaldehyde condensation products so as to provide condensation products having reduced tendencies to turn yellow and which will provide stain-resistance to polyamide textile substrates which comprises (a) dissolving a polymeric sulfonated phenol-formaldehyde condensation product in water at a pH between about 8.0 and about 12 to give an aqueous solution containing between about 10 and about 40 weight percent of said condensation product, (b) acidifying the resulting aqueous solution to a pH in the range between about 2.0 and 7.5 so as to form a slurry, (c) heating said slurry to a temperature in the range between about 50° and about 65° C. as so to form a system having at least two phases comprising an aqueous solution and a water-insoluble taffy-like material, (d) separating the aqueous solution and water-insoluble taffy-like material from one another, and (e) dissolving the water-insoluble material in water at a pH of at least about 8.0 to give a solution having a concentration of purified sulfonated phenol-formaldehyde condensation product of less than about 50 weight percent.

Claim 6

A process for removing color-formers from polymeric sulfonated phenol-formaldehyde condensation products so as to provide condensation products having reduced tendencies to turn yellow and which will provide stain-resistance to polyamide textile substrates which comprises (a) dissolving a polymeric sulfonated phenol-formaldehyde condensation product in water at a pH between about 8.0 and about 12 to give an aqueous solution containing between about 10 and about 40 weight percent of said condensation product, (b) acidifying the resulting aqueous solution to a pH in the range between about 2.0 and 7.5 so as to form a slurry, (c) heating said slurry to a temperature in the range between about 50° and about 65° C. as so to form a system having at least two phases comprising an aqueous solution and a water-insoluble taffy-like material, (d) separating the aqueous solution and water-insoluble taffy-like material from one another, and (e) dissolving the water-insoluble material in water at a pH of at least about 8.0 to give a solution having a concentration of purified sulfonated phenol-formaldehyde condensation product of less than about 50 weight percent.

Claim 7

The process of claim 4 wherein NaOH is used in steps (a) and (e) to provide the alkaline pH's recited therein.

Claim 8

The process of claim 4 wherein glacial acetic acid is used in step (b) to acidify said aqueous solution and thereby effect formation of said slurry.

Claim 9

A process for removing color-formers from polymeric sulfonated phenol-formaldehyde condensation products so as to provide condensation products having reduced tendencies to turn yellow and which will provide stain-resistance to polyamide textile substrates which comprises (a) dissolving a polymeric sulfonated phenol-formaldehyde condensation product in water at a pH between about 9.5 and about 10.0 to give an aqueous solution containing between about 25 and about 30 weight percent of said condensation product, (b) acidifying the resulting aqueous solution to a pH in the range between about 5.5 to about 6.5 so as to form a slurry, (c) heating said slurry to a temperature in the range between about 50° and about 55° C. so as to from a system having at least two phases comprising an aqueous solution and a water-insoluble taffy-like material, (d) separating the aqueous solution and water-insoluble taffy-like material from one another, and (e) dissolving the water-insoluble material in water at a pH between about 8.0 and about 9.5 to give a solution having a concentration of purified sulfonated phenol-formaldehyde condensation product of between about 28 and about 30 weight percent.

Claim 10

A process for removing color-formers from polymeric sulfonated phenol-formaldehyde condensation products so as to provide condensation products having reduced tendencies to turn yellow and which will provide stain-resistance to polyamide textile substrates which comprises (a) dissolving a polymeric sulfonated phenol-formaldehyde condensation product in water at a pH between about 9.5 and about 10.0 to give an aqueous solution containing between about 25 and about 30 weight percent of said condensation product, (b) acidifying the resulting aqueous solution to a pH in the range between about 5.5 to about 6.5 so as to form a slurry, (c) heating said slurry to a temperature in the range between about 50° and about 55° C. so as to from a system having at least two phases comprising an aqueous solution and a water-insoluble taffy-like material, (d) separating the aqueous solution and water-insoluble taffy-like material from one another, and (e) dissolving the water-insoluble material in water at a pH between about 8.0 and about 9.5 to give a solution having a concentration of purified sulfonated phenol-formaldehyde condensation product of between about 28 and about 30 weight percent.

Claim 11

The process of claim 7 wherein NaOH is used in steps (a) and (e) to provide the alkaline pH's recited therein.

Claim 12

The process of claim 7 wherein glacial acetic acid is used in step (b) to acidify said aqueous solution and thereby effect formation of said slurry.

Claim 13

The process of claim 9 wherein NaOH is used in steps (a) and (e) to provide the alkaline pH's recited therein.

Claim 14

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 1.

Claim 15

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 2.

Claim 16

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 3.

Claim 17

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 4.

Claim 18

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 5.

Claim 19

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 6.

Claim 20

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 7.

Claim 21

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 8.

Claim 22

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 9.

Claim 23

A polyamide textile substrate having deposited thereon an amount effective to provide stain-resistance of the product of claim 10.