Mask for ion, electron or X-ray lithography and method of making it
Assignee: International Business Machines Corp
•
Filing: 1987-05-01
•
Granted: 1989-08-08
•
Expires: 2007-05-01
Abstract
Abstract A mask for radiation beam lithography is formed from a semiconductor wafer by thinning a region into a membrane with a hole pattern defining the pattern of the mask. The membrane is doped with a tensile stress-generating material so that minimum doping exists at the periphery of the membrane with the maximum at its center. The difference in doping between the periphery and the center is chosen so that when the mask is irradiated with a given beam current intensity, the membrane is tension-free. To make a mask in the wafer, a hole pattern is formed by etching holes in the membrane or by depositing a layer on the membrane. The wafer is thinned from the opposite surface until the holes in the hole pattern are throughholes or until the desired thickness is reached. The membrane is doped with tensile-stress-generating material using ion implantation or diffusion proportionally to the temperature distribution existing in the membrane during irradiation with exposure beams.
Inventors
- 👤 Werner Zapka
- 👤 Jurgen Kempf
- 👤 Joachim Keyser
- 👤 Karl Asch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 06:32
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/20; G03F1/22; G03F7/00; G03F7/70; G03F7/708; G03F7/70858; G03F7/70866; G03F7/70875; Y; Y10; Y10S; Y10S430/00; Y10S430/167
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
123 words
A mask for radiation beam lithography comprising a membrane of semiconductor material having a pair of opposing surfaces and a center and a periphery about said center, said membrane having a laterally inhomogeneous doping profile across said membrane from said periphery of said membrane to said center of said membrane to said periphery of said membrane on the opposite side of said center, said doping concentration being maximum at said center of said membrane and said doping concentration being at a minimum at said periphery of said membrane, said doping concentration varying from the periphery of said membrane to the center of said membrane and to the periphery of said membrane on the opposite side of said center as substantially a parabolic function.
Claim 2
Dependent Claim
123 words
A mask for radiation beam lithography comprising a membrane of semiconductor material having a pair of opposing surfaces and a center and a periphery about said center, said membrane having a laterally inhomogeneous doping profile across said membrane from said periphery of said membrane to said center of said membrane to said periphery of said membrane on the opposite side of said center, said doping concentration being maximum at said center of said membrane and said doping concentration being at a minimum at said periphery of said membrane, said doping concentration varying from the periphery of said membrane to the center of said membrane and to the periphery of said membrane on the opposite side of said center as substantially a parabolic function.
Claim 3
Dependent Claim
67 words
A mask for radiation beam lithography in accordance with claim 1 wherein said membrane having been treated to have a laterally inhomogeneous doping profile across said membrane from said periphery of said membrane to said center to said periphery on the opposite side of the center by as follows: (a) additively doping with a nonuniform doping concentration of a doping element, or (b) subtractively out-diffusing already built-in-atoms.
Claim 4
Dependent Claim
40 words
A mask for radiation beam lithography in accordance with claim 1 wherein said doping concentration varies from the periphery to the center of said membrane by an amount of the order of 10 19 to 10 20 atoms/cm 3 .
Claim 5
Dependent Claim
34 words
A mask for radiation beam lithography in accordance with claim 3 wherein said membrane of semiconductor material comprises silicon, and said doping element is selected from the group consisting of boron, phosphorous and carbon.
Claim 6
Dependent Claim
135 words
A mask for radiation beam lithography comprising a semiconductor wafer having a pair of opposing surfaces, said wafer having a differently doped layer at least in regions form a first one of said opposing surfaces down to a predetermined depth spaced from the second one of said opposing surfaces, said wafer having been etched to leave a membrane of said differently doped layer, said membrane having a tensile-stress-generating doping which is nonuniform in doping concentration over the surface of said membrane with said doping concentration being minimum at the periphery of said membrane and at a maximum at its center, said doping concentration varying from the periphery of said membrane to the center of said membrane and to the periphery of said membrane on the opposite side of said center as substantially a parabolic function.
Claim 7
Dependent Claim
135 words
A mask for radiation beam lithography comprising a semiconductor wafer having a pair of opposing surfaces, said wafer having a differently doped layer at least in regions form a first one of said opposing surfaces down to a predetermined depth spaced from the second one of said opposing surfaces, said wafer having been etched to leave a membrane of said differently doped layer, said membrane having a tensile-stress-generating doping which is nonuniform in doping concentration over the surface of said membrane with said doping concentration being minimum at the periphery of said membrane and at a maximum at its center, said doping concentration varying from the periphery of said membrane to the center of said membrane and to the periphery of said membrane on the opposite side of said center as substantially a parabolic function.
Claim 8
Dependent Claim
20 words
A mask in accordance with claim 5 wherein said membrane has a thickness on the order of 2 μm-3 μm.
Claim 9
Dependent Claim
170 words
A mask for ion, electron or x-ray lithography, which comprises a semiconductor wafer having top and bottom surfaces said wafer having a differently doped layer at least in regions from said top surface of said wafer down to a depth of 2-3 μm from the said bottom surface of said wafer, said wafer being selectively etched from said bottom surface down to said bottom said differently doped layer thereby forming a thin membrane in the process, and a hole pattern defining a mask pattern being etched either into said membrane or into a layer deposited on said membrane, said membrane having a tensile-stress-generating doping material which is nonuniform in doping concentration over said membrane, with said doping concentration being at a minimum in the periphery of said membrane and at a maximum in its center, said doping concentration varying from the periphery of said membrane to the center of said membrane and to the periphery of said membrane on the opposite side of said center as substantially a parabolic function.
Claim 10
Dependent Claim
170 words
A mask for ion, electron or x-ray lithography, which comprises a semiconductor wafer having top and bottom surfaces said wafer having a differently doped layer at least in regions from said top surface of said wafer down to a depth of 2-3 μm from the said bottom surface of said wafer, said wafer being selectively etched from said bottom surface down to said bottom said differently doped layer thereby forming a thin membrane in the process, and a hole pattern defining a mask pattern being etched either into said membrane or into a layer deposited on said membrane, said membrane having a tensile-stress-generating doping material which is nonuniform in doping concentration over said membrane, with said doping concentration being at a minimum in the periphery of said membrane and at a maximum in its center, said doping concentration varying from the periphery of said membrane to the center of said membrane and to the periphery of said membrane on the opposite side of said center as substantially a parabolic function.
Claim 11
Dependent Claim
38 words
A mask in accordance with claim 7 characterized in that the concentration distribution of said tensile-stress-generating doping over said membrane is directly proportional to the temperature distribution during irradiation with electron, ion or X-ray beams in said membrane.
Claim 12
Dependent Claim
92 words
A mask in accordance with claim 7 where in said membrane is about 22×11 mm 2 and about 2 μm thick, that the overall hole surface amounts to 40% of the membrane surface and that it is tension-free if exposed to a beam current of 10 microamperes, and in that the non-compensated boron doping in the center of said membrane is higher than in its periphery by an amount (in 10 19 atoms/cm 3 ) which is in a ratio of approximately 3:20 to the beam current in microamperes to be used.
Claim 13
Dependent Claim
44 words
A mask in accordance with claim 7 in that the effect of said doping material is partly compensated by a stress relieving doping material for eliminating the tensile stress, said stress relieving doping material having in silicon a greater covalent atomic radius than silicon.
Claim 14
Dependent Claim
22 words
A mask in accordance with claim 10, said doping material comprising a material selected from the group consisting of arsenic and germanium.
Claim 15
Dependent Claim
14 words
A mask in accordance with claim 7, wherein said semiconductor wafer consists of silicon.
Claim 16
Dependent Claim
38 words
A mask in accordance with claim 12 characterized in that the concentration distribution of said tensile-stress-generating doping over the membrane is directly proportional to the temperature distribution during irradiation with electron, ion or X-ray beams in the membrane.
Claim 17
Dependent Claim
38 words
A mask as claimed in claim 12, including as said doping material a tensile-stress-generating doping material at least one element with a smaller covalent atomic radius than silicon, selected from the group consisting of boron, carbon and phosphorus.
Claim 18
Dependent Claim
39 words
A mask in accordance with claim 14 characterized in that the concentration distribution of the tensile stress-generating doping over the membrane is directly proportional to the temperature distribution during irradiation with electron, ion or X-ray beams in the membrane.
Claim 19
Independent Claim
218 words
A method of making a mask wherein a semiconductor wafer having a pair of opposing surfaces is differently doped to form a differently doped layer from one of said surfaces to a depth of 2-3 μm with respect to the remaining portion of said semiconductor wafer, where, from the opposite surface, said wafer is selectively etched down to said differently doped layer, with a membrane being formed in the process, etching a pattern of hole defining the mask pattern in said membrane, or into said semiconductor wafer where said membrane is to be formed respectively into a mask, or into a layer deposited on said membrane, said membrane being treated to have a laterally inhomogeneous doping profile to have minimum stress at the periphery of said membrane and maximum stress in the center of said membrane by means of an additional doping or out-diffusion to eliminate mechanical tensions produced through the first doping, and/or an additional non-uniform doping, said doping profile varying from the periphery of said membrane to the center of said membrane and to the periphery of said membrane on the opposite side of said center as substantially a parabolic function, whereby said inhomogeneous doping profile generates a tension stress being proportional to the temperature distribution developing thereover in the irradiation with ion, electron or x-rays.
Claim 20
Independent Claim
218 words
A method of making a mask wherein a semiconductor wafer having a pair of opposing surfaces is differently doped to form a differently doped layer from one of said surfaces to a depth of 2-3 μm with respect to the remaining portion of said semiconductor wafer, where, from the opposite surface, said wafer is selectively etched down to said differently doped layer, with a membrane being formed in the process, etching a pattern of hole defining the mask pattern in said membrane, or into said semiconductor wafer where said membrane is to be formed respectively into a mask, or into a layer deposited on said membrane, said membrane being treated to have a laterally inhomogeneous doping profile to have minimum stress at the periphery of said membrane and maximum stress in the center of said membrane by means of an additional doping or out-diffusion to eliminate mechanical tensions produced through the first doping, and/or an additional non-uniform doping, said doping profile varying from the periphery of said membrane to the center of said membrane and to the periphery of said membrane on the opposite side of said center as substantially a parabolic function, whereby said inhomogeneous doping profile generates a tension stress being proportional to the temperature distribution developing thereover in the irradiation with ion, electron or x-rays.
Claim 21
Dependent Claim
103 words
A method claimed in claim 16, wherein a p-doped or n-doped silicon wafer is, first, doped with boron to a depth of 2-3 μm, for partly compensating said boron doping there follows an additional non-uniform doping with a material selected from the group consisting of germanium, indium, arsenic and antimony, in such a manner that the concentration profile of the additional doping over said membrane is proportional to the inverse temperature distribution over said membrane developing in the irradiation with ion, electron or X-rays, with the additional doping having a minimum in the center of said membrane, and a maximum at the periphery.
Claim 22
Dependent Claim
51 words
A method in accordance with claim 16, wherein additional non-uniform doping is implemented by means of ion implantation, with the ion beam scanning said membrane, and that either the intensity of the beam or the speed of its motion is varied under computer control in accordance with the desired doping profile.
Claim 23
Dependent Claim
111 words
A method as claimed in claim 16, wherein p-doped or n-doped silicon wafer is, first, p + -doped with boron to a depth of 2-3 μm, following the producing of said membrane said boron doping is compensated by a doping with a material selected from the group consisting of germanium, indium, arsenic and antimony until absence of tension at room temperature, and said membrane being non-uniformly doped with a material selected from the group consisting of boron, carbon, phosphorus, in such a manner that the concentration distribution over said membrane developing during the non-uniform doping is proportional to the temperature distribution existing thereover in the irradiation in the electron or X-rays.
Claim 24
Dependent Claim
45 words
A method in accordance with claim 19, wherein doping is effected in such a manner that for the predetermined beam current the residual tension in said membrane is between zero and that tension which causes a maximum distortion in said membrane of approximately 10 nm.
References Cited (Backward Citations)
US3742230A
Cited
JPS5393785A
Cited
US4417946A
Cited
US4342817A
Cited
JPS5616136A
Cited
JPS5622433A
Cited
US4393127A
Cited
US4468799A
Cited
US4451544A
Cited
US4448865A
Cited
US4589952A
Cited
US4640844A
Cited
US4647517A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-07 | 1993-02-06 | 1993-08-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-07 | 1997-02-06 | 1997-08-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-07 | 2001-02-06 | 2001-08-08 | $7700.00 | Window Closed / Lapsed |