Electrochemical synthesis of ceramic films and powders
Assignee: Union Oil Company of California
•
Filing: 1988-02-24
•
Granted: 1989-11-21
•
Expires: 2008-02-24
Abstract
Abstract Ceramic precursor compositions, such as metal hydroxides and oxides, are electrochemically deposited in a biased electrochemical cell. The cell typically generates hydroxide ions that precipitate metallic or semimetallic ions to form insoluble solids that may be separated from the cell, then dried, calcined and sintered to form a ceramic composition.
Inventors
- 👤 R. Tom Coyle
- 👤 Jay A. Switzer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:03
CPC Classifications
C; C25; C25B; C25B1/00; C04; C04B; C04B35/00; C04B35/622; C25B1/01; Y; Y10; Y10S; Y10S204/00; Y10S204/06; Y10S264/00; Y10S264/25; Y10S264/36
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
72 words
A method for the production of a ceramic precursor composition, said method comprising the step of electrochemical deposition of a ceramic precursor composition in a biased electrochemical cell having a anode and a cathode wherein acid or base materials are electrochemically generated at the anode or cathode, respectively, of said cell and said acid or base materials reacting with starting materials in said electrochemical cell to produce an electrodeposited ceramic precursor composition.
Claim 2
Independent Claim
72 words
A method for the production of a ceramic precursor composition, said method comprising the step of electrochemical deposition of a ceramic precursor composition in a biased electrochemical cell having a anode and a cathode wherein acid or base materials are electrochemically generated at the anode or cathode, respectively, of said cell and said acid or base materials reacting with starting materials in said electrochemical cell to produce an electrodeposited ceramic precursor composition.
Claim 3
Dependent Claim
26 words
The method defined in claim 1 wherein said ceramic precursor composition is selected from the group consisting of metal-containing oxides, metal-containing hydroxides, carbides, nitrides and silicides.
Claim 4
Dependent Claim
16 words
The method defined in claim 1 further comprising the step of drying said ceramic precursor composition.
Claim 5
Dependent Claim
21 words
The method defined in claim 3 further comprising the step of calcining the dried ceramic precursor composition obtained in claim 3.
Claim 6
Dependent Claim
26 words
The method defined in claim 4 further comprising the step of sintering the calcined ceramic precursor composition obtained in claim 4 to produce a ceramic composition.
Claim 7
Dependent Claim
119 words
The method defined in claim 5 wherein said ceramic composition is selected from the group consisting of La 2 O 3 , SiC, ZrO 2 , AlN, CeO 2 , BaTiO 3 , Al 2 O 3 , SiO 2 , neodymium barium titanate, lanthanide barium cuprate, lanthanum strontium barium cuprate, bismuth strontium calcium cuprate, boron nitride, zinc ferrite, WC, TiC, gadolinium scandium, barium garnet, gadolinium scandium aluminum garnet, yttri um europium oxysulfide, UO 2 , ThO 2 , ThO 2 : Nd 2 O 3 , MgO, BeO, LiAlO 2 , TiO 2 , Pb(Zr,Ti)O 3 , ZnO, lead lanthanum zirconate titanate, SnO 2 , LaB 6 , and Ba 2 NaNb 5 O 15 and mixtures thereof.
Claim 8
Independent Claim
79 words
A method for producing a ceramic precursor composition, said method comprising the following steps: (1) electrochemically generating acid or base materials at an anode or at a cathode respectively, of a biased electrochemical cell containing an anode compartment separated from a cathode compartment, said acid or base materials reacting with starting materials contained in said compartments to produce an electrodesposited ceramic precursor composition and (2) said electrochemically deposited ceramic precursor composition obtained in step (1) is dispersed and dried.
Claim 9
Independent Claim
79 words
A method for producing a ceramic precursor composition, said method comprising the following steps: (1) electrochemically generating acid or base materials at an anode or at a cathode respectively, of a biased electrochemical cell containing an anode compartment separated from a cathode compartment, said acid or base materials reacting with starting materials contained in said compartments to produce an electrodesposited ceramic precursor composition and (2) said electrochemically deposited ceramic precursor composition obtained in step (1) is dispersed and dried.
Claim 10
Dependent Claim
24 words
The method defined in claim 7 further comprising step (3) wherein the dispersed and dried ceramic precursor composition obtained in step (2) is calcined.
Claim 11
Dependent Claim
25 words
The method defined in claim 8 further comprising step (4) wherein the calcined ceramic precursor composition obtained in step (3) is sintered or partially sintered.
Claim 12
Dependent Claim
31 words
The method defined in claim 8 further comprising step (4) wherein the dried ceramic precursor composition obtained in step (3) is compressed to form a green body and then is sintered.
Claim 13
Dependent Claim
35 words
The method defined in claim 8 wherein the calcined ceramic precursor composition obtained in step (3) has a crystallite size in the range from about 600 angstroms to about 10,000 angstroms, calculated as the diameter.
Claim 14
Dependent Claim
27 words
The method defined in claim 7 further comprising step (3) wherein the dispersed and dried ceramic precursor composition obtained in step (2) is sintered or partially sintered.
Claim 15
Dependent Claim
31 words
The method defined in claim 7 wherein said cathode compartment contains a metallic or semimetallic ion in a solution containing water and wherein said water is hydrolyzed to generate hydroxide ions.
Claim 16
Dependent Claim
36 words
The method defined in claim 7 wherein the dispersed and dried ceramic precursor composition obtained from step (2) has crystallite size in the range from about 50 angstroms to about 500 angstroms, calculated as the diameter.
Claim 17
Dependent Claim
38 words
The method defined in claim 7 wherein the dispersed and dried ceramic precursor composition obtained in step (2) has an average particle size in the range from about 0.1 micrometers to about 1.0 micrometers, calculated as the diameter.
Claim 18
Independent Claim
115 words
A method for producing a ceramic precursor composition, said method comprising the following steps: (1) electrochemically depositing a ceramic precursor composition in a cathode compartment of a biased electrochemical cell which contains an anode and anode compartment separated from a cathode and cathode compartment, said electrochemical cell generating a base material at the cathode in the cathode compartment and said ceramic precursor composition containing a metal oxide or metal hydroxide, (2) said electrochemically deposited ceramic precursor composition obtained in step (1) is dispersed and dried, and (3) said dispersed and dried ceramic precursor composition obtained in step (2) is compressed to a green body and sintered to produce a ceramic composition containing a metal oxide.
Claim 19
Independent Claim
115 words
A method for producing a ceramic precursor composition, said method comprising the following steps: (1) electrochemically depositing a ceramic precursor composition in a cathode compartment of a biased electrochemical cell which contains an anode and anode compartment separated from a cathode and cathode compartment, said electrochemical cell generating a base material at the cathode in the cathode compartment and said ceramic precursor composition containing a metal oxide or metal hydroxide, (2) said electrochemically deposited ceramic precursor composition obtained in step (1) is dispersed and dried, and (3) said dispersed and dried ceramic precursor composition obtained in step (2) is compressed to a green body and sintered to produce a ceramic composition containing a metal oxide.
References Cited (Backward Citations)
US3073763A
Cited
US3338802A
Cited
US4098725A
Cited
US4020134A
Cited
US4383897A
Cited
US4520077A
Cited
US4501818A
Cited
US4657879A
Cited
US4605631A
Cited
US4585540A
Cited
US4615736A
Cited
US4657754A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-20 | 1993-05-22 | 1993-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-20 | 1997-05-22 | 1997-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-20 | 2001-05-22 | 2001-11-21 | $7700.00 | Window Closed / Lapsed |