US4882398A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Optically clear reinforced organosiloxane compositions
Assignee: Dow Silicones Corp
•
Filing: 1988-08-26
•
Granted: 1989-11-21
•
Expires: 2008-08-26
Abstract
Abstract The presence of up to about 40 percent by weight of a resinous organosiloxane copolymer consisting essentially of trimethylsiloxy, dimethylvinylsiloxy and SiO 2 units in a diorganovinylsiloxy-terminated polydiorganosiloxane containing at least 95 mol percent of dimethylsiloxane units and having a viscosity greater than about 12 Pa.s at 25 degrees C., unexpectedly decreases the viscosity of the mixture relative to the viscosity of the polydiorganosiloxane. Elastomers obtained by curing these mixtrues using an organohydrogensiloxane in the presence of a platinum-containing hydrosilation catalyst are transparent and particularly suitable for fabrication or incorporation into optical devices such as windows, windshields and lenses.
Inventors
- 👤 Godfrey C. Mbah
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:58
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20; C08G77/22; C08G77/24
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
215 words
In a curable composition comprising (1) a diorganovinylsiloxy-terminated polydiorganosiloxane, (2) an amount of a resinous organosiloxane copolymer sufficient to improve the physical properties of the elastomer obtained by curing said composition. (3) an amount of an organohydrogensiloxane sufficient to cure said composition, and (4) an amount of a platinum-containing hydrosilation catalyst sufficient to promote curing of said composition. the improvement comprising (a) selecting said polydiorganosiloxane from those exhibiting a viscosity of at least 12 Pa.s at 25 degrees C. and wherein at least 95% of the repeating units are dimethylsiloxane units and any remainder are diorganosiloxane units wherein the organic groups bonded to silicon are monovalent hydrocarbon radicals or monovalent halogenated hydrocarbon radicals (b) selecting said organosiloxane copolymer from those consisting essentially of SiO 2 , trimethylsiloxy and dimethylvinylsiloxy units, where the molar ratio of the combination of trimethylsiloxy and dimethylvinylsiloxy units to SiO 2 units is from 0.6 to 1.1, inclusive and said copolymer contains from 1.5 to 3.5 weight percent of vinyl radicals, and (c) maintaining the concentration of said organosiloxane copolymer within the range of from 1 to about 45 weight %, based on the weight of said polydiorganosiloxane to achieve a reduction in the viscosity of said composition relative to the viscosity of the composition in the absence of said copolymer.
Claim 2
Dependent Claim
215 words
In a curable composition comprising (1) a diorganovinylsiloxy-terminated polydiorganosiloxane, (2) an amount of a resinous organosiloxane copolymer sufficient to improve the physical properties of the elastomer obtained by curing said composition. (3) an amount of an organohydrogensiloxane sufficient to cure said composition, and (4) an amount of a platinum-containing hydrosilation catalyst sufficient to promote curing of said composition. the improvement comprising (a) selecting said polydiorganosiloxane from those exhibiting a viscosity of at least 12 Pa.s at 25 degrees C. and wherein at least 95% of the repeating units are dimethylsiloxane units and any remainder are diorganosiloxane units wherein the organic groups bonded to silicon are monovalent hydrocarbon radicals or monovalent halogenated hydrocarbon radicals (b) selecting said organosiloxane copolymer from those consisting essentially of SiO 2 , trimethylsiloxy and dimethylvinylsiloxy units, where the molar ratio of the combination of trimethylsiloxy and dimethylvinylsiloxy units to SiO 2 units is from 0.6 to 1.1, inclusive and said copolymer contains from 1.5 to 3.5 weight percent of vinyl radicals, and (c) maintaining the concentration of said organosiloxane copolymer within the range of from 1 to about 45 weight %, based on the weight of said polydiorganosiloxane to achieve a reduction in the viscosity of said composition relative to the viscosity of the composition in the absence of said copolymer.
Claim 3
Dependent Claim
50 words
A composition according to claim 1 where any silicon-bonded organic groups in said polydiorganosiloxane other than methyl are selected from the group consisting of phenyl and 3,3,3-trifluoropropyl, the viscosity of the polydiorganosiloxane is up to 12,500 Pa.s and the concentration of said copolymer is from 5 to 35 weight percent.
Claim 4
Dependent Claim
101 words
A composition according to claim 2 where said polydiorganosiloxane is a polydimethylsiloxane or a copolymer containing 97 mol percent dimethylsiloxane units and 3 mol percent diphenylsiloxane units, the organohydrogensiloxane is a dimethylsiloxane/methylhydrogensiloxane copolymer, the platinum catalyst is a complex of hexachloroplatinic acid and a low molecular weight vinyl-containing organosiloxane compound and is present in an amount equivalent to 5 to 50 parts of platinum per million parts of curable composition and the molar ratio of silicon-bonded hydrogen atoms in said organohydrogensiloxane to the vinyl radicals present in the combination of said polydiorganosiloxane and said organosiloxane copolymer is from 0.2 to 5.
Claim 5
Dependent Claim
27 words
A composition according to claim 3 where said platinum catalyst is a reaction product of hexachloroplatinic acid and sym-tetramethyldivinyldisiloxane and the composition contains a platinum catalyst inhibitor.
Claim 6
Dependent Claim
28 words
A composition according to claim 1 where said composition is in two parts with said organohydrogensiloxane and said platinum-containing catalyst being located in different parts of said composition.
Claim 7
Dependent Claim
22 words
A composition according to claim 5 where each of said parts contains a portion of said polydiorganosiloxane and said resinous organosiloxane copolymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-20 | 1993-05-22 | 1993-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-20 | 1997-05-22 | 1997-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-20 | 2001-05-22 | 2001-11-21 | $7700.00 | Window Closed / Lapsed |