Composite containing coated fibrous material

Claim 2

A process for producing a composite containing at least about 10% by volume of boron nitride coated fibrous material and having a porosity of less than about 20% by volume which comprises: (a) forming a slurry of infiltration-promoting material and organic binding material in a liquid medium; (b) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (c) depositing a silicon-wettable coating on said boron nitride-coated fibrous material leaving no significant portion of said boron nitride exposed; (d) providing the resulting coated fibrous material substantially as a layer; (e) casting said slurry onto said coated fibrous material in an amount sufficient to form a tape therewith; (f) evaporating said liquid medium forming a tape; (g) firing said tape to remove said organic binding material producing a porous body; (h) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in silicon in an amount of at least about 0.1% by weight of elemental silicon; (i) contacting said porous body with infiltrant associated infiltrating means whereby said infiltrant is infiltrated into said porous body; (j) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (k) cooling said product producing said composite.

Claim 3

The process according to claim 1, wherein said silicon-wettable material and said infiltration-promoting material are comprised of elemental carbon.

Claim 4

The process according to claim 1, wherein said infiltration-promoting material is comprised of a mixture of at least 10% by volume of elemental carbon and at least 10% by volume of silicon carbide.

Claim 5

The process according to claim 1, wherein said fibrous material is selected from the group consisting of aluminum oxide, mullite, a carbon-containing material, elemental carbon, a SiC-containing material, silicon carbide, a silicon nitride-containing material, silicon nitride and mixtures thereof.

Claim 6

The process according to claim 1, wherein said fibrous material is comprised of elemental carbon.

Claim 7

The process according to claim 1, wherein said fibrous material is a silicon carbide-containing material.

Claim 8

The process according to claim 1, wherein said composite has a porosity of less than about 10% by volume.

Claim 9

A process for producing a composite containing at least about 10% by volume of boron nitride coated fibrous material and having a porosity of less than about 20% by volume which comprises: (a) forming a slurry of infiltration-promoting material and organic binding material in a liquid medium; (b) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (c) depositing a silicon-wettable coating on said boron nitride-coated fibrous material leaving no significant portion of said boron nitride exposed; (d) providing the resulting coated fibrous material substantially as a layer; (e) casting said slurry onto said coated fibrous material in an amount sufficient to form a tape therewith; (f) evaporating said liquid medium forming a tape; (g) assembling a plurality of said tapes to produce a layered structure; (h) laminating the layered structure to form a laminated structure; (i) firing said laminated structure to remove said organic binding material producing a porous body; (j) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in silicon in an amount of at least about 0.1% by weight of elemental silicon; (k) contacting said porous body with infiltrant associated infiltrating means whereby said infiltrant is infiltrated into said porous body; (l) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (m) cooling said product producing said composite.

Claim 10

A process for producing a composite containing at least about 10% by volume of boron nitride coated fibrous material and having a porosity of less than about 20% by volume which comprises: (a) forming a slurry of infiltration-promoting material and organic binding material in a liquid medium; (b) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (c) depositing a silicon-wettable coating on said boron nitride-coated fibrous material leaving no significant portion of said boron nitride exposed; (d) providing the resulting coated fibrous material substantially as a layer; (e) casting said slurry onto said coated fibrous material in an amount sufficient to form a tape therewith; (f) evaporating said liquid medium forming a tape; (g) assembling a plurality of said tapes to produce a layered structure; (h) laminating the layered structure to form a laminated structure; (i) firing said laminated structure to remove said organic binding material producing a porous body; (j) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in silicon in an amount of at least about 0.1% by weight of elemental silicon; (k) contacting said porous body with infiltrant associated infiltrating means whereby said infiltrant is infiltrated into said porous body; (l) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (m) cooling said product producing said composite.

Claim 11

The process according to claim 8, wherein said silicon-wettable material and said infiltration-promoting material are comprised of elemental carbon.

Claim 12

The process according to claim 8, wherein said infiltration-promoting material is comprised of a mixture of at least about 10% by volume of elemental carbon and at least about 10% by volume of silicon carbide.

Claim 13

The process according to claim 8, wherein said fibrous material is selected from the group consisting of aluminum oxide, mullite, a carbon-containing material, elemental carbon, a SiC-containing material, silicon carbide, a silicon nitride-containing material, silicon nitride, and mixtures thereof.

Claim 14

The process according to claim 8, wherein said fibrous material is comprised of elemental carbon.

Claim 15

The process according to claim 8, wherein said fibrous material is a silicon carbide-containing material.

Claim 16

The process according to claim 8, wherein said composite has a porosity of less than about 10% by volume.

Claim 17

A process for producing a composite containing at least about 10% by volume of boron nitride coated filaments and having a porosity of less than about 20% by volume which comprises: (a) forming a slurry of infiltration-promoting material and organic binding material in a liquid medium; (b) depositing a coating of boron nitride on a filament producing a boron nitride coated filament having a diameter of at least about 50 microns leaving no significant portion of said filament exposed; (c) providing a plurality of the resulting coated filaments substantially as a layer wherein said coated filaments are spaced from each other; (d) casting said slurry onto said coated filaments in an amount sufficient to form a tape therewith; (e) evaporating said liquid medium forming a tape; (f) firing said tape to remove said organic binding material producing a porous body; (g) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in silicon in an amount of at least about 0.1% by weight of elemental silicon; (h) contacting said porous body with infiltrant-associated infiltrating means whereby said infiltrant is infiltrated into said porous body; (i) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (j) cooling said product producing said composite.

Claim 18

A process for producing a composite containing at least about 10% by volume of boron nitride coated filaments and having a porosity of less than about 20% by volume which comprises: (a) forming a slurry of infiltration-promoting material and organic binding material in a liquid medium; (b) depositing a coating of boron nitride on a filament producing a boron nitride coated filament having a diameter of at least about 50 microns leaving no significant portion of said filament exposed; (c) providing a plurality of the resulting coated filaments substantially as a layer wherein said coated filaments are spaced from each other; (d) casting said slurry onto said coated filaments in an amount sufficient to form a tape therewith; (e) evaporating said liquid medium forming a tape; (f) firing said tape to remove said organic binding material producing a porous body; (g) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in silicon in an amount of at least about 0.1% by weight of elemental silicon; (h) contacting said porous body with infiltrant-associated infiltrating means whereby said infiltrant is infiltrated into said porous body; (i) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (j) cooling said product producing said composite.

Claim 19

The process according to claim 15, wherein said infiltration-promoting material is comprised of elemental carbon.

Claim 20

The process according to claim 15, wherein said infiltration-promoting material is comprised of a mixture of at least about 10% by volume of elemental carbon and at least about 10% by volume of silicon carbide.

Claim 21

The process according to claim 15, wherein said fibrous material is selected from the group consisting of aluminum oxide, mullite, a carbon-containing material, elemental carbon, a SiC-containing material, silicon carbide, a silicon nitride-containing material, silicon nitride, and mixtures thereof.

Claim 22

The process according to claim 15, wherein said fibrous material is comprised of elemental carbon.

Claim 23

The process according to claim 15, wherein said fibrous material is a silicon carbide-containing material.

Claim 24

The process according to claim 15, wherein said composite has a porosity of less than about 10% by volume.

Claim 25

A process for producing a composite containing at least about 10% by volume of boron nitride coated filaments and having a porosity of less than about 20% by volume which comprises: (a) forming a slurry of infiltration-promoting material and organic binding material in a liquid medium; (b) depositing a coating of boron nitride on a filament producing a boron nitride coated filament having a diameter of at least about 50 microns leaving no significant portion of said filament exposed; (c) providing a plurality of said boron nitride coated filaments substantially as a layer wherein said filaments are spaced from each other; (d) casting said slurry onto said coated filaments in an amount sufficient to form a tape therewith; (e) evaporating said liquid medium forming a tape; (f) assembling a plurality of said tapes to produce a layered structure; (g) laminating the layered structure to form a laminated structure; (h) firing said laminated structure to remove said organic binding material producing a porous body; (i) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in silicon in an amount of at least about 0.1% by weight of elemental silicon; (j) contacting said porous body with infiltrant-associated infiltrating means whereby said infiltrant is infiltrated into said porous body; (k) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (l) cooling said product producing said composite.

Claim 26

A process for producing a composite containing at least about 10% by volume of boron nitride coated filaments and having a porosity of less than about 20% by volume which comprises: (a) forming a slurry of infiltration-promoting material and organic binding material in a liquid medium; (b) depositing a coating of boron nitride on a filament producing a boron nitride coated filament having a diameter of at least about 50 microns leaving no significant portion of said filament exposed; (c) providing a plurality of said boron nitride coated filaments substantially as a layer wherein said filaments are spaced from each other; (d) casting said slurry onto said coated filaments in an amount sufficient to form a tape therewith; (e) evaporating said liquid medium forming a tape; (f) assembling a plurality of said tapes to produce a layered structure; (g) laminating the layered structure to form a laminated structure; (h) firing said laminated structure to remove said organic binding material producing a porous body; (i) providing an infiltrant comprised of boron and silicon containing elemental boron in solution in silicon in an amount of at least about 0.1% by weight of elemental silicon; (j) contacting said porous body with infiltrant-associated infiltrating means whereby said infiltrant is infiltrated into said porous body; (k) heating the resulting assembly in a partial vacuum to a temperature at which said infiltrant is molten and infiltrating said molten infiltrant into said porous body to produce an infiltrated product; and (l) cooling said product producing said composite.

Claim 27

The process according to claim 22, wherein said infiltration-promoting material is comprised of elemental carbon.

Claim 28

The process according to claim 22, wherein said infiltration-promoting material is comprised of a mixture of at least about 10% by volume of elemental carbon and at least about 10% by volume of silicon carbide.

Claim 29

The process according to claim 22, wherein said fibrous material is selected from the group consisting of aluminum oxide, mullite, a carbon-containing material, elemental carbon, a SiC-containing material, silicon carbide, a silicon nitride-containing material, silicon nitride, and mixtures thereof.

Claim 30

The process according to claim 22, wherein said fibrous material is comprised of elemental carbon.

Claim 31

The process according to claim 22, wherein said fibrous material is a silicon carbide containing material.

Claim 32

The process according to claim 22, wherein said composite has a porosity of less than about 10% by volume.