Oxidation-inhibited carbonous materials
Assignee: General Atomics Corp
•
Filing: 1985-12-06
•
Granted: 1990-01-09
•
Expires: 2005-12-06
Abstract
Abstract Composites comprising high-temperature fibers reinforcing a carbonous matrix are protected from oxidation by a B2O3-based glass which includes a refractory oxide to stabilize the viscosity of the glass. Precursors of B2O3 and the refractory oxide are dispersed into a carbon char-yielding material; the material is used to impregnate sheets of fibers; the sheets are laid up as plies; and the laid-up plies are carbonized and graphitized using heat and pressure to form a composite structure. The composite structure is then coated with an additional mix of char-yielding material and precursors, and the coated structure is heated to carbonize the material and leave a seal coat on the structure. Then, an outer coating of a refractory material is deposited on the structure. Oxygen which seeps through the seal coat is initially scavenged at high temperatures by the RO and B2O3 precursors, converting the same to a B2O3-RO glass which protects both the internal pore surfaces of the composite as well as the outer structural surfaces from oxidation.
Inventors
- 👤 Paul E. Gray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 06:22
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/80; C04B41/81; C04B41/85; C04B41/87; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83; C04B41/45; C04B41/50; C04B41/5025; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12069; Y10T428/1209; Y10T428/24; Y10T428/24355; Y10T428/24372; Y10T428/24421; Y10T428/30
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
233 words
An oxygen-resistant, high-temperature structure comprising a carbonous structural matrix formed with interstices throughout, boron, in elemental form and/or as moiety of a compound, said boron being dispersed throughout said matrix, silicon in elemental form and/or as a moiety of a compound, said silicon being dispersed throughout said matrix, plus an additional metal or metalloid, in elemental form and/or as a moiety of a compound, said metal or metalloid being dispersed throughout said matrix, said boron, said silicon and said additional metal or metalloid each oxidizing when exposed to a high-temperature, oxidizing environment to form borosilicate plus a metal oxide or a metalloid oxide within the interstices and at the surface of said matrix; the boron plus silicon plus said additional metal or metalloid, calculated as if in their fully oxidized forms, comprising between about 10 about 1000 weight percent of the carbon in said matrix, said silicon, calculated as a silicon oxide, being present in amounts of from about 3 to about 40 mole percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide; at high temperatures, the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the borosilicate which forms.
Claim 2
Dependent Claim
233 words
An oxygen-resistant, high-temperature structure comprising a carbonous structural matrix formed with interstices throughout, boron, in elemental form and/or as moiety of a compound, said boron being dispersed throughout said matrix, silicon in elemental form and/or as a moiety of a compound, said silicon being dispersed throughout said matrix, plus an additional metal or metalloid, in elemental form and/or as a moiety of a compound, said metal or metalloid being dispersed throughout said matrix, said boron, said silicon and said additional metal or metalloid each oxidizing when exposed to a high-temperature, oxidizing environment to form borosilicate plus a metal oxide or a metalloid oxide within the interstices and at the surface of said matrix; the boron plus silicon plus said additional metal or metalloid, calculated as if in their fully oxidized forms, comprising between about 10 about 1000 weight percent of the carbon in said matrix, said silicon, calculated as a silicon oxide, being present in amounts of from about 3 to about 40 mole percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide; at high temperatures, the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the borosilicate which forms.
Claim 3
Dependent Claim
243 words
An oxygen-resistant, high-temperature composite comprising a structure which includes a carbonous matrix formed with interstices throughout and reinforcing, high-temperature fibers disposed within said matrix, boron, in elemental form and/or as moiety of a compound, said boron being dispersed throughout said matrix, silicon in elemental form and/or as a moiety of a compound, said silicon being dispersed throughout said matrix, plus an additional metal or metalloid, in elemental form and/or as a moiety of a compound, said metal or metalloid being dispersed throughout said matrix, said boron, said silicon plus said additional metal or metalloid each oxidizing when exposed to a high-temperature, oxidizing environment to form borosilicate plus a metal oxide or a metalloid oxide within the interstices and at the surface of said matrix, the boron plus silicon plus said additional metal or metalloid, calculated as if in their fully oxidized forms, comprising between about 10 about 1000 weight percent of the carbon in said matrix, said silicon, calculated as silicon oxide, being present in amounts of from about 3 to about 40 mole percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide; at high temperatures, the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the borosilicate which forms.
Claim 4
Dependent Claim
243 words
An oxygen-resistant, high-temperature composite comprising a structure which includes a carbonous matrix formed with interstices throughout and reinforcing, high-temperature fibers disposed within said matrix, boron, in elemental form and/or as moiety of a compound, said boron being dispersed throughout said matrix, silicon in elemental form and/or as a moiety of a compound, said silicon being dispersed throughout said matrix, plus an additional metal or metalloid, in elemental form and/or as a moiety of a compound, said metal or metalloid being dispersed throughout said matrix, said boron, said silicon plus said additional metal or metalloid each oxidizing when exposed to a high-temperature, oxidizing environment to form borosilicate plus a metal oxide or a metalloid oxide within the interstices and at the surface of said matrix, the boron plus silicon plus said additional metal or metalloid, calculated as if in their fully oxidized forms, comprising between about 10 about 1000 weight percent of the carbon in said matrix, said silicon, calculated as silicon oxide, being present in amounts of from about 3 to about 40 mole percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide; at high temperatures, the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the borosilicate which forms.
Claim 5
Dependent Claim
14 words
An oxygen-resistant composite according to claim 2 in combination with an outer refractory coating.
Claim 6
Dependent Claim
56 words
An oxygen-resistant composite according to claim 2 having a seal coat covering the structural surfaces of said composite, said seal coat containing boron, silicon and an additional metal or metalloid, said boron, silicon and additional metal or metalloid of said seal coat each oxidizing in a high-temperature, oxidizing environment to further protect said composite from oxidation.
Claim 7
Dependent Claim
22 words
A composite according to claim 4 in combination with an outer refractory coating that covers said composite structure and said seal coat.
Claim 8
Dependent Claim
29 words
A composite in accordance with claim 2 wherein said additional metal or metalloid is selected from the group consisting of Ti, Zr, Hf, Al, Y, Sc, La, and Ce.
Claim 9
Independent Claim
251 words
A method of preparing a high-temperature, oxygen-resistant carbonous structure comprising in a carbon char-yielding material, dispersing boron, in elemental form and/or as a moiety of a compound, dispersing silicon in elemental form and/or as a moiety of a compound and also dispersing an additional metal or metalloid, in elemental form and/or as a moiety of a compound, and heating said char-yielding material to carbonize the same and thereby form a carbonous matrix, said boron, silicon and additional metal or metalloid being dispersed in amounts within said char-yielding material such that in said carbonous matrix that forms, the boron plus silicon plus additional metal or metalloid, calculated as if in their fully oxidized forms, comprise between about 10 about 1000 weight percent of the carbon in said matrix, said silicon, calculated as silicon oxide, being present in amounts of from about 3 to about 40 percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide, said boron, silicon and additional metal or metalloid each oxidizing when exposed to a high-temperature, oxidizing environment to form borosilicate and a metal oxide or a metalloid oxide within the interstices and at the surface of said matrix; at high temperatures the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the borosilicate which forms.
Claim 10
Independent Claim
251 words
A method of preparing a high-temperature, oxygen-resistant carbonous structure comprising in a carbon char-yielding material, dispersing boron, in elemental form and/or as a moiety of a compound, dispersing silicon in elemental form and/or as a moiety of a compound and also dispersing an additional metal or metalloid, in elemental form and/or as a moiety of a compound, and heating said char-yielding material to carbonize the same and thereby form a carbonous matrix, said boron, silicon and additional metal or metalloid being dispersed in amounts within said char-yielding material such that in said carbonous matrix that forms, the boron plus silicon plus additional metal or metalloid, calculated as if in their fully oxidized forms, comprise between about 10 about 1000 weight percent of the carbon in said matrix, said silicon, calculated as silicon oxide, being present in amounts of from about 3 to about 40 percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide, said boron, silicon and additional metal or metalloid each oxidizing when exposed to a high-temperature, oxidizing environment to form borosilicate and a metal oxide or a metalloid oxide within the interstices and at the surface of said matrix; at high temperatures the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the borosilicate which forms.
Claim 11
Independent Claim
288 words
A method of preparing a high-temperature, oxygen-resistant composite comprising in a carbon char-yielding material, dispersing boron, in elemental form and/or as a moiety of a compound, dispersing silicon in elemental form and/or as a moiety of a compound, dispersing silicon in elemental form and/or a moiety of a compound and also dispersing an additional metal or metalloid, in elemental form and/or as a moiety of a compound, impregnating reinforcing, high-temperature fibers with said dispersion, forming a three-dimension structure with said dispersion-impregnated fibers, and heating said three-dimensional structure to carbonize said char-yielding material and thereby form a carbonous structure in which a carbonous matrix is reinforced by said fibers, said boron, silicon and metal or metalloid being dispersed in amounts within said char-yielding material such that in said carbonous matrix that forms, the boron plus silicon plus additional metal or metalloid, calculated as if in their fully oxidized forms, comprise between about 10 about 1000 weight percent of the carbon in said matrix, said silicon, calculated as silicon oxide, being present in amounts of from about 3 to about 40 mole percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide, said boron, silicon and additional metal or metalloid each oxidizing when exposed to a high-temperature, oxidizing environment to form borosilicate and a metal oxide or a metalloid oxide within the interstices and at the surface of said carbonous structure; at high temperatures the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the borosilicate which forms.
Claim 12
Independent Claim
288 words
A method of preparing a high-temperature, oxygen-resistant composite comprising in a carbon char-yielding material, dispersing boron, in elemental form and/or as a moiety of a compound, dispersing silicon in elemental form and/or as a moiety of a compound, dispersing silicon in elemental form and/or a moiety of a compound and also dispersing an additional metal or metalloid, in elemental form and/or as a moiety of a compound, impregnating reinforcing, high-temperature fibers with said dispersion, forming a three-dimension structure with said dispersion-impregnated fibers, and heating said three-dimensional structure to carbonize said char-yielding material and thereby form a carbonous structure in which a carbonous matrix is reinforced by said fibers, said boron, silicon and metal or metalloid being dispersed in amounts within said char-yielding material such that in said carbonous matrix that forms, the boron plus silicon plus additional metal or metalloid, calculated as if in their fully oxidized forms, comprise between about 10 about 1000 weight percent of the carbon in said matrix, said silicon, calculated as silicon oxide, being present in amounts of from about 3 to about 40 mole percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide, said boron, silicon and additional metal or metalloid each oxidizing when exposed to a high-temperature, oxidizing environment to form borosilicate and a metal oxide or a metalloid oxide within the interstices and at the surface of said carbonous structure; at high temperatures the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the borosilicate which forms.
Claim 13
Independent Claim
170 words
A method of protecting a high-temperature structure from oxidation comprising dispersing, in a carbon char-yielding material, boron, silicon and an additional metal or metalloid, each in either elemental form and/or as a moiety of a compound, said silicon, calculated as silicon oxide, being present in amounts of from about 3 to about 40 mole percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said additional metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide, applying said dispersion to surfaces of said structure, and carbonizing said char-yielding material thereon to form a seal coat, the boron, silicon and additional metal or metalloid in said seal coat ultimately oxidizing in a high-temperature, oxidizing environment to form borosilicate and metal oxide or metalloid oxide; at high temperatures, the metal oxide or metalloid oxide that forms stabilizing the viscosity of the molten phase the borosilicate that forms.
Claim 14
Independent Claim
170 words
A method of protecting a high-temperature structure from oxidation comprising dispersing, in a carbon char-yielding material, boron, silicon and an additional metal or metalloid, each in either elemental form and/or as a moiety of a compound, said silicon, calculated as silicon oxide, being present in amounts of from about 3 to about 40 mole percent of silicon plus boron, calculated as silicon oxide plus boron oxide, said additional metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 50 mole percent of boron plus silicon, calculated as boron oxide plus silicon oxide, applying said dispersion to surfaces of said structure, and carbonizing said char-yielding material thereon to form a seal coat, the boron, silicon and additional metal or metalloid in said seal coat ultimately oxidizing in a high-temperature, oxidizing environment to form borosilicate and metal oxide or metalloid oxide; at high temperatures, the metal oxide or metalloid oxide that forms stabilizing the viscosity of the molten phase the borosilicate that forms.
Claim 15
Dependent Claim
173 words
An oxygen-resistant, high-temperature composite comprising a structure which includes a carbonous matrix formed with interstices throughout and reinforcing, high-temperature carbon fibers disposed within said matrix, a metal or metalloid, in elemental form and/or as a moiety of a compound, dispersed throughout said structure, and boron, dispersed throughout said structure as a moiety of boron carbide, said boron and said metal or metalloid oxidizing when exposed to a high-temperature, oxidizing environment to form boron oxide and a metal oxide or a metalloid oxide within the interstices and at the surface of said matrix, the boron plus metal or metalloid, calculated as if in their fully oxidized forms, comprising between about 10 about 1000 weight percent of the carbon in said matrix, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 25 mole percent of boron, calculated as boron oxide; at high temperatures, the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the boron oxide which forms.
Claim 16
Dependent Claim
173 words
An oxygen-resistant, high-temperature composite comprising a structure which includes a carbonous matrix formed with interstices throughout and reinforcing, high-temperature carbon fibers disposed within said matrix, a metal or metalloid, in elemental form and/or as a moiety of a compound, dispersed throughout said structure, and boron, dispersed throughout said structure as a moiety of boron carbide, said boron and said metal or metalloid oxidizing when exposed to a high-temperature, oxidizing environment to form boron oxide and a metal oxide or a metalloid oxide within the interstices and at the surface of said matrix, the boron plus metal or metalloid, calculated as if in their fully oxidized forms, comprising between about 10 about 1000 weight percent of the carbon in said matrix, said metal or metalloid, calculated as if fully oxidized, being present in an amount of from about 3 to about 25 mole percent of boron, calculated as boron oxide; at high temperatures, the metal oxide or metalloid oxide which forms stabilizing the viscosity of the molten phase of the boron oxide which forms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-08 | 1993-07-10 | 1994-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-08 | 1997-07-10 | 1998-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-08 | 2001-07-10 | 2002-01-09 | $7700.00 | Window Closed / Lapsed |