Process for the manufacture of open porous sintered bodies being prepronderantly composed of glass ceramics
Assignee: Schott AG
•
Filing: 1988-09-19
•
Granted: 1990-02-27
•
Expires: 2008-09-19
Abstract
Abstract A process for manufacturing open porous sintered bodies with large open pore volume and defined pore diameters and which at least predominantly consist of glass-ceramics. They are obtained by sintering a mixture of sinterable powder and an inorganic soluble salt with defined grade of grain, the melting point of which is above the densification temperature of the sinterable powder. For the formation of a molded body the mixture of sinterable powder and inorganic salt is submitted to a molding process. The molded body is sintered in a sintering process and the soluble salt being contained in the molded body is lixiviated. As a main constituent the sinterable powder contains a pulverized crystallizable glass powder. The sintering process is performed in such a way that the crystal phases being produced during the crystallization of the crystallizable glass, and therefore the material properties, too, are controlled by the guidance of the sintering process as well as by the ion exchange taking place between the sinterable powder and the inorganic salt and which is controlled by their composition. Afterwards, the sintered body is transformed to the final glass-ceramic texture.
Inventors
- 👤 Friedrich Siebers
- 👤 Werner Kiefer
- 👤 Maria Sura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:37
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/0009; B01J37/0018; B01J37/08; C; C03; C03B; C03B19/00; C03B19/06; C03B32/00; C03B32/02; C03C; C03C11/00
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
185 words
A process for them manufacture of open porous sintered bodies at least predominantly consisting of glass ceramics comprising the steps of: (a) mixing a sinterable powder with a ground crystallizable glass powder to form a main constituent, the sinterable powder comprising a ground solder glass having a viscosity which si below the viscosity of the crystallizable glass powder when heated to a sintering temperature (b) adding to the main constituent an inorganic salt of defined grain size to form a molding material, the melting point of the salt being above the densification temperature of the sinterable powder, (c) submitting the molding material to a molding process for the formation of a molded body, (d) sintering the molded body in a sintering process to form a sintered body, the salt and sinterable powder being selected such that an ion exchange occurs between the salt and the sinterable powder during the sintering process, (e) cooling the sintered body, (f) leaching the salt contained in the sintered body to form pores within the body, and (g) transforming the sintered body into a final glass-ceramic body having open pores.
Claim 2
Dependent Claim
185 words
A process for them manufacture of open porous sintered bodies at least predominantly consisting of glass ceramics comprising the steps of: (a) mixing a sinterable powder with a ground crystallizable glass powder to form a main constituent, the sinterable powder comprising a ground solder glass having a viscosity which si below the viscosity of the crystallizable glass powder when heated to a sintering temperature (b) adding to the main constituent an inorganic salt of defined grain size to form a molding material, the melting point of the salt being above the densification temperature of the sinterable powder, (c) submitting the molding material to a molding process for the formation of a molded body, (d) sintering the molded body in a sintering process to form a sintered body, the salt and sinterable powder being selected such that an ion exchange occurs between the salt and the sinterable powder during the sintering process, (e) cooling the sintered body, (f) leaching the salt contained in the sintered body to form pores within the body, and (g) transforming the sintered body into a final glass-ceramic body having open pores.
Claim 3
Dependent Claim
19 words
The process of claim 1 wherein the transforming step comprises heating the sintered body subsequent to the leaching step.
Claim 4
Dependent Claim
24 words
The process of claim 2 wherein the heating step subsequent to the leaching step is performed at a temperature greater than the sintering step.
Claim 5
Dependent Claim
16 words
The process of claim 1 wherein the transforming step is performed prior to the leaching step.
Claim 6
Dependent Claim
42 words
The process of claim 1 wherein the sinterable powder comprises at least one component selected from the group consisting of: ground glass, pulverized and ceramicized glass ceramics, crystalline products in the form of particles, whiskers or fibers, and mixtures of these substances.
Claim 7
Dependent Claim
22 words
The process of claim 1 wherein the sinterable powder contains a retarding substance for retarding the surface crystallization of the crystallizable powder.
Claim 8
Dependent Claim
47 words
The process of claim 6 wherein the retarding substance comprises a member selected from the group consisting of: B 2 O 3 , P 2 O 5 , and other boron- or phosphorous-containing compounds which will evaporate or decompose at about the temperature of the sintering step.
Claim 9
Dependent Claim
28 words
The process of claim 1 wherein the sintering step is performed in an atmosphere containing a member selected form the group consisting of: boron, phosphorous, and mixtures thereof.
Claim 10
Dependent Claim
34 words
The process of claim 1 wherein the inorganic salt is selected from the group consisting of: alkali or alkaline earth halides, sulphates, carbonates, nitrates, phosphates and hydrates thereof, double salts thereof, and mixtures thereof.
Claim 11
Dependent Claim
20 words
The process of claim 1 wherein the crystallizable glass powder includes a nucleating agent for achieving an additional volume crystallization.
Claim 12
Dependent Claim
27 words
The process of claim 1 wherein the adding step further comprises admixing a particulate organic substance which is burnt out during the course of the sintering step.
Claim 13
Dependent Claim
215 words
A process for the manufacture of open porous sintered bodies at least predominantly consisting of glass ceramics comprising the steps of: (a) mixing a sinterable powder with a ground crystallizable glass powder to form a main constituent, the sinterable powder comprising a ground solder glass having a viscosity which is below the viscosity of the crystallizable glass powder when heated to a sintering temperature, (b) adding to the main constituent an inorganic salt selected from the group consisting of: alkali or alkaline earth halides, sulphates, carbonates, nitrates, phosphates and hydrates thereof, double salts thereof, and mixtures thereof to form a molding material, the melting point of the salt being above the densification temperature of the sinterable powder, (c) submitting the molding material to a molding process for the formation of a molded body, (d) sintering the molded body in a sintering process at a temperature and for a time sufficient to cause some ion exchange between the salt and the sinterable powder to form a sintered body, (e) cooling the sintered body, (f) leaching the inorganic salt remaining in the sintered body to form pores within the body, and (g) heating the leached sintered body to a temperature greater than the sintering step temperature to transform it into a final glass-ceramic body having open pores.
Claim 14
Dependent Claim
215 words
A process for the manufacture of open porous sintered bodies at least predominantly consisting of glass ceramics comprising the steps of: (a) mixing a sinterable powder with a ground crystallizable glass powder to form a main constituent, the sinterable powder comprising a ground solder glass having a viscosity which is below the viscosity of the crystallizable glass powder when heated to a sintering temperature, (b) adding to the main constituent an inorganic salt selected from the group consisting of: alkali or alkaline earth halides, sulphates, carbonates, nitrates, phosphates and hydrates thereof, double salts thereof, and mixtures thereof to form a molding material, the melting point of the salt being above the densification temperature of the sinterable powder, (c) submitting the molding material to a molding process for the formation of a molded body, (d) sintering the molded body in a sintering process at a temperature and for a time sufficient to cause some ion exchange between the salt and the sinterable powder to form a sintered body, (e) cooling the sintered body, (f) leaching the inorganic salt remaining in the sintered body to form pores within the body, and (g) heating the leached sintered body to a temperature greater than the sintering step temperature to transform it into a final glass-ceramic body having open pores.
Claim 15
Dependent Claim
193 words
A process for the manufacture of open porous sintered bodies at least predominantly consisting of glass ceramics comprising the steps of: (a) mixing a sinterable powder with a ground crystallizable glass powder to form a main constituent, the sinterable powder containing a retarding substance for retarding the surface crystallization of the crystallizable powder comprising a member selected from the group consisting of: B 2 O 3 , P 2 O 5 , and other boron- or phosphorous-containing compounds which will evaporate or decompose at about a sintering temperature of the main constituent; (b) adding to the main constituent an inorganic salt of defined grain size to form a molding material, the melting point of the salt being above the densification temperature of the sinterable powder, (c) submitting the molding material to a molding process for the formation of a molded body, (d) heating the molded body in a sintering process to form a sintered body, (e) cooling the sintered body, (f) leaching the salt contained in the sintered body to form pores within the body, and (g) re-heating the sintered body sufficient to transform it into a final glass-ceramic body having open pores.
Claim 16
Dependent Claim
193 words
A process for the manufacture of open porous sintered bodies at least predominantly consisting of glass ceramics comprising the steps of: (a) mixing a sinterable powder with a ground crystallizable glass powder to form a main constituent, the sinterable powder containing a retarding substance for retarding the surface crystallization of the crystallizable powder comprising a member selected from the group consisting of: B 2 O 3 , P 2 O 5 , and other boron- or phosphorous-containing compounds which will evaporate or decompose at about a sintering temperature of the main constituent; (b) adding to the main constituent an inorganic salt of defined grain size to form a molding material, the melting point of the salt being above the densification temperature of the sinterable powder, (c) submitting the molding material to a molding process for the formation of a molded body, (d) heating the molded body in a sintering process to form a sintered body, (e) cooling the sintered body, (f) leaching the salt contained in the sintered body to form pores within the body, and (g) re-heating the sintered body sufficient to transform it into a final glass-ceramic body having open pores.
Claim 17
Dependent Claim
15 words
The process of claim 13 wherein the re-heating step is performed after the leaching step.
Claim 18
Dependent Claim
15 words
The process of claim 13 wherein the re-heating step is performed before the leaching step.
Claim 19
Dependent Claim
193 words
A process for the manufacture of open porous bodies having a large open pore volume and defined pore diameters, at least predominantly consisting of glass-ceramics comprising the steps of: (a) mixing a sinterable powder comprising predominantly a crystallizable glass powder with an inorganic soluble salt of defined grain size to form a molding material, the densification (vitrification) temperature of the sinterable powder being below the melting point of the salt, (b) molding the molding material to form a molded body, (c) sintering the molded body in a sintering process comprising a first heat treatment in which an ion exchange takes place between the crystallizable glass and the salt to form a sintered body in which crystal phases are produced due to crystallization of the crystallizable glass powder, (d) cooling the sintered body, (e) transforming the sintered body by a second heat treatment into a body having a glass-ceramics texture the material properties of which are determined by the composition of the sinterable powder and salt mixture, and the amount of ion exchange taking place during the first heat treatment, and (f) leaching salt from the sintered body to form pores within the body.
Claim 20
Dependent Claim
193 words
A process for the manufacture of open porous bodies having a large open pore volume and defined pore diameters, at least predominantly consisting of glass-ceramics comprising the steps of: (a) mixing a sinterable powder comprising predominantly a crystallizable glass powder with an inorganic soluble salt of defined grain size to form a molding material, the densification (vitrification) temperature of the sinterable powder being below the melting point of the salt, (b) molding the molding material to form a molded body, (c) sintering the molded body in a sintering process comprising a first heat treatment in which an ion exchange takes place between the crystallizable glass and the salt to form a sintered body in which crystal phases are produced due to crystallization of the crystallizable glass powder, (d) cooling the sintered body, (e) transforming the sintered body by a second heat treatment into a body having a glass-ceramics texture the material properties of which are determined by the composition of the sinterable powder and salt mixture, and the amount of ion exchange taking place during the first heat treatment, and (f) leaching salt from the sintered body to form pores within the body.
Claim 21
Dependent Claim
30 words
The process of claim 16 wherein the second heat treatment comprises heating the sintered body subsequently to the leaching step while retaining the open porous structure of said sintered body.
Claim 22
Dependent Claim
30 words
The process of claim 16 wherein the second heat treatment is performed at a temperature greater than the sintering step while retaining the open porous structure of said sintered body.
Claim 23
Dependent Claim
48 words
The process of claim 16 further comprising the step of adding as a component of the sinterable powder at least one of the group consisting of: ground glass; pulverized and ceramized glass ceramics; crystalline products in the form of particles, whiskers or fibers; and mixtures of these substances.
Claim 24
Dependent Claim
25 words
The process of claim 19 further comprising the step of adding a component to the sinterable powder for lowering the temperature at which sintering occurs.
Claim 25
Dependent Claim
30 words
The process of claim 19 further comprising the step of adding a ground solder glass, the viscosity of which, when heated, is below the viscosity of the crystallizable glass powder.
Claim 26
Dependent Claim
26 words
The process of claim 19 further comprising the step of adding a component to the sinterable powder for retarding the surface crystallization of the crystallizable powder.
Claim 27
Dependent Claim
38 words
The process of claim 19 further comprising the step of adding a component to the sinterable powder consisting essentially of a solder glass with a least 5 wt.-% B 2 O 3 and/or P 2 O 5 .
Claim 28
Dependent Claim
49 words
The process of claim 19 further comprising the step of adding as a component of the sinterable powder at least one compound containing boron and/or phosphorous so that during the sintering step a boron- and/or phosphorous-containing atmosphere is produced by evaporation and/or decomposition of said at least one compound.
Claim 29
Dependent Claim
16 words
The process of claim 16 wherein the sintering step is carried out in a boron-containing atmosphere.
Claim 30
Dependent Claim
16 words
The process of claim 16 wherein the sintering step is carried out in a phosphorous-containing atmosphere.
Claim 31
Dependent Claim
18 words
The process of claim 16 wherein the sintering step is carried out in a boron- and phosphorous-containing atmosphere.
Claim 32
Dependent Claim
37 words
The process of claim 16 further comprising the step of coating at least one of the components of the sinterable powder with a material for diminishing the densification temperature before mixing said powder with the inorganic salt.
Claim 33
Dependent Claim
37 words
The process of claim 16 further comprising the step of coating at least one of the components of the sinterable powder with a material for retarding the surface crystallization before mixing said powder with the inorganic salt.
Claim 34
Dependent Claim
56 words
The process of claim 16 further comprising the step of choosing the composition of the inorganic salt and components of the sinterable powder other than the crystallizable glass so that during the sintering process and crystallization of the crystallizable glass, at best, only a small ion exchange takes place between said components and the inorganic salt.
Claim 35
Dependent Claim
63 words
The process of claim 16 wherein the compositions of the sinterable powder and the inorganic salt are chosen such that during the sintering process and/or during the crystallization of the crystallizable glass an intensive ion exchange or rather mechanical reaction takes place which make the crystallizable phase be formed as desired whereby soluble salt is present after the sintered body has cooled down.
Claim 36
Dependent Claim
33 words
The process of claim 16 wherein the mixing step comprises using alkali or alkaline earth halides, sulphates, carbonates, nitrates, phosphates and hydrates thereof, double salts and mixtures thereof for said inorganic soluble salt.
Claim 37
Dependent Claim
21 words
The process of claim 16 wherein the transforming step comprises crystallizing the surface of the sintered body into a glass-ceramics state.
Claim 38
Dependent Claim
26 words
The process of claim 16 further comprising the step of adding a nucleating agent to the crystallizable glass powder in order to achieve a volume crystallization.
Claim 39
Dependent Claim
30 words
The process of claim 16 further comprising the step of adding organic expedients and/or a liquid to the mixture of sinterably powder and inorganic salt prior to the molding process.
Claim 40
Dependent Claim
25 words
The process of claim 35 wherein the molding step comprises one or more of the steps of dry pressing, extruding, injection molding or slip casting.
Claim 41
Dependent Claim
47 words
The process of claim 16 further comprising the steps of adding organic substances to the mixture of sinterable powder and soluble inorganic salt, and burning the organic substances out in the course of the sintering step to form cavities, the cavities being retained in the subsequent steps.
Claim 42
Dependent Claim
43 words
The process of claim 37 further comprising the steps of preparing the mixture of sinterable powder and inorganic salt in the form of a slip, and infiltrating the slip into open spaces existing in an open-celled sponge-like body formed of the organic substances.
Claim 43
Dependent Claim
14 words
The process of claim 16 wherein the sintering step is performed by pressure admission.
References Cited (Backward Citations)
US1929425A
Cited
US2209163A
Cited
US3024118A
Cited
US3356513A
Cited
US3881944A
Cited
US4404291A
Cited
US4588540A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-26 | 1993-08-28 | 1994-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-26 | 1997-08-28 | 1998-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-26 | 2001-08-28 | 2002-02-27 | $7700.00 | Window Closed / Lapsed |