Copper etching process and product with controlled nitrous acid reaction
Assignee: PSI Star Inc
•
Filing: 1989-02-06
•
Granted: 1990-05-22
•
Expires: 2009-02-06
Abstract
Abstract Copper etching process and product in which a material which promotes the formation of nitrous acid is included in the copper. The copper is etched in a nitric acid solution, and the nitrous acid catalyzes the reaction between the nitric acid and the copper. The catalyst promoter is distributed within the copper to control where the nitrous acid is formed and, hence, the manner in which the copper is etched. In one disclosed embodiment, the material which promotes the formation of nitrous acid increases in concentration toward the substrate, or board to which the copper is bonded. The nitrous acid reacts vigorously with the copper, and the etch rate increases as the etch progresses through the copper toward the substrate. A polymer and/or a nitrous acid scavenger can be included in the etching solution to confine the etching reaction to the region in which the nitrous acid is formed.
Inventors
- 👤 Norvell J. Nelson
- 👤 Phillip A. Martens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 00:24
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/10; C23F1/14; C23F1/16; C23F1/18; H; H05; H05K; H05K3/00; H05K3/02; H05K3/06; H05K3/067; H05K1/00; H05K1/02; H05K1/09; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/24; Y10T428/24802; Y10T428/24917; Y10T428/25; Y10T428/256; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
49 words
In copper foil for use in a printed circuit board prepared by etching in a nitric acid solution: a material distributed within the copper foil for promoting the formation of nitrous acid from nitric acid in a controlled manner when the board is exposed to the nitric acid solution.
Claim 2
Dependent Claim
49 words
In copper foil for use in a printed circuit board prepared by etching in a nitric acid solution: a material distributed within the copper foil for promoting the formation of nitrous acid from nitric acid in a controlled manner when the board is exposed to the nitric acid solution.
Claim 3
Dependent Claim
28 words
The copper foil of claim 1 wherein the material which promotes the formation of nitrous acid increases in concentration from one surface of the foil toward the other.
Claim 4
Dependent Claim
58 words
In a printed circuit board which is processed in a nitric acid etching solution: a substrate, a layer of copper on one side of the substrate, and a material which promotes the formation of nitrous acid from nitric acid distributed within the copper to control the manner in which the copper is removed in the nitric acid solution.
Claim 5
Dependent Claim
58 words
In a printed circuit board which is processed in a nitric acid etching solution: a substrate, a layer of copper on one side of the substrate, and a material which promotes the formation of nitrous acid from nitric acid distributed within the copper to control the manner in which the copper is removed in the nitric acid solution.
Claim 6
Dependent Claim
30 words
The printed circuit board of claim 3 wherein the material which promotes the formation of nitrous acid decreases in concentration from the substrate toward the outer surface layer of copper.
Claim 7
Dependent Claim
71 words
In copper foil for use in a printed circuit board prepared by etching in a nitric acid solution: a material distributed within the copper foil for promoting the formation of nitrous acid from nitric acid in a controlled manner when the board is exposed to the nitric acid solution, said material being selected from the group consisting of zinc, tin, cadmium, magnesium, aluminum, an alkali metal, iron, lead, and combinations thereof.
Claim 8
Dependent Claim
71 words
In copper foil for use in a printed circuit board prepared by etching in a nitric acid solution: a material distributed within the copper foil for promoting the formation of nitrous acid from nitric acid in a controlled manner when the board is exposed to the nitric acid solution, said material being selected from the group consisting of zinc, tin, cadmium, magnesium, aluminum, an alkali metal, iron, lead, and combinations thereof.
Claim 9
Dependent Claim
28 words
The copper foil of claim 5 wherein the material which promotes the formation of nitrous acid increases in concentration from one surface of the foil toward the other.
Claim 10
Dependent Claim
80 words
In a printed circuit board which is processed in a nitric acid etching solution: a substrate, a layer of copper on one side of the substrate, and a material which promotes the formation of nitrous acid from nitric acid distributed within the copper to control the manner in which the copper is removed in the nitric acid solution, said material being selected from the group consisting of zinc, tin, cadmium, magnesium, aluminum, an alkali metal, iron, lead, and combinations thereof.
Claim 11
Dependent Claim
80 words
In a printed circuit board which is processed in a nitric acid etching solution: a substrate, a layer of copper on one side of the substrate, and a material which promotes the formation of nitrous acid from nitric acid distributed within the copper to control the manner in which the copper is removed in the nitric acid solution, said material being selected from the group consisting of zinc, tin, cadmium, magnesium, aluminum, an alkali metal, iron, lead, and combinations thereof.
Claim 12
Dependent Claim
32 words
The printed circuit board of claim 7 wherein the material which promotes the formation of nitrous acid decreases in concentration from the substrate toward the outer surface of the layer of copper.
References Cited (Backward Citations)
US3857681A
Cited
US3918926A
Cited
US3853716A
Cited
US3896256A
Cited
US3931030A
Cited
US3998601A
Cited
US4138470A
Cited
US4046620A
Cited
US4713144A
Cited
US4695348A
Cited
US4767661A
Cited
US4846918A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-21 | 1993-11-20 | 1994-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-21 | 1997-11-20 | 1998-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-21 | 2001-11-20 | 2002-05-22 | $7700.00 | Window Closed / Lapsed |