Method of forming a three-dimensional object by stereolithography and composition therefore
Assignee: Covestro Resins BV
•
Filing: 1989-10-31
•
Granted: 1990-07-17
•
Expires: 2009-10-31
Abstract
Abstract A stereolithographic method which employs an ultraviolet-curable liquid composition adapted to cure rapidly to a lightly cross-linked solvent-swellable three-dimensional complexly-shaped polymeric thin-walled element constituted by heat-softenable solid polymer upon exposure to ultraviolet dosage in the range of about 0.1 to about 10 Joules per square centimeter and which possesses reduced distortion comprises, from 20 to 80 weight percent, of a resinous polyacrylate or polymethacrylate dissolved in a combination of 10 to 45 weight percent of a liquid polyacrylate or polymethacrylate, which is preferably trifunctional, and 10 to 45 weight percent of liquid N-vinyl monomer, preferably N-vinyl pyrrolidone. Thus, the weight ratio of polyacrylate: polymethacrylate: N-vinyl monomer is about 1:2:2 to about 8:1:1. One of the foregoing polyacrylates or polymethacrylates is a polyacrylate and the other is a polymethacrylate so that good cure speed is accompanied by good distortion resistance. In the method, a reservoir of the liquid composition is established and its exposed surface is irradiated to solidify the surface and build up a thin-walled element which is removed from the reservoir, drained of liquid adhering thereto and cured.
Inventors
- 👤 Edward J. Murphy
- 👤 Robert E. Ansel
- 👤 John J. Krajewski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 18:39
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/0037; B; B29; B29C; B29C35/00; B29C35/02; B29C35/08; B29C39/00; B29C39/003; B29C39/006; B29C64/00; B29C64/10; B29C64/106; B29C64/124; B33; B33Y; B33Y70/00; B29K; B29K2025/00; B29K2033/00; B29K2033/04; B29K2055/00
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
99 words
An ultraviolet-curable liquid composition adapted to cure rapidly to a lightly cross-linked solvent-swellable three-dimensional complexly-shaped polymeric thin-walled element constituted by heat-softenable solid polymer upon exposure to ultraviolet dosage in the range of about 0.1 to about 10 Joules per square centimeter and which possesses reduced distortion comprising, from 20 to 80 weight percent, of a resinous polyacrylate or polymethacrylate dissolved in a combination of 10 to 40 weight percent of a liquid polyacrylate or polymethacrylate, one of the foregoing being a polyacrylate and the other being a polymethacrylate, and 10 to 30 weight percent of a liquid N-vinyl monomer.
Claim 2
Dependent Claim
99 words
An ultraviolet-curable liquid composition adapted to cure rapidly to a lightly cross-linked solvent-swellable three-dimensional complexly-shaped polymeric thin-walled element constituted by heat-softenable solid polymer upon exposure to ultraviolet dosage in the range of about 0.1 to about 10 Joules per square centimeter and which possesses reduced distortion comprising, from 20 to 80 weight percent, of a resinous polyacrylate or polymethacrylate dissolved in a combination of 10 to 40 weight percent of a liquid polyacrylate or polymethacrylate, one of the foregoing being a polyacrylate and the other being a polymethacrylate, and 10 to 30 weight percent of a liquid N-vinyl monomer.
Claim 3
Dependent Claim
28 words
An ultraviolet-curable liquid composition as recited in claim 1 in which the ultraviolet dosage is in the range of about 0.2 to about 5 Joules per square centimeter.
Claim 4
Dependent Claim
26 words
An ultraviolet-curable liquid composition as recited in claim 1 in which said resinous polyacrylate is used in an amount of from 45 to 70 weight percent.
Claim 5
Dependent Claim
33 words
An ultraviolet-curable liquid composition as recited in claim 1 in which said liquid polyacrylate or polymethacrylate is at least trifunctional and is used in an amount of from 15 to 30 weight percent.
Claim 6
Dependent Claim
19 words
An ultraviolet-curable liquid composition as recited in claim 4 in which said at least trifunctional liquid is a polymethacrylate.
Claim 7
Dependent Claim
20 words
An ultraviolet-curable liquid composition as recited in claim 5 in which said liquid is a polymethacrylate is trimethylol propane trimethacrylate.
Claim 8
Dependent Claim
26 words
An ultraviolet-curable liquid composition as recited in claim 1 in which said N-vinyl monomer is used in an amount of from 15 to 30 weight percent.
Claim 9
Dependent Claim
17 words
An ultraviolet-curable liquid composition as recited in claim 7 in which said N-vinyl monomer is N-vinyl pyrrolidone.
Claim 10
Dependent Claim
32 words
An ultraviolet-curable liquid composition as recited in claim 1 in which said composition includes from 1 to 10 weight percent of a photoinitiator effective to initiate the ultraviolet cure of (meth)acrylate functionality.
Claim 11
Dependent Claim
22 words
The composition as recited in claim 1 wherein the weight ratio of polyacrylate: polymethacrylate: N-vinyl monomer is about 1:2:2 to about 8:1:1.
Claim 12
Dependent Claim
22 words
The composition as recited in claim 1 wherein the weight ratio of polyacrylate: polymethacrylate: N-vinyl monomer is about 7:6:6 to about 14:3:3.
Claim 13
Dependent Claim
87 words
An ultraviolet-curable liquid composition adapted to cure rapidly to a lightly cross-linked solvent-swellable three-dimensional complexly-shaped polymeric thin-walled element constituted by heat-softenable solid polymer upon exposure to ultraviolet dosage in the range of about 0.2 to about 5 Joules per square centimeter and which possesses reduced distortion comprising, from 45 to 70 weight percent, of a resinous polyacrylate dissolved in a combination of 15 to 30 weight percent of a liquid trimethacrylate and 15 to 30 weight percent of a liquid N-vinyl pyrrolidone or a liquid N-vinyl caprolactam.
Claim 14
Dependent Claim
87 words
An ultraviolet-curable liquid composition adapted to cure rapidly to a lightly cross-linked solvent-swellable three-dimensional complexly-shaped polymeric thin-walled element constituted by heat-softenable solid polymer upon exposure to ultraviolet dosage in the range of about 0.2 to about 5 Joules per square centimeter and which possesses reduced distortion comprising, from 45 to 70 weight percent, of a resinous polyacrylate dissolved in a combination of 15 to 30 weight percent of a liquid trimethacrylate and 15 to 30 weight percent of a liquid N-vinyl pyrrolidone or a liquid N-vinyl caprolactam.
Claim 15
Independent Claim
158 words
A method of forming a three-dimensional thin-walled object comprising, providing a reservoir of liquid ultraviolet-curable ethylenically unsaturated material comprising, from 20 to 80 weight percent, of a resinous polyacrylate or polymethacrylate dissolved in a combination of 10 to 35 weight percent of a liquid polyacrylate or polymethacrylate, one of the foregoing being a polyacrylate and the other being a polymethacrylate, and 10 to 40 weight percent of liquid N-vinyl monomer, exposing the surface of said reservoir to a beam of ultraviolet light to apply a dosage in the range of about 0.1 to about 10 Joules per square centimeter to said surface to solidify the liquid near said surface to form a plurality of superposed layers of lightly cross-linked solvent-swellable three-dimensional complexly-shaped polymeric thin-walled element constituted by heat-softenable solid polymer in said reservoir, removing said element from said reservoir, draining excess polymerizable liquid from said element, and then completing the cure of said element to strengthen the same.
Claim 16
Independent Claim
158 words
A method of forming a three-dimensional thin-walled object comprising, providing a reservoir of liquid ultraviolet-curable ethylenically unsaturated material comprising, from 20 to 80 weight percent, of a resinous polyacrylate or polymethacrylate dissolved in a combination of 10 to 35 weight percent of a liquid polyacrylate or polymethacrylate, one of the foregoing being a polyacrylate and the other being a polymethacrylate, and 10 to 40 weight percent of liquid N-vinyl monomer, exposing the surface of said reservoir to a beam of ultraviolet light to apply a dosage in the range of about 0.1 to about 10 Joules per square centimeter to said surface to solidify the liquid near said surface to form a plurality of superposed layers of lightly cross-linked solvent-swellable three-dimensional complexly-shaped polymeric thin-walled element constituted by heat-softenable solid polymer in said reservoir, removing said element from said reservoir, draining excess polymerizable liquid from said element, and then completing the cure of said element to strengthen the same.
Claim 17
Dependent Claim
19 words
A method as recited in claim 13 in which said drained element is cured by exposure to ultraviolet light.
Claim 18
Dependent Claim
28 words
A method as recited in claim 13 in which said drained element is cured by exposure to heat at a temperature not in excess of about 325° F.
Claim 19
Dependent Claim
30 words
A method as recited in claim 13 in which said drained element is cured by exposure to heat at a temperature of from about 250° F. to about 300° F.
Claim 20
Dependent Claim
58 words
A light curable liquid composition comprising 20 to 80 weight percent of a resinous polyacrylate or polymethacrylate dissolved in a combination of 10 to 40 weight percent of a liquid polyacrylate or polymethacrylate and 10 to 30 weight percent of a liquid N-vinyl monomer, the weight ratio of polyacrylate: polymethacrylate: N-vinyl monomer being about 1:2:2 to about 8:1:1.
Claim 21
Dependent Claim
58 words
A light curable liquid composition comprising 20 to 80 weight percent of a resinous polyacrylate or polymethacrylate dissolved in a combination of 10 to 40 weight percent of a liquid polyacrylate or polymethacrylate and 10 to 30 weight percent of a liquid N-vinyl monomer, the weight ratio of polyacrylate: polymethacrylate: N-vinyl monomer being about 1:2:2 to about 8:1:1.
Claim 22
Dependent Claim
58 words
The composition as recited in claim 17 wherein the resinous polyacrylate or polymethacrylate is present in an amount of about 45 to 70 weight percent, the liquid polyacrylate or polymethacrylate is present in an amount of about 15 to 30 weight percent and the N-vinyl monomer is present in an amount of about 15 to 30 weight percent.
Claim 23
Dependent Claim
22 words
The composition as recited in claim 17 wherein the weight ratio of polyacrylate: polymethacrylate: N-vinyl monomer is about 7:6:6 to about 14:3:3.
Claim 24
Dependent Claim
58 words
The composition as recited in claim 19 wherein the resinous polyacrylate or polymethacrylate is present in an amount of about 45 to 70 weight percent, the liquid polyacrylate or polymethacrylate is present in an amount of about 15 to 30 weight percent and the N-vinyl monomer is present in an amount of about 15 to 30 weight percent.
References Cited (Backward Citations)
US2899402A
Cited
US2972170A
Cited
US3198868A
Cited
US3751399A
Cited
US3939049A
Cited
US4049757A
Cited
US4181752A
Cited
US4089918A
Cited
US4060678A
Cited
US4042654A
Cited
JPS5268267A
Cited
US4183991A
Cited
US4379864A
Cited
JPS56152803A
Cited
US4361689A
Cited
WO1982002559A1
Cited
US4379201A
Cited
US4446220A
Cited
US4430458A
Cited
US4393094A
Cited
EP0109177A1
Cited
EP0160957A2
Cited
US4734143A
Cited
US4575330A
Cited
US4575330B1
Cited
US4701509A
Cited
US4636534A
Cited
JPS61114818A
Cited
JPS61116321A
Cited
JPS61116322A
Cited
JPS61116320A
Cited
JPS61114817A
Cited
JPS61154815A
Cited
JPS61217219A
Cited
US4673705A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-16 | 1994-01-15 | 1994-07-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-16 | 1998-01-15 | 1998-07-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-16 | 2002-01-15 | 2002-07-17 | $7700.00 | Window Closed / Lapsed |